• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.173-180
• /
• 2009

Very-early strength latex-modified concrete(below ; VES-LMC) was developed for possible early-opening-to-traffic after overlay of bridge deck concrete. The purpose of this study is to analyze the cause of map, transverse and longitudinal cracking in VES-LMC and to provide a control method for minimizing occurrence of cracking. The proposed prevention method against map and transverse cracking was verified by field data. VES cement was modified as the unit cement content was reduced from 390kg/$m^3$ to 360kg/$m^3$. The maximum size of coarse aggregate was increased from 13mm to 19mm. The wire mesh and steel fiber were adopted in concrete mixture. From the results, the proposed prevention method against map and transverse cracking was verified since structural cracking was not occurred until 3 years after overlay.

• Journal of the Korea Concrete Institute
• /
• v.13 no.6
• /
• pp.575-583
• /
• 2001

The purpose of this study is to present the method of utilizing the recycled aggregate that are obtained from waste concrete as the concrete aggregate. We manufactured the recycled aggregate concrete with compressive strength of over 300kgf/㎠ to increase its weaker strength than the normal concrete, and compared the physical features of the recycled aggregate concrete with that of the normal concrete. As a result of the study, the mechanical performances such as compressive and tensile strength were generally reduced as the mixing rate of the recycled aggregate increased; however, it was possible to manufacture the concrete with the compressive strength of 300∼600kgf/㎠ using the adequate mixing material such as unit quantity of cement, compounding water and silicafume. However, a continuous study on long-term durability performance is required to manufacture and utilize the recycled aggregate concrete for the structure.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.102-103
• /
• 2020

Research for heat insulation of buildings is being carried out, in which a heat exchange barrier is used around the openings and balcony parts as a method for heat exchange blocks. However, the preparation for a fire is inadequate. In order to improve the EPS used as a heat exchange barrier in an attempt to solve this, there is a study on lightweight foamed concrete, but as the amount of EPS used for strengthening fire resistance increases, it becomes lower. There is no strength applied to buildings, and also. There is a limit to the amount of EPS used. In the study, we use oyster shells to secure the EPS replacement rate limit of lightweight Foamed concrete, and try to measure the change of physical properties depending on the unit cement content.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.39 no.1
• /
• pp.75-82
• /
• 1997

건설기술과 산업의 발전에 따라 구조물은 대형화되어 가고, 건설공사의 급격한 팽창으로 골재 수용량이 급증함에 따라 천연골재자원은 점차 부족현상을 면치 못할 처지에 있다. 또한, 무리한 천연골재의 채취는 자연환경을 훼손시킬 뿐만 아니라 자연보호 측면에서도 심각한 공해문제로 대두되고 있어 공급량 부족현상은 날로 심화되고 있다. 이에 세계 몇몇 나라에세는 산업부산물을 이용한 골재 생산으로 공해예방과 폐기물 활용방법을 연구하고 있다. 산업부산물중 플라이 애쉬 생산량은 전 세계적으로 매년 약 2억여톤에 달하고 있으나 이중 일부만 활용되고 있는 실정이다. 이와같은 부산물을 활용하기 위한 일환으로 산업부산물인 PFA(Pulverized Fuel Ash)로 만든 인공경량골재의 년생산량이 영국은 600,000$m^3$, 미국은 300,000$m^3$이며, 매년 증가주세에 있다. 고성능 경량골재 콘크리트는 단위중량의 증가없이 내구성과 강도를 향상시켜 실용화 측면에서 경제적인 효과가 있으며, 플라이 애쉬로 만든 경량골재는 시멘트와의 친화력이나 접착면에서 우수한 것으로 알려져 있다. 본 시험에 사용한 골재는 플라이 애쉬로 만든 인공경량 조골재와 강모래이고, 결합제로서 프틀랜드 시멘트를 사용하였다. 부수적인 결합재로서는 플라이 애쉬, 슬래그, 실리카 흄을 사용하였으며, 고성능 경량골재 콘크리트를 개발코자 재령 28일과 180일의 압축강도가 각각 50MPa와 60MPa가 되도록 배합설계를 하였다. 본 연구에서는 플라이 애쉬, 슬래그, 시리카 흄과 같은 산업부산물을 혼입했을때 경량골재 콘크리트의 압축강도, 휨강도, 동탄성계수, 공극체적, 공극률, 단위중량, 공극 크기별 분포등의 변화를 실험적으로 구명하여 재반 구조용 콘크리트에 활용하기 위한 기초자료를 마련코저 한다.있어 특정한 발육단계의 난포 사망기전을 연구하기 어렵다. 또한 난포는 생체 내에서 다양한 호르몬을 동시에 분비하기 때문에 특정한 난소국부호르몬이 사망기전에 미치는 영향을 조사하기 힘든 점이 있다. 최근 들어 난포체외배양이 다양하게 개발되면서, 이러한 어려운 점을 극복할 수 있게 되었다. 본 논문은 각 발육단계의 난포를 절단해 체외배양하면서, apoptosis DNA 절단 현상을 이용하여 각종 난소국부 호르몬들이 난포발육단계별로 사망기전에 미치는 영향을 요약해 보였다. 난포는 발육하면서 점차 복잡한 호르몬 경로를 생존을 위해 필요로 한다. Prevulatory난포생존에 필요한 난소국부호르몬들은 early antral 단계의 난포에서는 그 미치는 영향이 감소되다가 preantral단계의 난포에서는 영향을 전혀 미치지 못했다. 단지 예외는 cGMP처리로써, 세포내 cGMP수준을 일정하게 유지시켜주는 것이 난포발육단계에 무관하게 생존에 중요한 인자로, 장래 연구는 난포 세포내의 cGMP수준을 조절하는 기작을 규명하는데 있을 것이다.인정되지 않았다. 7. 농지보전 처리구인 배수구와 초생수로구는 비처리구에 비해 낮은 침두 유출량과 낮은 토양유실량을 나타내었다.구보다 14% 절감되는 것으로 나타났다.작용하는 것으로 사료된다.된다.정량 분석한 결과이다. 시편의 조성은 33.6 at% U, 66.4 at% O의 결과를 얻었다. 산화물 핵연료의 표면 관찰 및 정량 분석 시험시 시편 표면을 전도성 물질로 증착시키지 않고, Silver Paint 에 시편을 접착하는 방법으로도 만족한 시험 결과를 얻을 수 있었다.째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의 발달과 밀접한 관계가

• Environmental and Resource Economics Review
• /
• v.4 no.2
• /
• pp.307-344
• /
• 1995

이 논문은 산업공해의 발생 요인을 규명하는 부분과 여기서 규명된 요인에 따라 배출량을 규제하고 그 규제효과를 추정하는 두 가지 부분으로 이루어져 있다. 이 논문에서는 환경(環境) 산업연관(産業聯關) 분석(分析) 모형(模型)을 이용하여 우리 나라의 산업(産業) 공해(公害) 배출(排出) 요인(要因)을 규명하고자 하였다. 이 분석의 결과 얻은 잠정적 결론은 첫째, 우리 나라는 지난 10년간 에너지 절약적(節約的)인 기술개발(技術開發)등 에너지의 효율성과 생산기술(生産技術)(투입구조(投入構造))의 개선 등 생산기술측면에서는 대기오염 배출량을 감소시키는 구조적 변화가 있었던 반면에, 수출입(輸出入) 구조(構造)등 수요 측면에서는 그 배출량을 증가시키는 구조적 변화가 발생하였다. 그러나 전체적으로 구조적 요인은 공해 배출량을 증가시키지 않은 반면 경제 성장에 따른 생산 규모의 확대로 총 배출량은 크게 증가하였다. 산업공해의 배출량을 감축시키기 위한 한 가지 정책수단(政策手段)으로 우리는 일정 율의 탄산까스 배출량(排出量)을 규제하기 위해 필요한 공해 제거 비용을 계산하고 배출 단위 제거비용을 Pigou적 공해조세(公害租稅)로 제시함으로서 일정 배출량 감축 효과를 가지는 공해세를 계산하고자 시도하였다. 이 같은 배출 규제(規制)에 의한 물가상승(物價上昇)의 파급정도(波及程度)는 각 산업의 공해제거(公害除去)를 위한 중간투입물(中間投入物) 수요(需要)와 규제대상(規制對象) 산업(産業)과의 산업연관(産業聯關) 정도(程度)에 따라 상이하다. 배출량(排出量)이 큰 6대(大) 공해산업(公害産業)에 대한 규제(規制)는 자기(自己) 가격상승율(價格上昇率)이외에 산업연관효과(産業聯關效果)의 차이 때문에 산업별로 다른 물가 파급효과를 발생시킨다는 것을 보였다. 특히 석유와 석탄 등의 에너지에 대한 탄산까스 배출 규제는 규제 산업의 자기 가격을 매우 높은 율로 상승시키며, 각각 화학, 고무, 섬유, 의복 제품과 1 차금속, 전력 가스, 조립금속, 시멘트 등에 높은 물가 파급효과를 나타내므로서 이산화탄소의 배출 규제 내지 탄소세의 부과가 몇 몇 산업의 가격 경쟁력에 집중적인 영향을 줄 것임을 시사하고 있다.

• The Journal of the Korea Contents Association
• /
• v.14 no.12
• /
• pp.999-1009
• /
• 2014

In this paper, $CO_2$ emission and storage amount are evaluated for real RC (Reinforced Concrete) underground structure considering $CO_2$ amount including material manufacturing, moving, and construction, repairing timing stage regarding extended service life. Four mix proportions with mineral admixtures are prepared and $CO_2$ diffusion coefficient are obtained based on a micro modeling. Referred to carbonation durability limit state, $CO_2$ emission and storage amount are evaluated, which shows higher initial $CO_2$ emission is caused due to larger unit content of cement and the storage increases with more rapid carbonation velocity. Furthermore various $CO_2$ concentration is adopted for simulation of $CO_2$ evaluation including measured $CO_2$ concentration (600ppm). With higher concentration of $CO_2$ outside, carbonation velocity increases. In order to reduce $CO_2$ emission through entire service life, reducing initial $CO_2$ emission through mineral admixture like fly ash is more effective than increasing $CO_2$ storage through OPC since $CO_2$ is significantly emitted under manufacturing OPC and $CO_2$ storage in cover concrete of RC structure is not effective considering initial concrete amount in construction.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1996.04a
• /
• pp.24-29
• /
• 1996

The purpose of this study is to propose new estimation method of unit cement content in hardened concrete. In general, the quantity of cement in hardened concrete is tested by hydrochlonic acid dissolving cement paste, however, hydrochloric acid dissolves sea shell contained in sea sand and lime stone in concrete. Therefore, the tested cement content is apt to estimate greater than actual cement content. The sodium gluconate solution dissolves only cement in concrete, it is hard to dissolve sea shell and lime stone as CaCo3. The effects of the quantity, concentration and temperature of sodium gluconate solution, the ignition temperature, the ignition loss of cement on the cement content and the percentage of dissolution of cement were investigated to establish a test method. From the results of these tests, the fundamental test method for cement content of hardened concrete by sodium gluconate is proposed.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.39 no.1
• /
• pp.83-92
• /
• 1997

An experimental study of the application of Silica fume for the high strength concrete was conducted. Nine specimens with three different contents of silica fume, 0%, 10%, 20% and with three water-cement ratio 30%, 40%, 50% were tested. Results shows that 10% of silica fume and 30% of water-cement ratio has a maximum strength with 700kg/$cm^2$ of compressive strength and 64kg/$cm^2$ of splitting tensile strength and 100kg/$cm^2$ of flexural strength. Slump value of the tested samples decreases with increasing water-cement ratio and elapsed time of silica fume. Splitting tensile strength$({\sigma}_f)$ and flexural strength $({\sigma}_f)$ and static modulus of elasticity(E) can be correlated with compressive strength $({\sigma}_c)$ from a regression analysis.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.5
• /
• pp.189-195
• /
• 1998

콘크리트 구조물이 초기재령에서 외기에 노출될 때, 수부확산으로 인하여 수분의 이동이 일어나고, 또한 자체건조도 발생한다. 이러한 콘크리트 내부의 수분확산과 자체건조에 의하여 콘크리트의 위치에 따라 상대습도가 변호한다. 특히 고강도 콘크리트의 경우에 단위 시멘트량을 많이 사용하기 때문에 , 초기재령에서 콘크리트 단면의 수분분포는 자체건조에 의하여 큰 영향을 받는다. 본 연구에서는 초기재령에서 외기에 노출된 콘크리트 내부의 여러 위치에서 상대습도를 측정하였다. 또한 자체건조로 인한 콘크리트의 상대습도 변화를 측정하여 초기재령에서 수분확산과 자체건조가 콘크리트 내부의 각 위치에서 상대습도에 미치는 영향을 검코하였다. 그리고 수분확산 이론에 의하여 해석결과와 실험결과를 비교하여 \ulcorner재령에서 수분확산 이론의 타당성을 검증하였다. 저강도 콘크리트 단면의 수분분포는 주로 수분확산에 의하여 영향을 받았으며, 자체건조의 영향은 매우 작게 나타났다. 그렇지만 고강도 콘크리트는 수분확산 뿐만 아니라 자체건조에 의하여도 영향을 받았다. 또한 수분확산 이론에 의한 해석결과는 실험결과를 잘 예측하였다.

• Journal of the Korean GEO-environmental Society
• /
• v.18 no.6
• /
• pp.5-19
• /
• 2017

In this study, the effect of rock mass curtain grouting was investigated by analyzing the correlation between the parameters of the RMR & grout injection volume, Lugeon value & RQD, Lugeon value & cement injection volume. In order to investigate the effect of rock mass curtain grouting, we analyzed the grout injection volume of 315 curtain grouting holes at 9 tunnel face of NATM Subsea tunnels in gneiss area. The total grout injection volume in the Subsea tunnels study was slightly changed in some tunnels face but decreased with increasing the rating of parameters in spacing of discontinuity (R3, Js) and groundwater condition (R5). The geological anomalies of seismic survey (3D, TSP) and the inflow of probe hole were found to be more correlated of relative than the parameters of RMR. The unit injection volume was found to decrease with higher ratings in the parameters of the RMR except the weathering degree of the discontinuity (Jc, R4). The correlation between RQD and Lugeon values is not significant, but it can be confirmed that the Lugeon value tends to decrease as the RQD value increases.