• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.6
• /
• pp.915-919
• /
• 2012

In constructing all kinds of equipment and steel structure, parts with discontinuities such as weld defects formed in the welded structure can generate fatigue cracks that results in damage or accidents. In this study, weld zones are investigated with X-rays and the latent images are put on film. Weld zone defects can be verified by developing the film. As weld defects are investigated by radiographic testing and correlated with the welding condition, more appropriate welding conditions can be found. According to the result of X-ray radiographic inspection of butt welding ATOS 80 high-strength steel with a thickness of 12mm, the best conditions for welding without creating weld defects are 4 weld-passes, a protective gas of 20% $CO_2$ and 80% Ar, a protective gas flow of 20L/min, a welding current of 200A, an arc voltage of 24V, a welding speed of 14.4cm/min, a welding rod angle of $50^{\circ}$, a welding gap of 5 mm with a ceramic base, and sand pre-heating to $160^{\circ}$ Celsius prior to welding.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.5
• /
• pp.625-634
• /
• 1986

The strain distribution on a welded aluminum alloy transition joint produced by a static tensile load has been measured using a moire method combined with photoelastic coating method. The test specimens were made of aluminum alloy 6061-T6 and 2014-T6 butt welded with ER-4043 filler metal, and were post welded heat treated (solid solution heat treatment 502.deg. C 70min.) and precipitated (artificial aging 171.deg. C 600min.) to cause an abrupt change of mechanical properties between the base metals and weld metal. The photoelastic epoxy rubber was cemented on the specimen grating which had been reproduced on the specimen surface by using an electropolishing. The measurements were compared with strains computed by Finite Element Analysis. The following results were abtained. (1) The maximum strain were distributed along the center line in the transverse directiion of the weld metal. (2) The strain gradient along the fusion line increased approaching the V-groove tip and the maximum value was observed at a quarter of width from the V-groove tip. (3) The moire method combined with photoelastic coating was proved very useful for real time strain measurement in the welded aluminum alloy transition joint.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.4
• /
• pp.2021-2026
• /
• 2013

In this study, the effect on the welding angle distortion was reviewed by carrying out a thermal elastic-plastic analysis while changing the cooling condition(width, length, and distance from weld torch to cooling torch) the back of the welding zone for the butt weld joint. The review results revealed that maximum 57% of reduction in the angle distortion was achieved when the distance between weld torch and cooling tip of 25mm, cooling length of 80mm, and cooling width of 30mm were maintained.

• Journal of Welding and Joining
• /
• v.28 no.4
• /
• pp.33-40
• /
• 2010

The purpose of this study is to establish a predictive equation of transverse residual stress at the thick FCA butt weldment of large container vessel. The variables used were restraint degree, yield strength of base material, thickness of weldment and welding heat input. Restraint degree at the thick weldment of container ship having the various welding sequence was calculated using FEA. From the result, the H-type specimen was designed to reproduce the level of restraint degree at the actual weldment of containership. Based on the results, the predictive equations of the mean value and the distribution of transverse residual stress at each location of the weldment were established using dimensional analysis and multiple-regression method. The predictive equations were verified by comparing with those measured by XRD in the actual weldment of the ship.

• Journal of Welding and Joining
• /
• v.28 no.1
• /
• pp.54-59
• /
• 2010

Ship Blocks are assembled by welding, and among them, welding between large blocks (Pre-erection stage) is used as feature of butt. In this process, local material has a experience of thermal cycle and become finally shrunk. As for inconsistency of shrunk weldments and adjacent regions, ship structure would be deformed locally and globally. Thermal distortion analyses are done for control of these processes, and methodologies capable of ship block size among them are using 2-D shell element in FEM. A shell element takes charge of plate, so it has its thickness which is important for angular distortion by welding. By the way, a butt-welding consists normally of several passes, and weldment thickness are different at each pass. If a calculated final one-time welding shrinkage is acting on the shell element whose thickness is same as it of plate, then deformation value must be underestimated. This research developed a methodology that total deformation after multi-pass welding can be analyzed by one time at shell element having original thickness of its plate. We use the SDB thermal distortion analysis method and verified by several experiment. The both experimental and analysis results showed good agreements.

• Journal of the Society of Naval Architects of Korea
• /
• v.46 no.1
• /
• pp.24-30
• /
• 2009

The purpose of this study is to investigate the fatigue strength in accordance with back plate of butt welded specimens. Fatigue life of butt welded specimens was presented for determining the effect of back plates in terms of fatigue strength. As a results, fatigue strength of butt welded specimens with steel back plate show a decrease as compared against the butt welded specimens with ceramic back plate. Compared with the fatigue strength with respect to the existence of steel back plate, the specimens without back plate were much higher than the specimens with back plate.

• Journal of the Society of Naval Architects of Korea
• /
• v.44 no.6
• /
• pp.598-604
• /
• 2007

The purpose of this study is to establish the predictive method of welding distortion and residual stress for the channel I butt SA (submerged arc) weldment using FEA. In order to do it, the heat input model for the weldment was defined as the combined heat source with the surface heat flux of gaussian distribution and volumetric heat source uniformly distributed within weld groove by comparing the shapes of molten pool and temperature distribution obtained by FEA with those of experiments. The arc efficiency of SA welding for two-dimensional FE analysis was evaluated as 0.85. The welding distortion and residual stress of the weldment obtained by FEA and heat input model proposed have a good agreement with those obtained by experiment. Based on the results, it was suggested that the proper heat input model should be required to evaluate the welding distortion for weldment.

• Journal of Welding and Joining
• /
• v.23 no.4
• /
• pp.73-80
• /
• 2005

Arc blow being occurred by Electro-Magnetic force(EMF) during the electric arc welding prevents the formation of a sound weldment. In this study, the effects of arc position, groove size, tack weld and base plate on the EMF in a butt-joint welding of mild steel plate are analyzed by a computer simulation based on the finite element method. The EMF can be numerically identified to be caused by a difference of the magnetic flux-density between ahead of and behind the arc in case that the workpiece locates asymmetrically around the uc. When there exists an air gap of groove ahead of the arc in the welding direction, the similar magnetic force has been producted regardless of the arc position and the gap size. The tack weld alleviates the magnetic force to about one fourth at the finish end of the workpiece. The magnetic force can be also significantly reduced with the base plate to about one fifth at the start end of the workpiece containing a tack weld.

• Journal of Welding and Joining
• /
• v.29 no.5
• /
• pp.63-71
• /
• 2011

Three-dimensional finite element analysis is performed to study the temperature distribution phenomenon of TIG assisted friction stir welding (TAFSW) between dissimilar plates (Al 6061-T6 and stainless steel 304). TAFSW is a solid-state welding process that integrates TIG (Tungsten Inert Gas) into a friction stir welding (FSW), to preheat the harder material ahead of FSW tool during welding. In order to facilitate the industrial application of welding, 3D numerical modeling of heat transfer has been carried out applying Finite Element Method (FEM). The temperature distribution due to heat generation during TAFSW on dissimilar materials joint is analysed using in-house solver. Moving heat source along with frictional heat between the work specimens and tool surface is considered to calculate the heat input. The analytical model used predicts successfully the maximum welding temperatures that occur on the dissimilar materials during TAFSW. Comparison with the infra red camera and thermocouple measurement results shows that the results from the current numerical simulation have good agreement with the measured data.

• Journal of Welding and Joining
• /
• v.31 no.2
• /
• pp.57-62
• /
• 2013

Magnesium has good castability and limited workability, so its products have been manufactured by almost casting processes. In this study, a pulsed Nd:YAG laser was used to butt-weld the sand casting magnesium alloys. And the effect of welding conditions such as peak power, pulse width, welding speed was evaluated in detail. As a result of this study, large underfill and plenty of spatter taken place under the conditions with high peak power. Thus, it is recommended to use low peak power and long pulse width to obtain good welds with deep penetration. It is also confirmed that the welding speed and pps(pulse per second) are directly connected at weld defects such as underfill, porosity.