• Journal of the Korean Magnetics Society
• /
• v.7 no.1
• /
• pp.44-48
• /
• 1997

The nanocrystalline Nd-Fe-B alloys with low Nd content were prepared by rapid solidification technique. The alloys consist of both$\alpha$-Fe as the main phase and $Nd_2Fe_{14}B_1$ as a secondary phase and have an ultrafine grain structure of about 30 nm. The addition of Ga in $Nd_4Fe_{82}B_{10}Mo_3Cu_1$ alloy increases remanence up to 1.29 T and improves squareness. The nanocrystalline $Nd_5Fe_{81}B_9Mo_3Cu_1Ga_1$ alloy has a volume fraction of $Nd_2Fe_{14}B_1$ phase of around 35% due to the increase of Nd content and shows an improved coercivity. The remanence, coercivity and energy product of optimally annealed nanocrystalline $Nd_5Fe_{81}B_9Mo_3Cu_1Ga_1$ alloy are 1.24 T, 257.4 kA/m (3.23 kOe), and 100.3 kJ/ ㎥ (12.6 MGOe), respectively.

• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.356-364
• /
• 1997

In order to study effects of Cu and Be on the microstructure and tensile properties of rapidly solidified Al-Mg alloys, Al-Mg-Cu-Be alloys have been rapidly solidified by inert gas atomization process. Microstructure of rapidly solidified Al-Mg-Cu-Be powders exhibited refinement and good dispersion of Be particles as increasing of solidification rate. Solidification rate of atomized powders was estimated to be about $5{\times}10^{3{\circ}}C/s$. Inert gas atomized Al-Mg-Cu-Be powders were hot-processed by vacuum hot pressing at $450^{\circ}C$ under 100 MPa and hot extruded with reduction ratio in area of 25: 1 at $450^{\circ}C$. The extruded Al-Mg-Cu-Be powders consisted of recrystallized fine Al grains and homogeneously dispersed fine Be particles, and exhibited improved tensile properties with increase in Cu content. $Al_2CuMg$ compounds precipitated in grain and grain boundaries of Al-Mg-Cu-Be alloys with aging heat treatment after solution treatment. Hardness and tensile properties were improved by increasing Cu content and Be addition. Compared with extruded Al-Mg-Cu powders, the extruded Al-Mg-Cu-Be powders exhibited finer recrystallized grains and improved tensile properties by dispersion hardening of Be and subgrain boundaries pinned by fine Be particles. After aging treatment, hardness and tensile properties were improved due to restricted precipitation by increasing of dislocation density around Be particles in matrix.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.5
• /
• pp.811-816
• /
• 2006

The single layered magnetic thin films with anisotropic magnetoresistance behavior have advantage on micro integration due to their low cost in manufacturing. Although the conventional MCo (M=Cu, Ag) amorphous ribbons using a rapid solidification process have showed appropriate for magnetic property for bulk devices, they are not appropriate for micro-scale devices due to their brittleness. We prepared the thermal evaporated 100 nm-thick $Cu_{1-x}Co_x\;and\;Ag_{1-x}Co_x(x=0.1{\sim}0.7)$ films on silicon wafers and investigated the magnetic property of the as-depo films such as magnetization and magnetoresistance ratio. We confirmed that the maximum MR ratio of 1.4 and 2.6% at the external field of 0.5 Tesla in $CuCo_{30},\;AgCo_{40}$ films, respectively. Our result implies that AMR may be slightly less than those of the conventional CuCo and AgCo ribbons due to surface scattering, but their AMR ratio be enough for micro-scale application with easy integration compatibility for the process without surface oxidation.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.154-158
• /
• 1999

Magnetic properties and microstructure of nanocrystalline $\alpha$-(Fe, Co)-based Nd-(Fe, Co)-B-Nb-Cu alloys have been investigated. $Nd_x(Fe_{0.9}Co_{0.1})_{90-x}B_6Nb_3Cu_1$(x=2, 3, 4, 5, 6) alloys prepared by rapid solidification process show amorphous phase except the one with x=2. By a proper annealing, the amorphous in the alloy is changed to a nanocrystalline phase. It is confirmed that the nanocrystalline alloys are composed of $\alpha$-(Fe, Co) and $Nd_2(Fe, Co)_{14}B_1$ phase. The optimally annealed $Nd_3(Fe_{0.9}Co_{0.1})_87B_6Nb_3Cu_1$ alloy shows the highest remanence of 1.55 T. The coercivity increases with the increase of Nd content The maximum coercivity of 4.6 kOe is obtained from an optimally annealed $Nd_6(Fe_{0.9}Co_{0.1})_84B_6Nb_3Cu_1$ alloy, resulting in the maximum energy product of 10.6 MGOe.

• Journal of the Korean Magnetics Society
• /
• v.3 no.4
• /
• pp.284-288
• /
• 1993

Low temperature magnetic properties and crystal structures of melt-spun $Sm_{2}Co_{7}B_{3}$ compound were characterized. The magnetic measurements in the temperature range 77 K~450 K indicated that a spin-reorientation took place at about 150~160 K. A large anisotropy was observed(Ha=135 kOe at 300 K, 725 kOe at 77 K) for $Sm_{2}Co_{7}B_{3}$ although the magnetic moment is rather low. The crystal structure of the $Sm_{2}Co_{7}B_{3}$ compound was analyzed in detail by Rietveld analysis of powder diffraction pattern, and it was revealed that B(4h) atoms are not placed in the Sm(2e) layer but in between the Sm(2e) and Co($6i_{1}$) layers.

• Journal of the Korean Magnetics Society
• /
• v.2 no.3
• /
• pp.233-238
• /
• 1992

Melt-spun $Nd_{14}Fe_{76}Co_4B_6$ and $Nd_{10.5}Fe_{79}Co_2Zr_{1.5}B_7$ ribbons were prepared under an externally applied magnetic field. Magnetic properties in terms of anisotropy were evaluated by discussing the effect of textured structure of the ribbon samples as well as its powders. About 32 % increase in $(B{\cdot}H)_{max}$ and 18.8 % increase in $B_r$ were observed along the perpendicular direction of the ribbon plane which is more prominent for the Nd-Fe-Co-Zr-B than for the Nd-Fe-Co-B alloy. The enhancement of magnetic anisotropy was monitored by measuring the anisotropy constant of each alloy as a function of quenching rate of the ribbon. It was found that for the melt-spun ribbon quenched at slow rate(less than 7 m/s) the magnetic field effect was overwhelmed by the heat gradient effect through the ribbon thickness while the field effect was prominent at intermediate quenching rate (more than 7~11 m/s). The reproducible maximum energy product, $(B{\cdot}H)_{max}$=16.4 MGOe can be obtained from the Nd-Fe-Co-Zr-B alloy.

• Journal of the Korean Electrochemical Society
• /
• v.18 no.2
• /
• pp.68-74
• /
• 2015

To compare the microstructure and electrochemical properties between two binary alloys (Cr-Si, Ni-Si), two composition of binary alloys with the same capacity were selected using phase-diagram and prepared by matrix-stabilization method to suppress the volume expansion of Si by inactive-matrix. Master alloys were made by Arc-melting followed by fine structured ribbon sample preparation by Rapid Solidification Process (RSP, Melt-spinning method) under the same conditions. Also powder samples were produced by wet grinding for X-Ray Diffraction (XRD) and electrochemical measurements. As predicted from the phase diagram, only active-Si and inactive-matrix ($CrSi_2$, $NiSi_2$) were detected. The results of Scanning Electron Microscope (SEM) and Transmission Electron Microscopy - Energy Dispersive X-ray Spectroscopy (TEM-EDS) show that Cr-Si alloy has finer microstructure than Ni-Si alloy, which was also predictable through phase diagram. The electrochemical properties related to microstructure were evaluated by coin type full- and half-cells. Separately, self-designed test-cells were used to measure the volume expansion of Si during reaction. Volume expansion of Cr-Si alloy electrode with finer microstructure was suppressed significantly and improved in cycle capability, in comparison Ni-Si alloy with coarse microstructure. From these, we could infer the correlation of microstructure, volume expansion and electrochemical degradation and these properties might be predicted by phase diagram.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2001.11a
• /
• pp.30-30
• /
• 2001

$Bi_2Te_3$계 열전재료는 200~400K 정도의 저온에서 네어지 변환효율이 가장 높은 재료로써 열전냉각, 바런재로 등에 응요하기 위하여ㅠ 제조법 및 특서에 관한 많은 연구가 진행되어 왔다. $Bi_2Te_3$계 화합물은 rhombohedral의 결정 구조를 가지는 층상 화 ;물로 결정대칭성으로 인해 연전기적으로 큰 이방성을 나타낸다. 현재는 일반향용고법에 의해서 입자를 a축 방향으로 성장시켜 큰 결정립을 가진 다결정재료를 사용하고 있으나, c면이 매우 취약하기 때문에 가공서이 나쁘다. 따라서 이와같은 단점을 개선하기 위하여 기계적 강도를 높일 수 있는 가공공정 및 합금설계에 대한 연구가 활발히 진행되고 있다. 측히 열간 압출법으로 제조된 열전재료는 결정립의 미세화와 높은 이방성으로 성능지수와 기계적 강도를 향상시킬 수 있다는 연구결과가 보고되고 있다 또한 Schultz드의 연구결과에 의하면 $Bi_2Te_3$ 계 열전재료는 소성변형에 의하여 발생한 점결함에 의하여 캐리어 농도가 변화되며 이로 인하여 재료의 전기적 성질이 결정된다고 하였다. 따라서 상당히 큰 소성가공량과 열전측성과의 관계를 규명하는 것은 매우 중요하다. 이에 본 연구에서는 압출변수 중 소성가공량에 중요한 변수로 작요아는 압출비를 변화시켜 최적의 열간 소성가공량을 검토하고, 이에 따른 열전측성과 압출비와의 상관관계에 대하여 연구하는 것을 목적으로 하였다. 연구에 사용된 N형의 조성은$Bi_2Te_{2.75}Se_{0.15}$로서 순도 99.99를 사용하였고, dopant로 0.1wt%의 $SbI_3$를 사용하였다. $Bi_2Te_{2.75}Se_{0.15}$ 분말은 가스분사법(Gas atomization Process)를 이용하여, 용탕제조시 아르곤가스로 산화를 방지하였고, 냉매로는 질소가스를 이용하였다. 제조된 분말을 기ㅖ적 분급법을 이용하여 분급하였고, 냉매로는 질소가스를 이용하였다. 제조된 분말을 기계적 분급ㅂ법을 이용하여 분급하였고, 압출에 이용된 분말은 250$\mu\textrm{m}$이하의 크기를 사용하였다. 또한 분말제조과정 중 형성되는 표면산화층을 제거하기 위하여 36$0^{\circ}C$에서 4시간동안 수소 환원처리를 행하였다. 제조된 분말은 열간 압출을 위하여 Aㅣcan에 넣고 냉간성형체를 만들고, 진공처리를 한 후 밀봉하여 탈가스처리를 하였다. 압출다이는 압출비가 각각 28:1과 16:1인 평다이(9$0^{\circ}C$)를 사용하여 각각 내경이 9, 12cm이고, 길이가 50, 30cm인 압출재를 제조하였다. 열간압출한 후의 미세조직을 광학현미경으로 압출방향에 평행한 방향과 수직방향으로 관찰하였고, 열간 압출재 이방성을 검토하기 위하여 X선 회절분석을 실실하여 결정방위를 확인하였다. 전기 비저항 및 Seebeck 계수 측정을 위하여 각각 2$\times$2$\times$10$mm^3$ 그리고 5$\times$5$\times$10$mm^3$ 크기의 시편을 준비하였다.준비하였다.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.29 no.5
• /
• pp.681-688
• /
• 1996

To investigate the effort of drying methods on the physicochemical properties of agar, gel strength, viscosity, melting and setting point, and phase transition by differential scanning calorimetery (DSC) during its heating were determined. In addition the structural differences of agar powder by scanning electron microscope (SEM) was examined. The most shortest onset temperature of gel strength increase was extruding method among any other methods. Viscosity of agar with hot air method, 400.00 cps at $45^{\circ}C$, was markedly increased, but with spraying and extruding ones were little change. The melting and setting point, and the temperature for maximum endothermic and enthalpy for agar with extruding one, $80.01^{\circ}C,\;36.05^{\circ}C\;and\;61.72^{\circ}C,\;0.73\;cal/g$, respectively, were lowest among the drying ones. But in the case of reheating after gelling, there were little change in all methods. Observing the surface structure of agar with SEM, extruding method showed the most unstable with absorptive property.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.880-894
• /
• 1995

Magnetic properties of $Nd_{x}{(Fe_{0.9}Co_{0.1})}_{90-x}B_{6}Nb_{3}Cu_{1}(x=\;3,\;4,\;5)$ rrelt-spun alloys with 6 at% B content were studied aiming for finding out a new $\alpha$-Fe based Nd-Fe-B nanocrystalline alloy with good hard magnetic properties. $Nd_{x}{(Fe_{0.9}Co_{0.1})}_{90-x}B_{6}Nb_{3}Cu_{1}$ melt-spun alloys prepared by RSP crystallized to nanocrystalline phase. An optimally annealed $Nd_{3}{(Fe_{0.9}Co_{0.1})}_{87}B_{6}Nb_{3}Cu_{1}$ melt-spun alloys had larger volume ratio of $\alpha$-Fe(Co) than that of higher Nd content alloy and showed high remanence of about 1.6 T. On the contrary, the increase of Nd content in $Nd_{x}{(Fe_{0.9}Co_{0.1})}_{90-x}B_{6}Nb_{3}Cu_{1}$ alloys gave rise to gradual increase of an amount of $Nd_{2}{(Fe,\;Co)}_{14}B$ phase and improved coercivity. An optimally annealed $Nd_{5}{(Fe_{0.9}Co_{0.1})}_{85}B_{6}Nb_{3}Cu_{1}$ alloy showed the most improved hard mag¬netic properties. The remanence, coercivityand energy product of the alloy were 1.35 T, 219 kA/m (2.75 kOe), and $129\;kJ/m^{3}$ (16.2 MGOe), respectively.