• Journal of the Korean Magnetics Society
• /
• v.24 no.6
• /
• pp.186-190
• /
• 2014

To establish the coating conditions for $^{57}Co$, non-radioactive Co ions are dissolved in an acid solution and electroplated on to a copper plate. Then, the thermal diffusion of electroplated Co into a copper matrix was studied to apply a $^{57}Co$ $M{\ddot{o}}ssbauer$ source. Nanocrystalline Co particles were coated on a Cu substrate using DC electro-deposition at a pH of 1.89 to 5 and $20{\sim}30mA/cm^2$. The average grain size was up to 54 nm as the pH increased to 5. The second phase of Co-oxide was formatted as the pH was increased above 4. The diffusion degree was evaluated by mapping using scanning electron microscopy (SEM). The influence of different annealing conditions was investigated. The diffusion depth of Co depends on the annealing temperature and time. The results obtained confirm that the deposited Co diffused almost completely into a copper matrix without substantial loss at an annealing temperature of $900^{\circ}C$ for 2 hours.

• Journal of Powder Materials
• /
• v.22 no.6
• /
• pp.432-437
• /
• 2015

The en-riched $^{58}Ni$ powders are dissolved in acid solution and coated on a Cu target for proton irradiation at cyclotron to produce $^{57}Co$ radioisotope. The condition of the plating bath and the coating process are determined using the en-riched powders. To establish the coating conditions for $^{57}Co$, non-radioactive Co ions are dissolved in an acid solution and electroplated on to a rhodium plate. The thermal diffusion of electroplated Co into a rhodium matrix was studied to apply a $^{57}Co$ Mssbauer source. The diffusion depth from surface to matrix of Co is depended on the annealing temperature and time. The deposited Co atoms diffuse completely into a rhodium (Rh) matrix without substantial loss at an annealing temperature of 1200 for 4 hours.