• Korean Chemical Engineering Research
• /
• v.51 no.4
• /
• pp.411-417
• /
• 2013

To use as an anode material of lithium secondary battery, graphite-silicon composite powders are prepared by ball-milling with silicon nanoparticles (average diameter 100 nm, 0~50 wt%) and graphite powder (average diameter $15{\mu}m$) and their electrochemical properties are examined. As the silicon content increases, the graphite becomes smaller by the ball-milling and amorphous phase appears whereas the silicon do not suffer the change of nanocrystalline phases and embeds within the amorphous phase of graphite. Cyclic voltammetry at low scan rate reveals that typical oxidation peaks of graphite and silicon appear at 0.2~0.35 and 0.55~0.6 V, respectively, with higher reversibility for repeated cycles. In contrast, the high-scan-rate redox behavior is very irreversible for repeated cycles. High irreversible capacity is exhibited in the initial charging-discharging cycles, but it diminishes as the cycle number increases. The saturated discharge capacity achieves about 485 mAh $g^{-1}$ at 50th cycle for the composite of Si 20 wt%. This is due to the formation of amorphous graphite morphology by the adequate composition (C:Si=8:2 w/w), which efficiently buffers the volume change during alloying/dealloying between silicon and lithium.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.54-54
• /
• 1999

다이아몬드 합성시 질소 첨가는 Cn 화합물의 합성가능성을 비롯하여 다이아몬드의 질소 도핑, 성장 속도 및 결정성 변화 등 다양한 관점에서 중요한 의미를 가지고 있다. 본 연구에서는 다이아몬드의 일반적인 합성조건에서 질소를 첨가하여 합성된 막의 형상 및 상 변화에 대해 고찰하였다. 막은 다이아몬드 전처리시킨 Si 기판위에 microwave plasma CVD 장치를 이용하여 합성하였다. 유입되는 혼합가스(CH4+H2+N2)에서 N2 첨가량을 0-95%까지 변화시켰다. 이때 CH4 농도는 5%로 고정하였고, 합성온도는 90$0^{\circ}C$-115$0^{\circ}C$까지 변화시켰다. 이와 같이 합성된 막의 표면조직 및 성장 두께를 측정하기 위해 주사전자현미경을 이용하였다. 상의 분석은 Raman, XRD 및 TEM 분석을 이용하였으며, 조성분석을 위해 XPS 및 AES를 사용하였다. 질소 첨가량에 따라 합성된 막은 첨가하지 않은 경우에 다이아몬드 결정에서 시작하여 질소첨가에 따라 결정면이 깨지는 것으로 나타났다. 그러나 30%, 45%의 경우는 다시 결정면이 나타났다. 다량의 질소가 첨가되었을 때, 다시 결정면을 보이는 다이아몬드가 합성된 것은 매우 흥미로운 결과이다. 한편 질소와 메탄만의 기체하에서는 다시 결정면이 관찰되지 않았다. 이들 상의 구조는 XRD 및 TED 분석을 통해 모두 다이아몬드로 확인되었다. 기체내의 질소의 첨가에 관계없이 고상내에 질소는 확인되지 않았다. 따라서 이방법에 의한 CN 화합물의 합성은 힘든 것으로 보여진다. 이들 실험 결과를 근거로 온도 및 조성에 따른 기체의 열역학적 계산을 통하여 합성거동과의 연관성을 검토하였다. anode는 매우 높은 충전용량을 갖는데 첫 번째 방전시에 Li2O를 생성하여 비가역적 반응을 나타내고 계속되는 충방전 동안 Li-Sn 합금이 생성되어 2차전지의 가역적 반응을 가능하게 한다. SnO2 는 대기중에서 Li 금속보다 안정하기 때문에 전지의 제작 공정 및 사용 면에서 매우 우수한 물질이지만 아직까지 SnO2 구조적 특성과 전지의 충, 방전 특성에 대한 관계의 규명을 위한 정확한 정설은 제시되고 있지 못하다. 본 연구에서는 TFSB anode 물질로써 SnOx박막을 상온에서 여러 전도성 콜렉터 위에 증착하여 그 충, 방전 특성을 보고하였다. 증착된 SnOx박막의 표면은 SEM, AFM으로 분석하였으며 구조의 분석은 XR와 Auger electron spectroscope로 하였다. 충, 방전 특성을 분석하기 위하여 리늄 foil을 대극과 참조 전극으로 하여 EC:DMC=1:1, 1M LiPF6 액체 전해질을 사용한 Half-Cell를 구성하여 100회 이상의 정전류 충, 방전 시험을 행하였다. Half-Cell test 결과 박막의 구조, 콜렉터의 종류 및 Sn/O비에 따라 서로 다른 충, 방전 거동을 나타내었다.다. 거의 없었다. 5mTorr 일 때가 가장 좋았다.수 있음을 알 수 있었다. 그러므로, RNA바이러스의 하나인 BVDV의 viral replicon을 이용하여 다양한 종류의 포유동물 세포에 유전자 발현벡터로써 사용할 수 있음으로 post-genomics시대에 다양한 종류의 단백질 기능연구에 맡은 도움이 되리라 기대한다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(na

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.3
• /
• pp.121-127
• /
• 2007

We have applied mechanical alloying (MA) to get $Mg_2Si$ thermoelectric material with nano-sized grains. An optimal milling and heat treatment conditions to obtain the single phase of $Mg_2Si$ compound with fine microstructure were investigated by X-ray diffraction and differential scanning calorimetry (DSC) measurement. The $Mg_{66.7}Si_{33.3}$ MA samples ball-milled for $20{\sim}180\;hrs$ exhibit two broad exothermic heat releases around $220^{\circ}C$ and $570^{\circ}C$. On the other hand, MA sample ball-milled far 260 hrs exhibits only a sharp exothermic peak at $230^{\circ}C$ Single phase Mg2Si powder can be obtained by MA of $Mg_{66.7}Si_{33.3}$ mixture for 60 hours and subsequently heated up to $620^{\circ}C$. Sintering of the MA powders was performed in a spark plasma sintering (SPS) machine using graphite dies at $800{\sim}900^{\circ}C$ under 50 MPa. The shrinkage of sintering sample during SPS was significant at about $200^{\circ}C$. All compact bodies have a high relative density above 94% with metallic glare on the surface.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.131-131
• /
• 2018

최근 절삭공구산업은 자동차, 항공기, IT, 선박, 에너지 등 첨단산업의 증가로 인해 CGI, CFRP, 내열합금 등 난삭재의 수요가 증가하고 있다. 난삭재는 고내열, 고경도, 초경량 같은 특성을 지니며 우수한 기계적 물성을 갖지만 가공의 어려움이 있어 산업에 적용하는데 한계가 있다. 이러한 한계를 극복하기 위해 개발된 가공기술 중 하드 코팅은 공구코팅비용 대비 공구의 표면경도와 수명을 효율적으로 향상시킬 수 있다고 알려져 있다. 대표적인 하드코팅으로는 AlN계, TiN계 코팅이 있다. 이러한 코팅의 경우 높은 기계적 물성과 우수한 내마모성으로 인해 절삭공구의 성능을 향상시킬 수 있기 때문에, 많은 연구가 진행되고 있으며 절삭공구산업에서 각광받고 있다. 기존 선행연구 결과에 따르면 질화물 코팅의 우수한 물성은 질화물(Nitride) 생성 및 질화 공정에 의한 코팅층의 고밀도화에 의해 나타난다고 알려져 있다. 그 중에서 AlCrN coating은 우수한 내마모성 및 향상된 고온경도를 갖고 있다. AlCrN based coating에 미량의 원소를 첨가하여 기존 AlCrN coating의 기계적 특성을 더욱 향상 시킨 coating은 일반적인 고성능 코팅 대비 공구수명이 길다고 알려져 있으며, 전반적으로 우수한 특성에 의해 전 세계적으로 습식 및 건식 기계 가공 용도로 사용되고 있다. 본 연구에서는 AlCrN based coating에 미량의 원소를 첨가한 coating의 우수한 기계적 특성의 원인을 규명하기 위해 텅스텐카바이드(WC) 기판 위에 아크 이온 플레이팅 장비를 이용하여 AlCrN based coating을 증착 시킨 sample을 분석하였다. 결정구조 및 상 분석을 위해 X선 회절분석(XRD)을 실시하였으며, 미세 구조를 분석하기 위해 전계방출형 주사전자현미경(FE-SEM), 투과 전자현미경(TEM) 분석을 실시하였다. 또한 코팅층의 화학적 성분 분석을 위해 EDX분석을 실시하였으며 기계적 특성 평가를 위해 나노압입시험(Nano-indentation test)을 진행하였다.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.4
• /
• pp.141-150
• /
• 2006

Nanocrystalline CoW thin/thick film alloys were electodeposited from citrate baths to investigate the influences of metal ion concentration, current density and solution pH on chemical composition, current efficiency, residual stress, surface morphology, and microstructure of the film. Deposit W (tungsten) content in CoW thin/thick film increased with increasing W ion concentration, current density, and solution pH in the plating bath. It was observed that residual stress in CoW thin/thick film decreased with increasing W ion concentration and solution pH. CoW thin film exhibited mixed phases of hop Co [(100) and (002)] and hcp $Co_3W$ [(002) and (201)] at W ion concentration with 0.02 to 0.08 M. The microstructure of CoW thin film at W ion concentration of 0.1 to 0.2 M was close to amorphous phase. The dominant phases were found to be hop Co (002) and hop $Co_3W$ [(200), (002) and (201)] at the current densities of 5, 10, 25, and $100mA{\cdot}cm^{-2}$ CoW thin film at the current densities of 50 and $75mA{\cdot}cm^{-2}$ was close to amorphous phase. At solution pH 8.7, CoW thin film exhibited hcp Co (002) and hop $Co_3W$ [(200), (002) and (201)]. Below solution pH 8.7, CoW thin film exhibited amorphous microstructure. The optimum electrodeposition conditions for CoW thin/thick film were found to be W ion concentration of 0.08 M, current density of $10mA{\cdot}cm^{-2}$, and solution pH 8.7.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.162-162
• /
• 2017

AlCrN 코팅은 높은 경도, 낮은 표면 조도 등의 상온에서의 우수한 기계적 특성 이외에 고온에서 안정한 합금상의 형성으로 인하여 우수한 내열성을 보이는 코팅이며, Si을 첨가하여 나노복합구조를 갖는 AlCrSiN 코팅은 고경도 특성을 나타내는 나노결정립과 고내열성을 나타내는 $Si_3N_4$ 비정질이 동시에 존재함으로써 뛰어난 고온 특성까지 보유하여 공구 코팅으로의 적용 가능성이 크다. 본 연구에서는, 가혹화된 공구사용 환경 대응 하는 더욱 우수한 내마모성 및 내열성을 보이는 코팅막을 개발하기 위해 AlCrN/AlCrSiN 이중층 코팅을 합성하였다. 합성된 코팅의 구조 및 물성을 분석하기 위해 field emission scanning electron microscopy(FE-SEM), nano-indentation, atomic force microscopy(AFM) 및 ball-on-disk wear tester를 사용하였다. 내열성을 확인하기 위하여 코팅을 furnace에 넣어 500, 600, 700, 800, 900도에서 30분 동안 annealing한 후에 nano-indentation을 사용하여 경도를 측정을 하였다. 5:5, 7:3, 9:1의 두께 비율로 AlCrN/AlCrSiN 이중층 코팅을 합성하였으며 모든 코팅의 두께는 $3{\mu}m$로 제어되었다. AlCrN 코팅층의 두께가 증가할수록, 이중층 코팅의 경도 및 내마모성은 점차 향상되었지만 코팅의 밀착력은 감소하였다. 일반적으로 AlCrN 코팅은 상대적으로 높은 잔류응력을 갖고 있으므로, AlCrN 층의 두께비율이 증가함에 따라 코팅내의 잔류응력이 높아져 코팅의 경도는 증가하고 밀착특성은 낮아진 것으로 판단된다. AlCrSiN 상부층 공정시 기판 바이어스 전압을 -50 ~ -200V 로 증가시키면서 이중층 코팅을 합성하였다. XRD 분석 결과, 공정 바이어스 전압이 증가함에 따라 AlCrSiN 상부층은 점차 비정질화 되었고, 코팅의 경도와 표면 특성이 향상되는 것을 확인하였다. 이러한 특성 향상은 높은 바이어스 인가가 이온 충돌효과의 증가를 야기시켰으, 이로 인해 치밀한 코팅층 합성에 의한 결과로 판단된다. AlCrN/AlCrSiN 이중층 코팅을 어닐링 한 후 경도 분석 결과, -150, -200V에서 합성한 코팅은 900도 이상에서 26GPa 이상의 높은 경도를 보인 것으로 보아 우수한 내열성을 갖는 것으로 확인 되었다. 이는 AlCrSiN 상부층의 높은 Si 함량 (11at.%) 으로 인한 충분한 $Si_3N_4$ 비정질상의 형성과, 고바이어스 인가로 인한 AlCrN 결정상과 $Si_3N_4$ 비정질상의 고른 분배가 코팅의 내열성을 향상시키는데 기여를 한 결과로 판단된다.

• Progress in Medical Physics
• /
• v.20 no.2
• /
• pp.80-87
• /
• 2009

Phase transformation, superelastic characteristics and variation of surface residual stress were studied for Nitinol shape memory alloy through application of UNSM technology, and life extension methods of stent were also studied by using elastic resilience and corrosion resistance. Nitinol wire of ${\phi}1.778$ mm showed similar surface roughness before and after UNSM treatment, but drawing traces and micro defects were all removed by UNSM treatment. It also changed the surface residual stress from tensile to compressive values, and XRD result showed less intensive austenite peak and clear martensite and additional R-phase peaks after UNSM treatment. Fatigue resistance could be greatly improved through removal of surface defects and rearrangement of surface residual stress from tensile to compressive state, and development of surface modification system to improve not only bio-compatability but also resistance to corrosion and wear will make it possible to develop vascular stent which can be used for circulating system diseases which run first cause of death of recent Koreans.

• Journal of the Korean Magnetics Society
• /
• v.21 no.2
• /
• pp.77-82
• /
• 2011

The use of soft magnetic materials have been increasing in the various industrial fields according to the increasing demand for high performance, automatic, miniaturing equipments in the recent our life. In this study, we investigated the effect of factors on the core loss and magnetic properties of electrical steel and soft magnetic composites. Furthermore, we reviewed the major efforts to reduce the core loss and improve the soft magnetic properties in the two main soft magnetic materials. Domain purification which results from reduced density of defects in cleaner electrical steels is combined with large grains to reduce hysteresis loss. The reduced thickness and the high electrical conductivity reduce the eddy current component of loss. Furthermore, the coating applied to the surface of electrical steel and texture control lead to improve high permeability and low core loss. There is an increasing interest in soft magnetic composite materials because of the demand for miniaturization of cores for power electronic applications. The SMC materials have a broad range of potential applications due to the possibility of true 3-D electromagnetic design and higher frequency operation. Grain size, sintering temperature, and the degree of porosity need to be carefully controlled in order to optimize structure-sensitive properties such as maximum permeability and low coercive force. The insulating coating on the powder particles in SMCs eliminates particle-to-particle eddy current paths hence minimizing eddy current losses, but it reduces the permeability and to a small extent the saturation magnetization. The combination of new chemical composition with optimum powder manufacturing processes will be able to result in improving the magnetic properties in soft magnetic composite materials, too.