• Journal of the Korean Applied Science and Technology
• /
• v.33 no.3
• /
• pp.483-491
• /
• 2016

Even though the antifogging property of nanosilica coated glass surface is highly increased due to the hydrophilic hydroxyl groups on nanosilica surface, the durability of this property on outdoor glass was diminished rapidly after rain washing. In addition the topology of nanosilica coated glass surface plays very important roles to control an light transmittance or antireflection property. To improve these coating durability and characteristics a hydrophilic nanosilica coating on glass was prepared by coating with 1.5 wt% of nanosilica (Ludox) suspension in the presence of hydrolyzed tetraethylorthosilicate (TEOS). The optimum hydrolysis condition of TEOS in acidic or basic aqueous solution was also examined by contact angle measurement. The final transparent hydrophilic coating layer coated with nanosilica-TEOS in acidic condition (pH=4) showed much improved durability of hydrophilic surface as well as higher visible light transmittance than original uncoated glass by 2 % point.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.370.2-370.2
• /
• 2016

투명 박막 태양전지는 건물과 일체화 된 building-integrated photovoltaics (BIPV) 시스템에 적용되어 건물의 외장재로서 외관의 심미적 가치를 높일 수 있다. 현재 BIPV 모듈은 glass 타입의 형태가 시장을 주도할 것으로 예상되며[1], 건물의 외부 미관을 고려하여 투명 박막 태양전지에 색을 구현하는 연구가 진행되고 있다. 투명 박막 태양전지에 적용하기 위한 목적으로 본 연구에서는 스핀코팅을 이용하여 표면 플라즈몬 효과가 큰 Cu 나노입자를 Si 웨이퍼와 유리기판 위에 각각 분포 시킨 후, 광학적 특성을 분석하였다. 스핀코팅의 속도(rpm)를 다양하게 변화 시킨 후 나노 입자의 분포를 관찰하였으며, 속도가 증가할수록 나노입자의 수는 감소함을 확인하였다. 또한 속도가 증가할수록 입자 사이의 거리는 멀어졌으며, 최저 속도 100 rpm에 비해 4000 rpm에서 스핀코팅 한 입자들은 응집이 상대적으로 되지 않았음을 관찰하였다. 속도가 증가할수록 입자가 기판 위에 적게 잔재하기 때문에 반사율과 투과율이 가시광선 영역에서 증가하였으며, 유리 기판에 구현한 색깔이 점차 옅어짐을 관찰하였다. 이러한 결과로부터 스핀코팅의 속도를 변화시킴으로써 나노입자의 분포 양상과 이에 따른 색상의 변화를 유발 할 수 있다는 사실을 확인하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.276-276
• /
• 2010

본 논문에서는 나노하이브리드 방법으로 제조된 변성 폴리이드계 나노하이브리드 절연코팅의 표면 굴곡특성을 비교 연구하였다. CS로 나노하이브리드화된 수지의 코팅표면의 표면거칠기를 AFM 으로 분석하여 그 변화를 비교하였다. CS로 처리된 나노하이브리드 코팅면의 경우 기초수지의 코팅면과 비교하여 기저재료와 상관없이 표면 거칠기는 현저히 줄어드는 경향을 나타내었다. 이는 20nm 이하의 균일한 CS입자가 균일하게 분산되어 수지 내에 자리하므로 기저물질의 거칠기를 보완하는 역할을 하기 때문으로 분석된다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.61-62
• /
• 2011

실리카 나노입자를 분산시킨 기능성 코팅 소재를 개발하였다. 본 기능성 코팅 소재는 마그내슘 판재에 적용하여 내스크래치 및 내부식성을 향상시키기 위한 것이다. 최근 마그네슘 판재는 스마트 폰 및 이동통신 기기의 외장재소재로 각광을 받고 있다. 그러나 표면의 기계적 강도가 약하고, 특히 수분에 의한 부식이 심각하여 사용에 많은 제한을 받고 있다. 본 연구에서는 실리카 나노입자가 분산된 유무기 하이브리드 코팅을 적용하여 기계적 강도 및 내부식성을 향상하고자 하였다. 분산하는 나노입자의 크기를 달리하여 코팅층으로부터 각각 다른 물리적 화학적 특성을 유도할 수 있었다. 각 코팅 층의 특성은 연필경도, 기판 휨 각도, 그리고 electrochemical impedance spectroscopy 등을 이용하여 평가하였고, 최종적으로 휴대폰 신뢰성 평가 기법을 적용하여 상용화 적용성도 평가하였다.

• Membrane Journal
• /
• v.15 no.1
• /
• pp.34-43
• /
• 2005

The poly(vinyl alcohol) (PVA)-based thin film composite nanofiltration (NF) membranes were prepared by coating polysulfone ultrafiltration membranes, sulfonated polyethersulfone and polyamide NF membranes with aqueous PVA solution by a pressurizing method. The PVA was cross-linked with aqueous glutaraldehyde solution. The NF membranes coated with a very low concentration of PVA on all the support membranes was successfully prepared. With increasing the hydrophilicity of the support membranes, the water flux increased. Especially, ζ-potential of negatively charged polyamide NF membrane was reduced by coating the membrane with PVA. A fouling experiment was carried out with positively charged surfactant, humic acid, complex of humic acid and calcium ion and bovine serum albumin. A non-coated polyamide NF membrane was significantly fouled by various foulants. The fouling process when using humic acid and protein occurred at the isoelectric point. There was severe fouling when using humic acid and adding bivalent cations. By coating the polyamide NF membrane with aqueous PVA solution, fouling was reduced. The polyamide NF membrane coated with PVA was resistant to the acidic and basic solution.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.92.1-92.1
• /
• 2018

표면증강 라만 산란(Surface Enhancement Raman Scattering, SERS) 기판의 경우, 규칙적인 배열을 갖는 나노구조 및 나노패턴 기판과 금속 나노구조의 고밀도 패킹이 고감도 화학물질 검출에 중요하다. 또한 폭넓은 응용 가능성에도 불구하고 기판 제작의 비용이 높고 재현성이 떨어져 상용화에 어려움을 겪고 있다. 본 연구에서는 다공성 알루미나(Anodic Aluminum Oxide, AAO)를 사용하여 Ag 나노입자가 코팅된 나노기둥 배열(Nanopillar array)을 갖는 고분자 필름의 SERS-active 기판을 제작하여 공정비용을 낮추고, 대면적화로 생산성을 높이고자 한다. 다단계 양극산화 공정과 복제 기술을 통해 다양한 지름과 높이를 갖는 맥주병 형상의 나노기둥 배열을 제조하였고, aspect ratio가 2.3인 나노기둥 배열에서 최대의 SERS 신호 강도와 높은 재현성을 확인하였다. SERS 신호의 세기는 Ag 나노입자가 코팅된 나노기둥 배열의 열처리 온도와 분석 물질의 농도에 따라 비례하며 이를 바탕으로 정량적인 고감도 진단, 바이오 화학 물질 센서에 매우 적합함을 알 수 있다.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.2
• /
• pp.531-540
• /
• 2019

Hydrophilic and hydrophobic nanosilica and tetraethyl orthosilicate (TEOS) as a coupling agent was used to form a coarse spike structure as well as an excellent reactive hydroxyl groups on the glass surface. Then, a second treatment was carried out using a trichloro-(1H,1H,2H,2H)perfluorooctylsilane(TPFOS) solution for ultimate water repellent glass surface formation. The formation of hydrophobic coating layer on glass surface using silica aerosol, which is hydrophobic nanosilica, was not able to form a durable hydrophobic coating layer due to the absence of reactive -OH groups on the surface of nanosilica. On the other hand, a glass surface was first coated with a coating liquid prepared with hydrophilic hydroxyl group-containing nanosilica and hydrolyzed TEOS, and then coated with a TPFOS solution to introduce a hydrophobic surface on glass having a water contact angle of $150^{\circ}$ or more. The sliding angle of the coated glass was less than $1^{\circ}$, which meant the surface had a super water-repellent property. In addition, as the content of hydrophilic nanosilica increased, the optical transmittance decreased and the optical transmittance also decreased after 2nd coating with the TPFOS solution. The super-hydrophobic property of the coated glass was remained up to 50 times of rubbing durability test, but only hydrophobic property was shown after 200 times of rubbing durability test. Conclusively, the optimal coating conditions was double 1st coatings with the HP3 coating solution having a hydrophilic nanosilica content of 0.3 g, and subsequent 2nd coating with the TPFOS solution. It is believed that the coating solution thus prepared can be used as a surface treatment agent for solar cells where light transmittance is also important.

• Journal of Industrial Convergence
• /
• v.21 no.9
• /
• pp.33-39
• /
• 2023

Nano-sized materials can be coated on various substrates, and since this material is transparent and conductive, it can be used as a transparent electrode for electronic devices or an electrode for power supply. In this study, CNT and Ag nanowires were repeatedly coated using the silk screen technique, and samples formed up to 5 times were fabricated, and their optical and electrical properties were measured and analyzed. It was confirmed that marks were formed on the surface of the silkscreen-coated sample according to the coating direction, and the trend of transmittance and surface resistance according to the number of times of coating was investigated. As the number of coatings increased, transmittance and surface resistance tended to decrease. In particular, in the case of transmittance, the range of change was large in the samples coated 2 and 5 times. These changes were confirmed by the Ag nanowire coating. In addition, starting from 700 nm, the previous wavelength region increased according to the wavelength, while the above showed a tendency to decrease. The surface resistance was lowered from 9Ω/cm² when coating once to 0.856Ω/cm² when coating five times. It was found that the resistance value was affected by Ag similarly to the permeability. In the future, it is necessary to realize a desired transparent electrode through Ag concentration and coating of Ag nanowires with other methods and fusion with highly transparent CNT to apply to electronic devices.

• Composites Research
• /
• v.35 no.2
• /
• pp.80-85
• /
• 2022

This work presents an experiment study to evaluate the nanoparticle adhesion and surface hydrophobicity characteristics of Teflon-polyurethane top coat depending on the number of multi-wall carbon nanotube (MWCNT) coatings, which is a carbon-based hydrophobic particle. In order to measure the adhesion between the nanoparticles and the top coat, adhesion pull-off test was performed with different MWCNT oxidation times. Static contact angle and roughness measurements were carried out to characterize the surface hydrophobic behavior. Through the roughness evaluation, it was confirmed that the carbon nanotubes were wetted in the Teflon-polyurethane top coat, and the degree carbon nanotube wetting was confirmed through a USB-microscope. As a result, it was found that the larger the degree of wetting, the better the adhesion. From the experimental results, as the hydrophobicity of Teflon-polyurethane increased, the adhesive propertydecreased with the number of coatings. It was possible to improve the adhesive force and determine the number of coatings of carbon nanotubes with optimized hydrophobicity.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.23.1-23.1
• /
• 2010

Alkanethiol (CH3(CH2)nSH) 자기 조립 박막은 금, 은, 팔라듐 그리고 구리와 같은 금속 물질과 결합하여 산화 방지 보호막, 생화학적 멤브레인 그리고 케미컬 센서로 널리 이용되었다. 전도성을 가진 많은 금속 분말 중에서, 구리는 뛰어난 열, 전기 전도성과 풍부한 양으로 다른 귀금속에 비교하여 경제성까지 갖춘 물질이다. 그러나 이러한 구리 나노 분말은 대기에 노출된 구리 분말이 쉽게 산화된다는 결정적인 단점 때문에 그동안 널리 이용되지 못하였다. 이러한 구리의 단점을 극복하고 뛰어난 전도성의 특징을 이용하고자, Langmuir-Blodgett (LB), layer by layer (LbL), electrophoretic deposition (EPD), self-assembled monolayer (SAM)과 같은 구리 나노 분말 위에 유기 박막을 형성하고자 하는 많은 방법이 시도되어왔다. 이러한 방법들 대부분은 습식 방법으로 진행되었으며, 약 2-nm 두께의 SAM 구조를 형성할 수 있음이 많은 연구를 통하여 확인되었다. 그러나 습식 기반의 SAM 구조는 단지 수일 동안만 유효하며, 이는 코팅을 수행하면서 점차 떨어지는 source solvent의 순도와 적합하지 않은 코팅 조건, 그리고 이러한 원인으로 형성된 부실한 막질 구조 때문으로 추측된다. 게다가 이러한 습식 기반 공정은 코팅 막의 두께 조절과 코팅 시 solvent의 순도를 일정하게 유지하는 것이 매우 복잡하고 어려운 작업으로 알려져 왔다. 본 실험에서는 고 진공 챔버 (< $4.0{\times}10-6$ torr) 시스템을 이용하여 습식 기반 공정의 문제점을 극복하고 구리 나노 분말의 산화를 막기 위한 실험을 진행하였다. 1-octanethiol (CH3(CH2)7SH)은 중간 길이의 hydrocarbon (n=7) 구조를 가진 특징 때문에 코팅 물질로 사용되었다. 게다가, alkanethiol 족 특유의 물질인 황(sulfur)은 구리와 결합하여 산화방지 보호막의 역할을 수행할 수 있다. 저 진공 조건에서는 10-nm의 multilayer가 일괄적으로 코팅됨을 확인할 수 있었다. 본 실험에서는 약 10-nm 두께의 자기 조립 박막(self assembled monolayers: SAMs)이 고 진공 조건에서 구리 나노 분말 표면 위에 코팅 조건의 변경을 통해서 5-nm에서 10-nm 두께의 1-octanethiol SAMs 구조를 얻어낼 수 있었다. 이는 고 진공 조건에서 1-octanethiol SAMs의 코팅 두께를 조절함으로 다양한 크기의 분말에 코팅 물질로 쓰일 수 있음을 알 수 있다.