• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.31-36
• /
• 2003

In this study, nano-sized NiCuZn-ferrites for the multi-layered chip inductor application were prepared by a coprecipitation method and its electromagnetic properties were analyzed. Also, the property of low temperature sintering were studied with the initial heat treatment of powder.$(Ni_{0.4-x}Cu_xZn_{0.60})_{1+w}(Fe_2O_4)_{1-w}$ (x=0.2, w=0.03) were calcined at $300^{circ}C~750^{circ}C.$ The sintered NiCuZn-ferrites at $900^{\circ}C$ showed good apparent density $4.90g/cm^3,$ and magnetic properties of initial permeability 164 and quality factor 72. As the calcination temperature increase, the grain size of NiCuZn-ferrite increased with irregular grain distribution and its magnetic properties were deteriorated.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.04a
• /
• pp.46-47
• /
• 2006

고주파유도가열 연소합성법으로 60MPa의 기계적 압력과 고주파유도가열 장치의 총용량 (15KW)의 90%의 출력을 가해 75초의 짧은 시간에 97%이상의 상대밀도를 갖는 $TaSi_2-SiC$ 복합체를 제조하였으며, 제조된 시편의 미세조직 사진으로부터 선형분석법으로 측정한 $TaSi_2-SiC$ 의 평균 결정립크기는 각각 250nm 과 60nm 이었다. 또한 제조된 시편을 연마하여 비커스 경도계를 이용하여 기계적 특성평가를 한 결과 경도 와 파괴인성은 각각 $1366Kg/mm^2$ 와 $305MPam^{1/2}$ 이었다.

• Journal of Powder Materials
• /
• v.18 no.1
• /
• pp.73-77
• /
• 2011

$Y(OH)_3$ nanowires were synthesized by a hydrothermal reaction of metallic Y with aqueous solution of LiOH. The morphology and the size of the nanowires changed with varying the volume of the LiOH solution inside the autoclave. $Y(OH)_3$ nanowires transformed to $Y_2O_3$ by a subsequent heat-treatment without morphological change. By a proper control of hydrothermal reaction parameter and heat-treatment, the yield of pure $Y_2O_3$ nanowires up to 97% was attained.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.10a
• /
• pp.352-355
• /
• 2003

비자성이며 비전도성의 물리적 성질을 갖는 자연산 퀄쯔(quartz)와 용암석 스코리아를 대상으로 마그네타이징 처리를 하여 분석하였다. 마그네타이징 처리를 위하여 강력한 기계화학적 분쇄 반응을 시켰으며, 분쇄 반응시 알코올계의 솔벤트를 반응 용매로 사용하였다. 퀄쯔와 스코리아의 마그네타이징 처리에서 비교적 비중이 큰 퀄쯔의 경우와 비중이 작은 스코리아의 경우에도 분쇄된 분말이 물에 뜨는 것을 확인할 수 있으며, 친유성으로 기름에 대한 흡착 성질이 우수함을 확인하였다. 자연산 퀄쯔와 함께 스코리아를 바탕물질로 하여 기계-화학적 반응 기술로 고 분산성 흡착반응에 의한 고분자 물잘 생성을 유도하여 나노복합체를 제조하였다. 반응의 처리조건과 적용과정에 따라서 기계-화학적 반응을 통하여 얻어진 물질은 자기적 성질과 유전체 및 전기적 성질을 동시에 나타낸다. 부착성 융합 복합물질의 특징을 고려하여 시그니토마그네틱스(Segneto-magnetics)로 분류되는 합성분말은 특히 유류성분에 대하여 높은 흡착성을 가지며, 강한 자기적 성질을 띄는 10-50 nm 두께의 하나 또는 그 이상의 이질적 융합 화합물 층이 석영이나 수정체의 표면에 합성되어 특유의 자기, 전기적 성질을 나타낸다.

• 한국신재생에너지학회:학술대회논문집
• /
• 2005.11a
• /
• pp.656-659
• /
• 2005

Nanocrystalline ceria powders were prepared by hydrothermal treatment of cerium(IV) ammonium nitrate solution without a precipitating agent. A systematic investigation of the effect of hydrothermal temperature and react ion time on the physical properties of the product powders was carried out. When the hydrothermal temperature was increased, the product ceria powders exhibited larger crystallite size with higher yield. Increasing reaction time produced more crystalline ceria powders attributed to further hydrothermal reactions and structural rearrangement. The physical properties of ceria powders can be control led by adjusting the hydrothermal conditions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.67-70
• /
• 2003

단원계 및 이원계 촉매를 이용하여 나노 감지 소자를 합성하였고, 이를 이용하여 가연성 후막 가스 센서를 제작, 촉매 시스템에 따른 가스 감지 특성을 비교하였다. 단원계의 경우 Pd 및 Pt를 각각 3wt%로, 이원계의 경우 Pd:Pt 농도를 1:2~2:1wt%로 각각 제어하여 평균 입도가 15 nm 인 $SnO_2$ 나노 분말에 도핑, 감지물질을 합성하였다. 그 후 감지물질을 paste로 만들어 인쇄, 가스센서 제작 후 $450{\sim}600^{\circ}C$의 온도로 열처리하였다. 그 결과 이원계 촉매 시스템을 가진 가스 센서는 시효 시간에 따라 감도 값이 변하는 불안정한 현상을 나타내었다, 그러나 단원계 촉매의 경우 시효 시간이 지나도 감도 값이 안정된 현상을 나타내었다. 특히 3wt% pt를 도핑하여 $500^{\circ}C$에서 열처리한 경우 5시간 시효 후에도 감도 값의 변화 폭이 3.5% 이하의 매우 안정된 특성을 나타내었고 반응 시간도 20초 이하로 매우 빠른 응답 특성을 나타내었다.

• Journal of the Korean Magnetics Society
• /
• v.27 no.3
• /
• pp.87-91
• /
• 2017

Carbon-encapsulated Ni and metal Ni nanoparticles were synthesized by levitational gas condensation (LGC). Methane ($CH_4$) gas was used to coat the surface of the Ni nanoparticles. The Ni particles had a core diameter of 10 nm, and were covered by 2~3 nm thin carbon layers with multi-shells structure.The low magnetization comparing with the Ni nanoparticles without carbon-shell results in the coexistence of nonmagnetic carbon and a large surface spin percentage with disordered magnetization orientation for the nanoparticles. Biginelli reactions in the presence of L-proline and Ni and carbon encapsulated Ni nanoparticles were carried out to change the ratio between stereoisomers. The obtained S-enantiomers for 3,4-dihydropyrimidine (DHPM) using catalysts of Ni, and Ni@C was an excess of about ${\Delta}{\sim}7.4%$ and ${\Delta}{\sim}19.6%$, respectively. The nanopowders were fully recovered using magnet to reuse as a catalyst. The Ni@C was shown at same yield to formation of 3,4-DHPM, though it was recycled for catalyst in the reaction.

• Korean Chemical Engineering Research
• /
• v.49 no.6
• /
• pp.781-785
• /
• 2011

In this work, a nano-sized samaria-doped ceria(SDC) was prepared by a urea-based hydrothermal method and characterized by XRD, FESEM and TEM. It was observed that the increase in synthesis time and temperature gave rise to crystallity and particles size. Moreover, the synthesised powders had a excellent ion-conductivity(0.1 S/cm at 600~$800^{\circ}C$) which is suitable for electrolyte of intermediate temperature-solid oxide fuel cell(IT-SOFC). Subsequently for use as electrolyte for anode-supported IT-SOFC, we tried to deposit the SDC powder on a porous NiO-SDC substrate by electrophoretic deposition(EPD) method. From the FESEM observation, a compact

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.103-103
• /
• 2003

대기나 물에 용해된 여러 가지 유해한 유기물을 분해하기 위한 방안으로서 다양한 광촉매 재료를 이용하려는 시도가 진행되고 있다. 하지만 광촉매 반응은, 현탁액 내에서 submicrometer 크기를 갖는 반도체재료에서 발생하므로 처리된 폐수로부터 촉매를 제거해야 하는 정제공정 (downstream process)이 필요하며, 이는 경제적인 측면에서 큰 경비를 요구하게 된다. 이를 해결 하기 위하여, 가장 우수한 광촉매 재료로 평가받는 TiO$_2$를 glass beads, sands, silica gel등의 물질에 고정시키거나, TiO$_2$를 자성 입자에 코팅시킨 형태인, 자성 광촉매입자를 응용하려는 연구가 최근 활발하게 진행되고 있다. 따라서 본 연구에서는 광촉매의 고정화와 재활용 효율을 향상시키기 위하여 TiO$_2$ 나노입자를 y-Fe$_2$O$_3$ 나노입자의 표면에 코팅하여 나노입자의 큰 비표면적을 활용하고 미세구조를 제어하여 입자간의 고정특성과 자기적 특성의 제어기술을 확립하고자 하였다.

• Applied Chemistry for Engineering
• /
• v.30 no.6
• /
• pp.694-697
• /
• 2019

In recent years, titanium dioxide powders were produced as nanoparticles or nanowires or nanotubes in one-dimensional structure, and mesoporous spheres in 3-D to improve their crystallinities, which were further used as photo-electrode materials and for preventing photo-aging. In this study, a nano sol composed of titanium dioxide exhibiting a high crystallinity was synthesized using n-alcohol as a solvent. The crystallinity of the nano sol was confirmed by FE-SEM, and XRD, while the UV blocking rate confirmed by UV-Vis spectrometry results. Changes in the crystallinity were investigated by varying the types of solvents such as butanol, propanol and ethanol. The synthesized particle sizes were from 200 to 250 nm, and the optical transmittance showed a high blocking rate in the UVB and UVA range. It is expected that a high transmittance at 550 nm wavelength can increase the photoelectric conversion efficiency of solar cells and the UV blocking efficiency.