• Korean Chemical Engineering Research
• /
• v.52 no.6
• /
• pp.807-813
• /
• 2014

The Ag-impregnated activated carbon was produced from bamboo activated carbon by soaking method of silver nitrate solution. The carbonization and activation of raw material was conducted at $900^{\circ}C$. Soaking conditions are the variation of silver nitrate solution concentration (0.002~0.1 mol/L) and soaking time (maximum 24 h). The specific surface area and pore size distribution of the prepared activated carbons were measured. Also, NO and activated carbon reaction were conducted in a thermogravimetric analyzer in order to use for de-NOx agents of used activated carbon. Carbon-NO reactions were carried out with respect to reaction temperature ($20{\sim}850^{\circ}C$) and NO gas partial pressure (0.1~1.8 kPa). As results, Ag amounts are saturated within 2h, Ag amounts increased 1.95 mg Ag/g (0.2%)~ 88.70 mg Ag/g (8.87%) with the concentration of silver nitrate solution in the range of 0.002~0.1 mol/L. The specific volume and surface area of bamboo activated carbon of impregnated with 0.2% silver were maximum, but decreased with increasing Ag amounts of activated carbon due to pore blocking. In NO reaction, the reaction rate of impregnated bamboo activated carbon was retarded as compare with that of bamboo activated carbon. Measured reaction orders of NO concentration and activation energy were 0.63[BA], 0.69l[BA(Ag)] and 80.5 kJ/mol[BA], 66.4 kJ/mol[BA(Ag)], respectively.

• Korean Chemical Engineering Research
• /
• v.54 no.5
• /
• pp.671-677
• /
• 2016

The impregnated alkali metal (Na, K), and the alkali earth metal (Ca, Mg) activated carbons were produced from the bamboo activated carbon by soaking method of alkali metals and alkali earth metals solution. The carbonization and activation of raw material was conducted at $900^{\circ}C$. The specific surface area and the pore size distribution of the prepared activated carbons were measured. Also, NO and activated carbon reaction were conducted in a thermogravimetric analyzer in order to use for de-NOx agents of the used activated carbon. Carbon-NO reactions were carried out in the nonisothermal condition (the reaction temperature $20{\sim}850^{\circ}C$, NO 1 kPa) and the isothermal condition (the reaction temperature 600, 650, 700, 750, 800, $850^{\circ}C$, NO 0.1~1.8 kPa). As results, the specific volume and the surface area of the impregnated alkali bamboo activated carbons were decreased with increasing amounts of the alkali. In the NO reaction, the reaction rate of the impregnated alkali bamboo activated carbons was promoted to compare with that of the bamboo activated carbon [BA] in the order of BA(Ca)> BA(Na)> BA(K)> BA(Mg) > BA. Measured the reaction orders of NO concentration and the activation energy were 0.76[BA], 0.63[BA(Na)], 0.77[BA(K)], 0.42[BA(Ca)], 0.30 [BA(Mg)], and 82.87 kJ/mol[BA], 37.85 kJ/mol[BA(Na)], 69.98 kJ/mol[BA(K)], 33.43 kJ/mol[BA(Ca)], 88.90 kJ/mol [BA(Mg)], respectively.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.24 no.1
• /
• pp.3-10
• /
• 2016

Effects of acid ($HNO_3$ and HCl) modification on the adsorption properties of Pb(II) and Cu(II) onto bamboo-based activated carbon (BAC) were investigated through a series of batch experiments. The carbon content increased and oxygen content decreased with acid treatment. $HNO_3$ induced carboxylic acids and hydroxyl functional groups while HCl added no functional group onto BAC. The pseudo-second order model better described the kinetics of Pb(II) and Cu(II) adsorption onto experimented adsorbents, indicating that the rate-limiting step of the heavy metal sorption is chemical sorption involving valency forces through sharing or exchange of electrons between the adsorbate and the adsorbent. The equilibrium sorption data followed both Langmuir and Freundlich isotherm models. The adsorption capacities of BAC were affected by the surface functional groups added by acid modification. The adsorption capacities were enhanced up to 36.0% and 27.3% for Pb(II) and Cu(II), respectively by the $HNO_3$ modification, however, negligibly affected by HCl.

• Journal of the Korea Institute of Building Construction
• /
• v.11 no.5
• /
• pp.452-458
• /
• 2011

Bamboo is representing environmentally friendly building finishing materials as proven in the former researches. The purpose of this study is to evaluate the application properties of cementitious materials modified with bamboo charcoal as building finish materials. Flow test in fresh condition was conducted to assess the workability. Compressive and bending strength were measured after harding. As the thermal properties, thermal conductivity and density were measured. The properties were surpassing over them in case of using the pine charcoal in every tests. The thermal conductivity of them increased with the modified ratio. After the modified ratio 50%, the thermal conductivity decreased. Insolation and absorption performance is due to the lower density by modification of bamboo charcoal.

• Journal of Korean Society of Environmental Engineers
• /
• v.38 no.3
• /
• pp.144-149
• /
• 2016

The metal-impregnated activated carbon was produced from bamboo activated carbon by soaking method of metal nitrate solution. The carbonization and activation of raw material was conducted at $900^{\circ}C$. The specific surface area and pore size distribution of the prepared activated carbons were measured. Also, NO and activated carbon reaction were conducted in a thermogravimetric analyzer in order to use as de-NOx agents of used activated carbon. Carbon-NO reactions were carried out with respect to reaction temperature ($20^{\circ}C{\sim}850^{\circ}C$) and NO gas partial pressure (0.1 kPa~1.8 kPa). As results, the specific volume and surface area of bamboo activated carbon impregnated with copper were decreased with increasing Cu amounts of activated carbon. In NO reaction, the reaction rate of Cu impregnated bamboo activated carbon[BA(Cu)] was promoted to compare with that of bamboo activated carbon[BA]. But the reaction rate of Ag impregnated bamboo activated carbon[BA(Ag)] was retarded. Measured reaction orders of NO concentration and activation energy were 0.63[BA], 0.92[BA(Cu)], and 80.5 kJ/mol[BA], 48.5 kJ/mol[BA(Cu)], 66.4 kJ/mol[BA(Ag)], respectively.

• Food Engineering Progress
• /
• v.14 no.3
• /
• pp.249-255
• /
• 2010

Ten commercial activated carbons (ACs) prepared from four different sources (bamboo, wood, peat, and coal) were evaluated for their adsorptive efficiency of six volatile compounds (isoamyl alcohol, hexanal, furfural, ethyl lactate, ethyl octanoate, 2-phenyl ethanol) which were dissolved in a 30% alcoholic model solution. These six volatile compounds are frequently found in alcoholic beverages and possibly contribute to physiological hangover due to their high concentrations. They are also generally regarded as off-flavor compounds at certain levels in alcoholic beverages such as whisky and vodka. Two hundred mL of 30% alcoholic solutions containing these six volatile compounds were treated with 0.2 g of ACs while stirring for 16 hr; the treated solutions were then measured for their adsorptive efficiencies (or removal efficiencies) by gas chromatographic analysis using two different sampling methods (direct liquid injection and headspace-solid phase microextraction). The adsorptive efficiencies of the ACs varied depending on the identity of the volatile compounds and the source material used for making the ACs. Ethyl octanoate, 2-phenyl ethanol, and hexanal were removed at high efficiencies (34-100%), whereas isoamyl alcohol, ethyl lactate, and furfural were removed at low efficiencies (5-13%). AC prepared from bamboo showed a high removal efficiency for isoamyl alcohol, aldehydes (hexanal and furfural), and 2-phenyl ethanol; these major fusel oils have been implicated as congeners responsible for alcohol hangover.

• Korean Journal of Microbiology
• /
• v.45 no.4
• /
• pp.354-361
• /
• 2009

This study was carried out to develop an effective biocarrier-mediated bioaugmentation technology which will be useful for remediation of the crude oil-contaminated marine sediments. Enrichment of several microbial communities was made from several oil-polluted seashore sites and the two distinctively functional consortia have been successfully selected. These two consortia were grown together and used to manufacture the microbial agents for bioaugmentation of marine sediments polluted with crude oil. The most dominant species in the mixed culture was identified as Alcanivorax borkumensis based on pure culture and DGGE analysis. Bioaugmentation of oil-polluted marine sediments with the microbial agent MA-2 formulated using the mixed culture and biocarriers (activated carbon and minerals) was more effective, especially in combination with an oxygen producing (releasing) compound (ORC). Ninty percent of TPH was removed in the presence of ORC in 35 days while 74% in the absence of ORC. This indicated that the indigenous consortial degraders could be immobilized on the active carbon as a biocarrier to manufacture microbial agents and then effectively bioaugmented for remediation of the oil-polluted sediments.