• Clean Technology
• /
• v.12 no.4
• /
• pp.232-237
• /
• 2006

The zinc-based desulfurization sorbents for a fluidized-bed system were prepared by a spray drying method and the effects of the pH and viscosity of the slurry on the attrition resistance of the prepared sorbents were investigated in this work. In order to improve the attrition resistance, alumina sol was used for an inorganic binder and pH of the slurry was changed for its better dispersion in slurry. The attrition resistance of the prepared sorbents decreased due to the phase transition of alumina sol to gel as the slurry pH increased to its basicity. The optimum pH condition for the good attrition resistance of the sorbents was about 6.0 in this study. It was confirmed that the attrition property of the sorbents were varied with the viscosity of the slurry. The attrition resistance of the sorbents prepared by the spray drying method increased as their bulk density increased, while it decreased as the surface area and porosity of the sorbents. The optimum viscosity for the high attrition was in the range 400-500 cP.

• Elastomers and Composites
• /
• v.46 no.2
• /
• pp.132-137
• /
• 2011

In the present investigation, thermal aging behavior of H-NBR/NBR blend with various H-NBR content was investigated. Mixture of dicumyl peroxide and sulfur were used as a curing agent. The influence of the thermal aging of the H-NBR/NBR blends on the solid state properties such as tensile strength, elongation at break, hardness and abrasion resistance was investigated. Tensile strength was increased with increasing H-NBR content, while abrasion resistance was decreased. Both elongation at break and hardness were not affected by the addition of H-NBR. The properties such as hardness, tensile strength and elongation at break of the aged samples were lower than unaged samples. However, the rate of deterioration of those properties was decreased by increasing the H-NBR content, which indicated that improved thermal aging behavior was obtained by the addition of H-NBR. Abrasion loss was increased with increasing aging time, but it became less by the addition of H-NBR addition.

• Elastomers and Composites
• /
• v.34 no.5
• /
• pp.391-398
• /
• 1999

Di-2-ethyl hexyl phthalate (DOP) and di-2-ethyl hexyl adiphate (DOA) were mixed with poly(vlnvl chlorides) [PVC] which have different degrees of polymerization (DP). Tensile strength, elongation, density, abrasion resistance, and hardness of these compounds were measured, High molecular weight PVC(DP 2500) was superior to that of DP 1300 for tensile strength, Hardness. But elongation and abrasion resistance of P1300 systems were better than those of P2500 systems. The densities of both systems were almost same. On the other hand, DOP Plasticized PVC was superior to DOA plasticized one for tensile strength, elongation, hardness. In cases of density, abrasion resistance, and flexual resistance, DOA systems were better than those of DOP systems.

• Journal of the Korean Society for Railway
• /
• v.13 no.4
• /
• pp.389-395
• /
• 2010

This paper is about the copper slider with high electric conductivity and resistance arc. A new copper slider which has enhanced resistance against frictional wear was developed. By alteration of its material components and manufacturing process, its material property has been enhanced. To verify its enhanced wear-resisting capacity, a laboratory test and a field test were carried out. As the laboratory test, a dynamo test was performed and its test result showed that the developed new copper slider had superior wear-resisting capacity to the currently used copper slider. The new one showed double durability of the current one and normal wearing characteristics. A filed test was performed on the Metro subway lines at service by Seoul Metro. The field test showed similar results to those from the laboratory test, which the d eveloped new copper slider has double superior durability and sound wearing patterns. Authors strongly believe that the replacement of the copper slider currently in use by the developed new one will contribute to the economic and efficient operation of the subway line system

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.166.2-166.2
• /
• 2016

최근 생산 장비의 발달로 인해 절삭공구, 전기전자 부품, 항공 및 자동차 부품 생산에 필요한 생산 장비의 수명연장, 고속 절단 및 고성능화가 중요시 되면서 우수한 내구성, 내마모성 및 고온 안정성을 갖는 기계부품 및 공구를 요구하게 되었다. 내마모성을 가지는 표면을 얻기 위해서는 TiN, TiC, AlN, Al2O3, CrN, ZrO2와 같은 경도 높은 물질을 증착하여 특성을 개선시키는 방법이 있다. 특히 AlN은 비교적 우수한 경도와 고온 안정성을 가지고 있어, 생산 장비의 고속 절단 및 반복되는 정밀 작업으로 인한 열충격과 마모를 완화시키는 역할을 하는 코팅재로 사용하기 적합하다. 본 실험에서는 RF-magnetron sputtering 방법을 이용하여 AlN 박막을 파워 150W, 질소가스 분압비에 따라 25%, 50%, 75%, 100%의 조건으로 금속기판 위에 증착하였다. 금속 기판 위에 제작된 AlN막은 XRD (X-ray Diffraction)을 사용하여 배향성을 확인하였고, HM-220 (Micro-vickers hardness tester)을 사용하여 AlN박막의 경도를 측정하였으며, SEM (Scanning Electron Microscope), AFM (Atomic Force Microscope)을 이용하여 표면의 구조와 거칠기를 측정하였다. 이 실험을 통하여 우수한 물성과, 치밀한 조직의 AlN박막이 고속 절삭 공구, 유공압 실린더, 베어링과 같은 금속부품의 코팅소재로 적용가능 할 것으로 기대된다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.10a
• /
• pp.37-37
• /
• 1999

Cr-N 계 박막은 경도가 높고 치밀한 층을 형성할 수 있으므로 현재 금형과 기계류 핵심부품의 내마모 및 내식성 향상을 위한 대표적인 물질로 많은 주목을 받고 있다. 본 연구에서는 아크 이온플레이팅 장비를 이용하여 질소분압, 바이어스 전원 등의 변화에 따른 Cr-N계 박막의 결정성 및 표면상태, 증착율, 그리고 내마모성을 조사하였다. Cr-N 계 박막을 증착하기 위해서 사용한 시편은 $20MM{\phi}{\times}4mmt$ 크기의 고속도 공구강 디스크이었으며, Trichloroethylene에서 5분간 초음파 세척을 한 후 건조하여 진공용기 내에 장착하였다. 박막을 증착하기전 시편의 표면을 깨끗하게 하기 위해서 Ar 이온 충격으로 플라즈마 전처리를 하였다. 증착된 Cr-N 계 박막의 두께는 CALOTEST와 XRF 두께 측정기를 이용하여 측정하였으며, 박막의 결정성과 내마모성은 X-선 회절분석기와 tribometer로 관찰하였다. 아크 전류를 변화시키면서 증착한 Cr-N 박막의 경우 층작율은 아크 전류가 50A에서 80A로 증가함에 따라 45nm/min에서 87nm/min으로 증가하였다. 그리고 바이어스 펄스의 duty-on 시간과 주파수가 증가할수도록 박막의 증착율은 감소함을 알 수 있었다. Duty-on 시간과 주파수의 증가는 기판에 오랫동안 이온의 충격을 가하므로서 상대적으로 가벼운 질소이온이 크롬과 결합하는 것을 방해하여 박막의 증착율이 감소할 것이다. 기판에 인가하는 바이어스 펄스의 duty-on 시간을 변화시키면서 증착한 Cr-N 박막에 대한 X-선 회절상을 조사한 결과 duty-on 시간이 20%인 경우에는 Crn(111), CrN(200)와 Crn(220) 피크 들만 나타나 입방정의 CrN 박막이 형성되었으며, duty-on 시간의 증가에 따라 $Cr_2N$ 상의 형성이 점점 많아져 80% duty-on 시간 경우에는 거의 CrN과 $Cr_2N$ 상이 공존하는 것으로 나타났다. 또한 duty-on 시간이 증가할수록 회절피크의 세기가 증가하여 결정화가 더 많이 진행되어짐을 알 수 있었다. 마찬가지로 바이어스 펄스이 주파수에 다른 결정성의 변화도 펄스의 주파수가 증가할수록 박막이 결정성이 좋아지고 $Cr_2N$ 상이 쉽게 형성되었다. 증착 진공도에 따른 결정성은 상대적으로 질소의 농도가 높은 낮은 진공도에서는 CrN 상이 주로 형성되었으며, 반대로 높은 진공도에서는 $Cr_2N$ 상이 많이 만들어졌다. 즉 $1.3{\times}10^{-2}Torr$의 증착 진공도에서는 CrN 상만이 보이는 반면 $9.0{\tiems}1-^{-2}Torr$ 진공도에서부터 $Cr_2N$ 상이 형성되기 시작하여 $5.0{\tiems}10^{-2}Torr$ 진공도에서는 두개의 상이 혼재되어 있음을 알 수 있었다. 박막의 내마모성을 조사한 결과 CrN 박막의 마찰 계수는 초기에 급격하게 증가한 후 0.5에서 0.6 사이의 값으로 큰 변화를 보이지 않았으며, $Cr_2N$ 박막도 비슷한 거동을 보였다.

• Archives of design research
• /
• v.19 no.2 s.64
• /
• pp.293-300
• /
• 2006

Mr. Miyazaki's heroines tend to be plucky young women who combine guileless decency with tough-mindedness. However, in his the latest film the female character often change herself into wise older women who sometimes serve as foils, sometimes as mother figures. His heroine, Sophie, starts out as a shy girl, but then a curse transforms her into 90-year-old. Her partner is Howl who supports and is supported by Sophie their mutual drawbacks. At first horrified by the change, she comes to embrace it as a liberation from anxiety, fear and self-consciousness, and discovers in herself a new zest for adventure. The castle is surely one of the most extraordinary contraptions to appear on screen recently, more ingenious in its way than the intergalactic armada. It ranges freely from place to place and is also, somehow, in several places at once, its magical front door opening onto different landscapes with the flip of a knob. It is not exactly haunted, but it is nonetheless infused with whimsical and sometimes somber spirits. Sophie, in both her incarnations, joins an impressive sisterhood of Miyazaki heroines, whose version of girl power presents a potent alternative to the mini-machismo that dominates American juvenile entertainment.

• Applied Chemistry for Engineering
• /
• v.26 no.4
• /
• pp.400-405
• /
• 2015

Traditional anti-reflective (AR) coating films prepared using tetraethylorthosilicate (TEOS) as a precursor absorbs water easily in addition to having a weak abrasion resistance. To improve the transmittance, hydrophobicity and abrasion resistance of AR coating film, various AR coating films were prepared using methyltrimethoxysilane (MTMS) as a precursor in addition to introducing a fluoroalkylsilane, acid catalyst, base catalyst and acid-base two step catalyst. The prepared AR coating films were then characterized by UV-Vis spectroscopy, contact angle analyzer, atomic force microscope (AFM), pencil scratch hardness test and cross-cut test. As a result, the transmittance of bare glass was 90.5%, while that of AR coating glass increased to 94.8% at curing temperature of $300^{\circ}C$. When the fluoroalkylsilane was added, the water contact angle of AR coating film increased from $96.3^{\circ}$ to $108^{\circ}$, indicating that the hydrophobicity of the film was greatly improved. The abrasion resistance of AR coating film was also improved by the acid catalyst, whereas the transmittance increased by the base catalyst. In the case of AR coating film prepared using an acid-base two step catalyzed reaction, both the transmittance and abrasion resistance of the film was synergistically enhanced as compared with those of AR coating films prepared without introduction of a catalyst.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.143-143
• /
• 2017

CrAlN 코팅은 높은 경도, 낮은 표면 조도 등의 상온에서의 우수한 기계적 특성 이외에 고온에서 안정한 합금상의 형성으로 인하여 우수한 내산화성 및 내열성을 보유하여 공구 코팅으로의 적용 가능성이 크다. 그러나 최근 공구사용 환경의 가혹화로 인하여 코팅의 내마모성 및 내열성 등의 물성 향상을 통한 공구의 수명 향상이 필요시 되고 있으며, 다양한 코팅 물질을 활용하여 다층 코팅을 합성함으로써 난삭재용 공구 코팅의 물성을 높이는 연구들이 진행되고 있다. 본 연구에서는 CrAlN 코팅과 WC-Co 6wt.% 모재 사이에 CrZrN, CrN, CrN/CrZrSiN 등의 중간층을 합성하여 CrAlN 코팅의 상온 및 고온 특성을 향상시키는 연구가 진행되었다. 합성된 코팅의 구조 및 물성을 분석하기 위해 field emission scanning electron microscopy(FE-SEM), nano-indentation, atomic force microscopy(AFM) 및 ball-on-disk wear tester를 사용하였다. 코팅의 고온 특성을 확인하기 위해 코팅을 furnace에 넣어 공기중에서 30분 동안 annealing 한 후에 nano-indentation을 사용하여 경도를 측정하였고, $500^{\circ}C$ annealing 코팅의 표면 조도 분석 및 $500^{\circ}C$에서 마찰마모시험을 실시하였다. CrAlN 코팅의 상온 특성을 분석한 결과, 모든 코팅의 경도(35.5-36.2 GPa)와 탄성계수(424.3-429.2 GPa)는 중간층의 종류에 상관없이 비슷한 값을 보인 것으로 확인됐다. 그러나, CrN/CrZrSiN 중간층을 증착한 CrAlN 코팅의 마찰계수는 0.33로 CrZrN 중간층을 증착한 CrAlN 코팅의 마찰계수(0.41)에 비해 향상된 값 보였으며, 코팅의 마모율 및 마모폭도 비슷한 경향을 보인 것으로 보아 코팅의 내마모성이 향상된 것으로 판단된다. 이것은 중간층의 H/E ratio가 코팅의 내마모성에 미치는 영향에 의한 결과로 사료된다. H/E ratio는 파단시의 최대 탄성 변형율로써, 모재/중간층/코팅의 H/E ratio 구배에 따라 코팅 내의 응력의 완화 정도가 변하게 된다. WC 모재 (H/E=0.040)와 CrAlN 코팅(H/E=0.089) 사이에서 CrN, CrZrSiN 중간층의 H/E ratio는 각각 0.076, 0.083 으로 모재/중간층/코팅의 H/E ratio 구배가 점차 증가함을 확인 할 수 있었고, 일정 응력이 지속적으로 가해지면서 진행되는 마모시험중에 CrN과 CrZrSiN 중간층이 WC와 CrAlN 코팅 사이에서 코팅 내부의 응력구배를 완화시키는 역할을 함으로써 CrAlN 코팅의 내마모성이 향상된 것으로 판단된다. 내열성 시험 결과, CrN/CrZrSiN 중간층을 증착한 코팅은 $1,000^{\circ}C$까지 약 28GPa의 높은 경도를 유지한 것으로 확인 되었다. $500^{\circ}C$ annealing 후 진행된 표면 조도와 마모시험 결과, 모든 코팅의 조도 값 및 마찰계수는 상온 값에 비해 증가하였으며 CrN/CrZrSiN 중간층을 증착한 CrAlN 코팅의 변화량이 가장 낮은 값을 보였다. 이는 CrZrSiN 중간층 내에 존재하는 $SiN_x$ 비정질상이 고온 annealing시에 산소 차폐막 역할을 하여, 코팅내의 잔류 산소에 의한 산화작용을 효과적으로 방지함으로써 코팅의 고온 특성이 향상된 것으로 판단된다.

• Journal of Labour Economics
• /
• v.41 no.1
• /
• pp.1-38
• /
• 2018

The paper investigates the determinants of female, maternal, and male employment in a comparable setting using an unbalanced panel data of 29 OECD countries from 2000-2013. Our empirical results show that early childhood childcare and education (ECEC) is positively associated with female employment. Furthermore, we find that ECEC does not hurt male employment. We also find that tax rates on the second earner are negatively associated with male employment as well as female employment. The estimated coefficients of ECEC, social expenditure, tax rates, and tertiary education attainment rates in maternal employment regressions are much larger in the absolute value than those in female employment regressions. Policy implications of our analysis are that an expansion of ECEC, a lower tax on secondary earner, and education are key to promote the total employment as well as female employment.