• Journal of Power System Engineering
• /
• v.16 no.5
• /
• pp.76-82
• /
• 2012

Duplex stainless steels have the dual microstructure of austenite and ferrite phases. This steel exhibits generally a high corrosion resistance and higher mechanical strength compared with austenitic stainless steels. The steels used in the investigation have the chemical composition of Fe-22Cr-xNi-yMn-0.2N in which the contents of Ni and Mn were varied with maintaining the equal [Ni/Cr] equivalent. The fraction of ferrite phase was increased with the increase of annealing temperature. The impact factor of Mn element on the [Ni] equivalent was amended on the basis of the results of the investigation. 4Mn-2Ni alloy showed the highest pitting corrosion resistance. The fraction ratio, grain size and misorientation angle between grains were measured, and the correlation with pitting potential was investigated.

• Journal of Korea Foundry Society
• /
• v.43 no.5
• /
• pp.230-240
• /
• 2023

The pitting corrosion behavior of 329LD cast lean duplex stainless steel and CF3M cast austenitic stainless steel was investigated in chloride environments. The pitting corrosion resistance of the 329LD alloy was superior to that of the CF3M alloy because the pitting potential, passive region, and critical pitting temperature of the low Ni-low Mo 329LD alloy were higher than those of the high Ni-medium Mo commercial CF3M alloy. There are two main reasons for the enhancement of the pitting corrosion resistance of high Cr-low Momedium N 329LD alloy compared to the low Cr-medium Mo CF3M alloy: First, the pitting resistance equivalent number (PREN_δ+γ) value of the 329LD alloy is higher than that of the CF3M alloy. Second, the passive region of the 329LD alloy is larger than that of the CF3M alloy. It indicates that the synergistic effect of the three elements by adding high Cr and low Mo-medium N to the 329LD alloy enhances the passivity of the passive film, thereby increasing the pitting corrosion resistance. It was verified that based on the PREN_γ of austenite (γ) and PREN_δ of ferrite (δ) values calculated using an N-factor of 16, the pitting corrosion of the 329LD alloy was selectively initiated at the γ-phases because PREN_γ value of austenite (γ) was smaller than that of ferrite (δ), and finally propagated from the γ-phase to the δ-phase.