• Electrical & Electronic Materials
• /
• v.7 no.5
• /
• pp.403-408
• /
• 1994

Dielectric and structural properties of $Ba_{1-x}$(Z $n_{1}$3/T $a_{2}$3/) $O_{3}$+1 mol% Mn $O_{2}$ (x=0, 0.01, 0.02, 0.03, 0.04) ceramics was investigated at microwave frequencies. With $Ba_{+2}$ shortage, the sinterability and the unloaded Q( $Q_{u}$) were much improved, and the ordering in B site and the lattice distortion was greatly enhanced and the structure approached the completely ordered structure. $Q_{u}$ was strongly correlated with these factors such as ordering ratio, lattice distortion and sinterability, and had the maximum value of 7500 at x=0.01. The dielectric constant was near 30 and the temperature coefficient of the resonant frequency was 2 ppm/.deg. C at x=0.01.1.1.1.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1190-1196
• /
• 2002

Microwave dielectric properties and multilayer characteristics $(1-x)BiNbO_4-xCaNb_2O_6$ (0${\le}$x${\le}$1.0) ceramics were investigated as a function of $CaNb_2O_6$ content. In the composition range of 0.25${\le}$x${\le}$0.75, the mixture phases of $BiNbO_4$ with stibotantalate structure and $CaNb_2O_6$ with columbite structure were detected and secondary phase or phase transition were not detected. Dielectric constant (K) of $(1-x)BiNbO_4-xCaNb_2O_6$ ceramics was largely dependent on the existing phase and could be estimated by the dielectric mixing rule calculated from maxwell equation. Typically, dielectric constant (K) of 26, quality factor (Qf) of 4300 GHz and Temperature Coefficient of resonant Frequency (TCF) of -18 ppm/${\circ}C$ were obtained for $0.5BiNbO_4-0.5CaNb_2O_6$ specimens with 0.8 wt% $CuV_2O_6$ sintered at 1000${\circ}C$ for 3h. The deviation of X-Y shrinkage and camber value of the multilayers obtained from $0.5BiNbO_4-0.5CaNb_2O_6$ green sheet sintered at 850∼950${\circ}C$ for 20 min. were smaller than those of $BiNbO_4$ multilayers.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.5
• /
• pp.217-222
• /
• 2007

Microwave dielectric properties of $(1-x)CaWO_4-xYNbO_4$ ceramics have been investigated as a function of $YNbO_4$ content($0.05{\leq}x{\leq}0.4$). A single phase with tetragonal scheelite structure was obtained up to x=0.10 and then the secondary phase with fergusonite structure was increased. With the increase of $YNbO_4$ content, apparent densities of the specimens were decreased. This results were due to the lower theoretical density of $YNbO_4(5.581g/cm^3)$ than that of $CaWO_4(6.117g/cm^3)$. Dielectric constant(K) and quality factor(Qf) were decreased with $YNbO_4$ content which could be attribute to the decrease of density and the increase of secondary phase. Temperature coefficient of resonant frequency (TCF) of the specimens with the $YNbO_4$ content was depended on dielectric mixing rule.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.2 s.31
• /
• pp.17-22
• /
• 2004

In this study, BNT($BaO-Nd_{2}O_3-TiO_2$) and $70P_{2}O_5-5B_{2}O_3-(25-x)BaO-xNa_{2}O$ glass-ceramic composites were fabricated and investigated in order to apply for low temperature cofired ceramic. The prepared BNT based glass-ceramic composites were sintered at $800{\sim}950^{\circ}C$ with the glass fit contents ranging from 10 to $15\;wt\%$. The properties such as sintering and dielectric property were investigated in the ceramic compositions according to the phosphate glass frit. The dielectric constant was varied between 10 to 40 and shrinkage rate was increased according to increasing glass frit.

• Journal of the Korean Ceramic Society
• /
• v.42 no.2 s.273
• /
• pp.132-139
• /
• 2005

Sintering behavior of $BaO-Nd_{2}O_3-TiO_2$ with a Pb-based glassceramics frit were investigated in order to understand an effect of glassceramics as a low temperature sintering agent on dielectric ceramics. A green sheet form was fabricated through tape casting method with the glassceramic fut added $BaO-Nd_{2}O_3-TiO_2$. The dispersion properties, rheological properties and final density of dielectric composit slurry as a function of amount and composition of organic additives was examined. The dispersants' addition was effective in controlling dispersion of the ceramics in solution. The addition of excessive dispersant showed adverse effect on dispersion. The prepared slurries, containing ceramic : powders, glass-ceramics and various kinds of organic viechles, exhibited typical shear thinning behavior. The best properties of tape casting appeared powder to solvent ratio 65 : 35 and amount of the binder 6 wt$\%$ and plasticizer 3 wt$\%$. The viscosity of the slurry was 677 cps and green/sintered density in the tape was $3.3 g/cm^3,\;5.56 g/cm^3$ respectively.

• Electrical & Electronic Materials
• /
• v.10 no.6
• /
• pp.533-540
• /
• 1997

The microwave dielectric properties of ((P $b_{1-x}$ C $a_{x}$)Zr $O_3$ and (P $b_{0.63}$,C $a_{0.37-x}$ $M_{x}$)Zr $O_3$(M=Mg,Sr) ceramics were investigated. In (P $b_{1-x}$ C $a_{x}$)Zr $O_3$ (X=0.33~0.40) ceramics, high quality factor and small temperature coefficient of resonant frequency were obtain in (P $b_{0.63}$C $a_{0.37}$)Zr $O_3$with perovskite structure. In the case of (P $b_{0.63}$C $a_{0.37-x}$M $g_{x}$)Zr $O_3$ dielectric constant temperature coefficient of resonant frequency increased and quality factor decreased due to increase of polarization of A-O bonding. When replacing Ca ion with Sr ion with large ion radius, polarization decreased with increased of bonding length and thus dielectric constant and temperature coefficient of resonant frequency decreased.decreased.creased.

• Electrical & Electronic Materials
• /
• v.10 no.9
• /
• pp.901-908
• /
• 1997

The microwave dielectric properties of (Na.$_{1}$2//Sm$_{1}$2/)TiO$_3$and (Li$_{1}$2//Nd$_{1}$2/)TiO$_3$ceramics were investigated. Dielectric constant quality factor and temperature coefficient of resonant frequency of (Li$_{1}$2//Nd$_{1}$2/)TiO$_3$ceramics sintered at 145$0^{\circ}C$ for 2 hours were 86.2, 2780(at 3.8GHz) and 215ppm/$^{\circ}C$respectively. The solid solution of X(Na.$_{1}$2//Sm$_{1}$2/)TiO$_3$-(1-X)(Li$_{1}$2//Nd$_{1}$2/)TiO$_3$increased delectric constant and quality factor were decreased. Whereas temperature coefficient of resonant frequency was optimized to zero at the composition of 0.6(Li$_{1}$2//Sm$_{1}$2/)TiO$_3$-0.4(Li$_{1}$2//Nd$_{1}$2/)TiO$_3$where dielectric constant and quality factor were 86.2, 95-(at 3.8GHz) respectively. Also band-pass filters made of this material were examined.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.165-169
• /
• 2004

Microwave dielectric properties and the behavior of low-temperature sintering of $Zn_{1-x}(Li_{1/2}La_{1/2})_xTiO_3$ ($0.01{\leq}x{\leq}0.05$) with 4 wt% $H_3BO_3$ were investigated as a function of $(Li_{1/2}La_{1/2})^{2+}$ content. The sintering temperature of the specimens can be reduced from $1150^{\circ}C$ to $875^{\circ}C$ with the addition of 4 wt% $H_3BO_3$ as a sintering agent. Dielectric constant (K) and Temperature Coefficient of resonant Frequency (TCF) with the substitution of ($(Li_{1/2}La_{1/2})^{2+}$ ion depended on dielectric mixing rule. Quality factor (Qf) depended on density and microstructure. Typically, K of 26.5, Qf of 19,030 GHz and TCF of 7.5 ppm$/^{\circ}C$ were obtained for the specimens with x=0.03 sintered at $875^{\circ}C$ for 3 h.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.1
• /
• pp.29-34
• /
• 2006

The effects of $B_2O_3$ addition on the low-temperature sintering behavior and microwave dielectric properties of $(Zn_{0.8}Mg_{0.2})TiO_3$ ceramic system were investigated. Highly dense samples were obtained at the sintering temperatures below $900^{\circ}C$. The $Q{\times}f_o$ values were determined by the microstructures and sintering shrinkages which are affected by the amount of $B_2O_3$ and sintering temperature. Temperature coefficient of resonance frequency($T_f$) changes to a positive value with increasing the amount of $B_2O_3$ due to the increased amount of rutile phase which is one of the reaction products between $(Zn_{0.8}Mg_{0.2})TiO_3$ and $B_2O_3$. For $6.19 moi.{\%}B_2O_3$-added $(Zn_{0.8}Mg_{0.2})TiO_3$ system, it exhibits ${\epsilon}_r$ = 23.5, $Q{\times}f_o$ = 53,000 GHz, and $T_f$ = 0 ppm/$^{\circ}C$ when sintered at $900^{\circ}C$ for 5 h.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.71-71
• /
• 2003

최근 통신용 전자부품의 소형화, 저가격화, 고기능화의 요구가 점점 더 증대되고 있으며 이를 위해서 기판의 배선밀도를 높이는 것과 개별 부품 또는 모듈의 크기와 무게를 줄이는 것이 절실히 필요하다. 본 연구에서는 저융점의 phosphate계 유리 프릿의 첨가를 통해 LTCC (Low Temperature Co-fired Ceramic) 에 적용 가능한 조성을 개발하고자 하였다. 마이크로파 용 유전재료로서 널리 사용되고있는 BNT (BaO-Nd$_2$O$_3$-TiO$_3$) 계 세라믹스에 저융점 유리 프릿의 양을 10-30wt% 범위로 변화시키면서 900-110$0^{\circ}C$ 범위에서 소결하여 이에 따른 수축률 변화와 상대밀도의 변화를 조사하였다 유리 프릿으로 P$_2$O$_{5}$-ZnO-BaO-Nd$_2$O$_3$ 계, P$_2$O$_{5}$-SnO-ZnO 계 2가지 조성의 유리를 사용하였다 그 결과로 소결체의 상대밀도는 소성온도가 900-110$0^{\circ}C$ 로 증가함에 따라 85-96% 로 증가하였고, 그 수축률은 소결온도 100$0^{\circ}C$ 에서 급격히 증가하였다. 이러한 결과는 저온 동시소성 세라믹 조성의 사용을 위해 좋은 결과가 예상된다.