• Membrane Journal
• /
• v.34 no.1
• /
• pp.50-57
• /
• 2024

In this experiment, Pd-Ag-Cu membrane was manufactured using electroless plating on an α-Al₂O₃ support. Pd, Ag and Cu were each coated on the surface of the support through electroless plating and heat treatment was performed for 18 h at 500℃ in H₂ in the middle of electroless plating to form Pd alloy. The surface of the Pd-Ag-Cu membrane was observed through Scanning Electron Microscopy (SEM), and the thickness of the Pd membrane was measured to be 7.82 ㎛ and the thickness of the Pd-Ag-Cu membrane was measured to be 3.54 ㎛. Energy dispersive X-ray spectroscopy and X-ray diffraction analysis confirmed the formation of a Pd-Ag-Cu alloy with a composition of Pd-78wt%, Ag-8.81wt% and Cu-13.19wt%. The gas permeation experiment was conducted under the conditions of 350~450℃ and 1~4 bar in H₂ single gas and H₂/N₂ mixed gas. The maximum H₂ flux of the hydrogen separation membrane measured in H₂ single gas is 74.16 ml/cm²·min at 450℃ and 4 bar for the Pd membrane and 113.64 ml/cm²·min at 450℃ and 4 bar for the Pd-Ag-Cu membrane. In the case of the separation factor measured in H₂/N₂ mixed gas, separation factors of 2437 and 11032 were measured at 450℃ and 4 bar.