The purpose of this study was to verify the causal relationship between self-directed learning ability and career maturity by Middle and High School Students in Seoul. This study used Seoul Education Longitudinal Study(SELS) data. Using autoregressive cross-lagged modeling, the results was followed. first, self-directed learning ability value was had a statistically significant positive effect in accordance with the time course from middle school 1st grade to high school 3rd grade. Second, career maturity also had a statistically significant positive effect in accordance with the time course from middle school 1st grade to high school 3rd grade. Third, previous self-directed learning ability had significant positive effect on the later career maturity, but the previous career maturity had no significant effect on later self-directed learning ability.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.93-100
• /
• 2009

This study forms part of a research project that was carried out on the development and application of high-strength concrete for large underground spaces. In order to develop 50MPa high-strength concrete, eight optimal mixtures with different portions of fly ash and ground granulated blast furnace slag were selected. For assessments of shrinkage characteristics, free shrinkage tests with prismatic specimens and shrinkage crack tests were performed. The compressive strength was more than 30MPa at 7days, and stable design strength was acquired at 28days. High-strength concrete containing blast furnace slag shows large autogenous shrinkage, while large shrinkage deformations and cracks will occur when mixtures are replaced with large volumes of cementitious materials. Hence, for these high-strength concrete mixtures, the curing conditions of initial ages that affect the reaction of hydration and drying effects need to be checked.

• International Journal of Highway Engineering
• /
• v.11 no.2
• /
• pp.99-109
• /
• 2009

Fine-size exposed aggregate portland cement concrete pavements (FEACP) have surface texture of exposed aggregate by removing upper 2$\sim$3mm mortar of surface of which curing is delayed by using delay-setting agent. FEACPs have advantages of maintaining low-noise and adequate skid-resistance level during the performance period than general portland cement concrete pavements. It is necessary to ensure the durability environmental loading to prevent unexpected distress during the service life of FEACP. In the process of curing, volume change accompanied change in by moisture and temperature could be an important cause of crack in concrete to construct for successful FEACP, The use of chloride containing deicer may accelerate defects of concrete pavement, such as crack and scaling. This study aim to evaluate environmental loading resistance of FEACP, based on the estimation of shrinkage-crack-control-capability by moisture evaporation and scaling by deicer in freeze-thaw reaction.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.7
• /
• pp.152-163
• /
• 2019

In this paper, effect of steel fiber inclusion, compressive strength of matrix, shear reinforcement and shear span to depth ratio on the flexural behavior of UHPFRC(Ultra High Performance Fiber Reinforced Concrete) were investigated with test of 10-UHPFRC beam specimens. All test specimens were subjected to the flexural static loading. It was shown that steel fiber significantly improve the shear strength of UHPFRC beams. 2% volume fraction of steel fiber change the mode of failure from shear failure to flexural failure and delayed the failure of compressive strut with comparatively short shear span to depth ratio. UHPFRC beams without steel fiber had a 45-degree crack angle and fiber reinforced one had lower crack angle. Shear reinforcement contribution on shear strength of beams can be calculated by 45-degree truss model with acceptable conservatism. Using test results, French and Korean UHPFRC design recommendations were evaluated. French recommendation have shown conservative results on flexural behavior but Korean recommendation have shown overestimation for flexural strength. Both recommendations have shown the conservatism on the flexural ductility and shear strength either.

• Journal of the Korea Concrete Institute
• /
• v.20 no.6
• /
• pp.797-807
• /
• 2008

For this study, the semi-adiabatic temperature rising test is accomplished by using ternary system cement (OPC, BFS, FA) reducing temperature crack. Two tests are conducted; one is for the paste test, and the other is for the concrete test. As the results of paste tests, using fly ash is better to reduce hydration temperature than doing blast furnace slag. In the case of the paste mixed ternary system cement, the more fly ash is mixed and the less blast furnace slag is used, the lower the temperature is. The less the mixture ratio of blast furnace slag is and the more the mixture ratio of fly ash is, the later the temperature rising velocity and descending velocity are. Besides, the temperature is lower if water/binder ratio is high. The use of ternary system cement has the retardation effect of temperature rising because the time to reach the maximum temperature is in the order of OPC100, binary system cement, and ternary system cement. From the test, the maximum temperature of concrete used ternary system cement is $8{\sim}11^{\circ}C$ lower than that of concrete used OPC100. Moreover, temperatures rising velocity and descending velocity of ternary system cement range $47{\sim}51%$ and $37{\sim}42%$ compared with OPC100. The specimen of concrete shows remarkable low internal temperature and slow temperature rising velocity and descending velocity compared with the specimen of paste because it is that temperature loss of concrete is much more than paste specimen according to aggregates.

• Tunnel and Underground Space
• /
• v.28 no.1
• /
• pp.97-110
• /
• 2018

The application of sprayed waterproofing membrane with high adhesion and ductility is considered to be promising as a measure for repair and reinforcement of a tunnel structure. Therefore, a powder-type and one-component membrane prototype with high tensile and bond strengths was made in this study. Then, its reinforcement effect on a shield segment was evaluated by carrying out a series of full-scale loading tests of segment specimens on which the membrane was sprayed. From the tests, it was confirmed that the initial cracking loads increased by approximately 34% due to cracking retardation by membrane coating. Even though the increase of failure loads were not so high as cracking loads, the strain-softening behaviors were observed from specimens coated by the membrane. Therefore, it is expected that the membrane coated on the inner surface of a lining might be effective in preventing its brittle failure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.9
• /
• pp.4602-4609
• /
• 2013

In summer and winter, the difference between the temperature during the day and that during the night is high, which leads to various problems during concrete placement, such as cracks and defects in the concrete as well as low durability and strength. Although nuclear power plant concrete is widely used for placement in all seasons, particular attention must be paid to its quality during the summer. Therefore, we evaluated the effects of a cooling method for mixing water, which is a commonly used hot weather precooling method, and the use of a retarder, on the characteristics of Nuclear Power Plant concrete. In the cooling method for mixing water, cold water at 5 was used, with 50% of the water content consisting of ice flakes. The effects of using a retarder were evaluated by reviewing the characteristics of the cement at the unset stage and after hardening. To evaluate the characteristics of the unset cement, we measured the slump, air volumes, setting times, and pressure strengths after hardening. Furthermore, we measured the heat of hydration at different temperatures; the loss of heat was minimized using insulation. Both the slump time and the complete ageing time of the air volume were found to be 120 min at $20^{\circ}C$ and 40 min at $40^{\circ}C$. In the case when the cooling method for mixing water was used and in the case when a retarder was used, the initial and final sets by penetration resistance were delayed, and the delay decreased with increasing air temperature. For the heat of hydration, the cooling method for mixing water not only lowered the maximum temperature but also delayed its attainment. However, the use of a retarder had no effect on the maximum temperature. Moreover, in the early ages (e.g., 3 and 7 days), the pressure strength of the concrete was lower than that of plain cement. However, the strength of 28-day concrete met the standard construction specifications.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.703-710
• /
• 2010

Reinforced concrete beams of existing structure often encounter insufficient shear problems for various reasons. Application of steel plates is one of widely used methods for shear strengthening of reinforced concrete beams that are insufficient of shear capacity. This study presents test results on strengthening shear deficient RC beams by external bonding of vertical and diagonal slit type steel plates with anchor bolt. Test parameters are width, interval, angle and length of slits with anchor bolt. The purpose was to evaluate the failure modes and shear capacities for RC beams strengthened by various slit type steel plates with anchor bolt. The results showed that the slit type steel plate specimens strengthened by adhesive bonding and bolting failed in shear fracture modes at maximum load. Flexural crack first occurred on the tension face of beam and then inclined cracks occurred on the shear span. Finally, slit type steel plates strengthened by adhesive bonding and fastening bolts managed to delay abrupt debonding and didn't detach fully from main body of RC beam.

• Explosives and Blasting
• /
• v.31 no.2
• /
• pp.14-24
• /
• 2013

The most effective way of the rock removing works in the downtown area is to removing rocks by splitting the rock by blasting with small amount of explosives in the hole. However environmental factors not only limit the applications but also increase the forbidden area. As this is a distributed multi-stage blasting method and to reduce vibration by applying the optimized precisioncontrol-blasting method, it is applicable in all situations. The process is to fix the stemming-help plastic sheet to the hole entrance when stemming explosives and insert detonator and explosive primer with same delay time, two or three sets. This method is more efficient in the downtown area where claims and dispute from vibration are expected. This method is easily usable by designing blast pattern even in the area where delay time blasting is difficult after multi-stage explosive stemming due to short length of blast hole (1.2~3.0m) and there is no detonator wire shortage or dead-pressure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.397-400
• /
• 2008

MgO powder-mixed concrete, expanded at the lower temperature around $850{\sim}1000$ degree celcius, might have long-term expansibility, which could remunerate for the contraction of concrete with delayed expansion, and through the process, the crack resistance of mass concrete might be improved. Currently used expandable concrete additive has three different types : CSA, CaO and MgO. In this study, therefore, such tests as carbonation, chloride diffusivity, freezing-thawing resistance and sulfate resistance after 56 days' curing were implemented and compared the results with the concrete with no MgO mixed to evaluate the durability of 5% MgO-mixed concrete after longer period of time. The degree of hydration for the MgO-mixed cement paste was analyzed after 1 day, 3 days, 7 days, 28 days, and 56 days using SEM, XRD, DSC.