• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.3
• /
• pp.477-486
• /
• 2008

Acrylic resin is widely used in dental practice. However, the residual monomer in acrylic resin could act as a negative biocompatability on human body. The aim of this study was to evaluate the amount of the monomer elution from polymerized orthodontic acrylic resin. Orthodontic acrylic resin was used in the study. The curing condition of the resin was controlled by temperature, pressure, aquatic and atmospheric environment. The duration and amount of monomer elution and timedependent plot was recorded by high performance liquid chromatography. The result showed that the only monomer eluted from the resin was methyl methacrylic acid. And the amount of the monomer elution has diminished considerably by time progress especially within 24 hours. Furthermore, elution of the residual monomer was significantly lower in group of pressure, moisture and elevated temperature than control (p<.05). According to this study, it was thought that the elution of residual monomer might be influenced by curing environment.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.2
• /
• pp.247-255
• /
• 2004

The purpose of this study was to examine the effects of resin composite monomers (Bis-GMA, TEGDMA, EGDMA, UDMA, HEMA, Camphorquinone) on the growth of the two cariogenic bacteria, Streptococcus mutans and Streptococcus sobrinus. We obtained the following results : 1. The growth rate of S. mutans and S. sobrinus was decreased significantly in the group of all composite resin monomer at a concentration of 0.03mmo1/L(P<0.01). 2. The growth rate of S. mutars in the group of UDMA at a concentration of 0.01 mmol/L and the group of CQ at a concentration of 0.005 mmol/L, 0.01 mmol/L was decreased significantly compared to the control group(P<0.01). 3. The growth rate of S. sobrinus in the group of HEMA, UDMA at a concentration of 0.01 mmol/L and the group of CQ at a concentration of 0.005mmol/L. 0.01mmo1/L was decreased significantly compared to the control group (P<0.01). 4. The growth rate of S. sobrinus in the group of EGDMA at a concentration of 0.001, 0.01, 0.03mmo1/L was decreased significantly compared to the control group(P<0.01) and were showed to be statistically significant difference between experimental groups(P<0.01).

• Restorative Dentistry and Endodontics
• /
• v.36 no.4
• /
• pp.313-323
• /
• 2011

Objectives: This study investigated the optimal combination of 3-component photoinitiation system, consisting of CQ, p-octyloxy-phenyl-phenyl iodonium hexafluoroantimonate (OPPI), and 2-dimethylaminoethyl methacrylate (DMAEMA) to increase the degree of conversion of resin monomers, and analyze the effect of the ratio of the photoinitiator to the co-initiator. Materials and Methods: Each photoinitiators (CQ and OPP) and co-initiator (DMAEMA) were mixed in three levels with 0.2 wt.% (low concentration, L), 1.0 wt.% (medium concentration, M), and 2.0 wt.% (high concentration, H). A total of nine groups using the Taguchi method were tested according to the following proportion of components in the photoinitiator system: LLL, LMM, LHH, MLM, MMH, MHL, HLH, HML, HHM. Each monomer was polymerized using a quartz-tungsten-halogen curing unit (Demetron 400, USA) for 5, 20, 40, 60, 300 sec and the degree of conversion (DC) was determined at each exposure time using FTIR. Results: Significant differences were found for DC values in groups. MMH group and HHM group exhibited greater initial DC than the others. No significant difference was found with the ratio of the photoinitiators (CQ, OPPI) to the co-initiator (DMAEMA). The concentrations of CQ didn't affect the DC values, but those of OPPI did strongly. Conclusions: MMH and HHM groups seem to be best ones to get increased DC. MMH group is indicated for bright, translucent color and HHM group is good for dark, opaque colored-resin.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.3
• /
• pp.298-307
• /
• 2010

The purpose of this study was to assess the effect on oxygen inhibition layer(OIL) for the interfacial bonding between resin composite layers, including shear bond strength, fracture modes and degree of conversion. The first layer of specimen was filled with Z-250(shade A3) and was cured for 40s. The second layer of specimen was filled with same composite(shade A1) and was cured for 40s. The first layer of specimens for each group were prepared by methods as followings. Control(curing in atmospheric air), Group1(curing against Mylar strip), Group2(scrubbed with a acetone-soaked cotton), Group3(using Tescera light cup), Group4(using Tescera heat cup), Group5(stored in disti1led water for 30days at $37^{\circ}C$), Group6 (using bonding agent). The results were as follows: 1. There was no statistically significant different shear bond strength between control and group 1(p>0.05). 2. Group 2 showed significantly lower shear bond strength than control and group 1(p<0.05). 3. The observation of the fracture surface leads to the evidence that a major difference occurs in the case of control, group1 and group 3 samples which break mainly cohesively while the other groups break in majority adhesively. 4. The results of FTIR showed that the degree of conversion was the highest in group 2 and the lowest in control group(p<0.05). It can be concluded that an OIL is not necessary for bonding with composite resin. But if a reduced critical amount of the unreacted monomer is present, it was detrimental to bonding additional layers of composite. Further study, such as the quantitative analysis of the unreacted monomer are required.

• The Journal of Korean Academy of Prosthodontics
• /
• v.50 no.2
• /
• pp.112-118
• /
• 2012

Purpose: The purpose of this study was to evaluate the difference in shear bonding strength between resin cements to dental materials when a universal primer (Monobond plus) was applied in place of a conventional primer. Materials and methods: Four groups of testing materials: gold alloy (Argedent Euro, n = 16), non precious metal (T-4, n = 20), zirconia (Cercon, n = 20) and glass ceramic (IPS e.max press, n = 20), were fabricated into discs, which were embedded in an acrylic resin matrix. The gold alloy specimens were airborne-particle abraded, 8 of the specimens were coated with Metal primer II, while the remaining 8 specimens were coated with Monobond plus. The non precious and zirconia specimen were airborne-particle abraded then, the control group received Alloy primer coating, while the other was coated with Monobond plus. Glass ceramic specimens were etched. 10 specimens were coated with Monobond-S and the remaining specimens were coated using Monobond plus. On top of the surface, Multilink N was polymerized in a disc shape. All of the specimens were thermal cycled before the shear bonding strength was measured. Statistical analysis was done with Two sample $t$-test or Mann-Whitney U test (${\alpha}$=.05). Results: There were no significant differences in bonding strength depending on the type of primer used in the gold alloy and glass ceramic groups ($P$>.05), however, the bonding strengths of resin cements to non precious metal and zirconia groups, were significantly higher when the alloy primer was used ($P$<.05). Conclusion: Within the limitations of this study, improvement of universal primers which can be applied to all types of restorations is recommended to precious metals and zirconia ceramics. But, the bond strengths of non precious metals and zirconia ceramics were significantly lower when compared to a 10-MDP primer. More research is needed to apply universal primers to all types of restorations.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.2
• /
• pp.284-292
• /
• 2005

The aim of this study was to identify and quantify the major or detectable monomers released from any of five commercially-available, light-cured pit and fissure sealants with three different light sources : conventional halogen light curing unit, plasma arc light curing unit and LED curing unit. After curing, specimens were immediately immersed in distilled water for different time intervals. The time related release of monomers were analyzed by high performance liquid chromatography(HPLC). Identification and quantitative analysis of monomers were performed by the comparison of the elution time and the absorption peak height of the eluates with those of the authentic sample. The result of this study can be summarized as follows. 1. Standard solution peaks with retention times of 2.3, 3.2, 5.6, 6.5, 10.4 minutes were identified as BPA, TEGDMA, UDMA, Bis-GMA, Bis-DMA, respectively. 2. None of the chromatograms of the tested sealants displayed peaks with the same retention time as that of the standard solution, except for TEGDMA. 3. The highest release rate of TEGDMA was observed during the 12hr period for all samples and declined thereafter. 4. The elution of TEGDMA from curing with Halogen curing unit for 20 second and LED for 10 second was less than that resulting from curing with Plasma arc for 3 second. 5. TEGDMA was detected at much lower levels in eluates from the Pit & Fissure $Sealant^{TM}$ than other sealants. The elution of TEGDMA from the $Helioseal^{(R)}$ F cured with Halogen light curing unit, the $Concise^{TM}$ cured with Plasma arc curing unit and the $Teethmate^{(R)}$ F-1 cured with LED curing unit were higher than other sealants.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.38 no.1
• /
• pp.18-25
• /
• 2022

Purpose: This study aimed to evaluate the color stability and antibacterial properties of the surface of polyethyl methacrylate (PEMA) resin with zirconia nanoparticles added. Materials and Methods: The control group was pure PEMA resin, and the experiment group was PEMA resin 15 mm in diameter and 2.5 mm in thickness disk-shaped specimens with 2, 4 and 8 w/v% of zirconia nanoparticles added, which were respectively divided into Group Z2, Group Z4, and Group Z8. After analyzing the surface roughness and color stability of the specimens, their antibacterial properties were evaluated using Porphyromonas gingivalis (P. gingivalis). The Statistical analysis was performed using when normality was met in the Shapiro-Wilk test, one-way ANOVA was used to test parameters, and Tukey's test was used as a post hoc test. When normality was not met, the Kruskal-Wallis test, a non-parametric test was used (P < 0.05). Results: The surface roughness measurement found that there was no significant difference between the experimental and control groups. The color stability evaluation showed that the Z2, Z4, and Z8 groups were within the color range of natural teeth. The adhesion of P. gingivalis was evaluated to be significantly reduced in Group Z2 compared to the control group (P < 0.05). In the Z2 group, Z4 group, and Z8 group, dead cells bacteria than the control group were observed. Conclusion: In conclusion, PEMA resin with zirconia nanoparticles added was within the range of natural teeth in color and reduced the adhesion of P. gingivalis.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.