장태석;조대형
- Journal of the Korean Magnetics Society
- /
- v.7 no.4
- /
- pp.173-179
- /
- 1997
Change in phases, microstructures, and magnetic properties by the variation of quench rate and heat treatment were investigated for melt-spun $Fe_{77}Pr_{15}C_8$ ribbons. The amorphization of as-spun ribbons increased as the quench rate increased. As a result, the ribbon quenched at 40 m/s was almost entirely amorphous. Similarly to cast alloys, the primary phase in crystalline ribbons quenched at 10 m/s was $\alpha$-Fe followed by the secondary $Fe_{17}Pr_2C_x$. Crystalline phases were still dominant in the ribbon spun at 20 m/s, but in this case crystallization of $Fe_{17}Pr_2C_x$ was remarkable with a little suppression of $\alpha$-Fe. At 30 m/s an amorphous phase obviously dominated in the as-spun ribbons with small fraction of crystals. Therefore, substantial amount of hard magnetic $Fe_{14}Pr_2C$ was not obtained from the as-spun state but, as in cast alloys, produced only by a solid-state transformation. Within a few minutes fine grains of $Fe_{14}Pr_2C$ were easily obtained at relatively low temperature when the degree of amorphization of as-spun ribbons was higher. The grain size of $Fe_{14}Pr_2C$ was well less than 1${\mu}{\textrm}{m}$. The ribbons quenched at 20 or 30 m/s yielded higher coercivities after heat treatment.
PDF

Choi, Y.J.;Jang, S.J.;Kim, S.W.;Jeon, B.S.;Kim, S.M.;Song, C.B.;Kim, Y.C.;Namkung, J.
- Journal of the Korean Magnetics Society
- /
- v.25 no.1
- /
- pp.4-9
- /
- 2015
This study was carried out to investigate a influence of humidity variation (%) on the magnetic properties and the surface flaws in the fabrication of Fe-based $Fe_{78}Si_9B_{13}$ amorphous alloy ribbon by Planar Flow Casting process. As a result, the size of the air pocket and the droplet which is observed in the contact surface and the free face of the amorphous alloy ribbon becomes large when the humidity increases and the size highly increases with the surface roughness at the same time. Especially, the surface roughness value which is made in the 65 % of the humidity is the lowest in the contact surface ($Ra=0.60{\mu}m$, $Rz=3.11{\mu}m$) and the free face ($Ra=0.47{\mu}m$, $Rz=3.00{\mu}m$). Also, in case of the soft magnetic property of the magnetic core which is made with the toroidal core of $23(OD)^*20(ID)^*20(H)$ size, in the sample of the amorphous alloy ribbon which is made in 65% of the humidity, the most excellent value is gained as $B_s(B_{700})=1.055T$, $H_c=0.083Oe$, permeability = 1,197 and core loss = 0.276W/kg.
https://doi.org/10.4283/JKMS.2015.25.1.004 인용 PDF KSCI