• Journal of the Korean Magnetics Society
• /
• v.22 no.5
• /
• pp.167-172
• /
• 2012

In order to analyze the formation mechanism of iron oxide nanoparticles, we measured the heat flow of $Fe(OL)_3$ precursor with temperature, and TEM images and AC susceptibility of aliquots samples sequentially taken from the reaction solution, respectively. The thermal decomposition of two OL-chain from $Fe(OL)_3$ produced the Fe-OL monomer, which were contributed to the formation of iron oxide nanoparticles. In the initial stage of nanoparticles formation, the small iron oxide nanoparticles had ${\gamma}-Fe_2O_3$ structure. However, as the iron oxide nanoparticles were rapidly growth, the iron oxide nanoparticles showed ${\gamma}-Fe_2O_3$-FeO core-shell structure which the FeO layer was formed on the surface of ${\gamma}-Fe_2O_3$ nanoparticles by insufficient oxygen supply from the reaction solution. These nanoparticles were transformed to $Fe_3O_4$ structure by oxidation during long aging time at high temperature. Finally, the $Fe_3O_4$ nanoparticles with high saturation magnetization and stable in the air could be easily synthesized by the thermal decomposition method.

• Journal of the Korean Magnetics Society
• /
• v.25 no.1
• /
• pp.10-15
• /
• 2015

The model for the magneto-impedance of composite wires composed of highly conductive nonmagnetic metal core and soft magnetic shell was derived based on the Maxwell's equations. The Cu($100{\mu}m$ diameter)/$Ni_{80}Fe_{20}$($15{\mu}m$ thickness) core/shell composite wire was fabricated by electrodeposition. The impedance spectra for the $Cu/Ni_{80}Fe_{20}$ core/shell composite wire were measured in the frequency range of 10 kHz~10 MHz under longitudinal dc magnetic field in 0 Oe~200 Oe. The spectra of complex permeability in circumferential direction were extracted from the impedance spectra by using the derived model. The extracted spectra of complex permeability showed relaxation-type dispersion which is well curve-fitted with Debye equation with single relaxation frequency. By analyzing the magnetic field dependence of the complex permeability spectra, it has been verified that the composite wire has magnetic anisotropy in longitudinal direction and the origin of the single relaxation process is the magnetization rotation in circumferential direction.

• Journal of the Korean Magnetics Society
• /
• v.10 no.6
• /
• pp.269-273
• /
• 2000

Fe-l7Cr-2M(M=Si, Nb, Mo) alloy powder was prepared by plasma electrode rotating atomizer and than the alloy powder was formed and sintered. The particle shape of the Fe-l7Cr-2M(M=Si, Nb, Mo) alloy power is spherical. The saturation magnetization of the sintered Fe-17Cr-2Mo and Fe-l7Cr-2Nb alloy are 155 emu/g. The saturation magnetization of the sintered Fe-l7Cr-2Si alloy is less than that of the sintered Fe-l7Cr-2Mo and Fe-l7Cr-2Nb alloy. The amplitude relative permeability of the sintered Fe-l7Cr-2M(M=Si, Nb, Mo) alloy has the maximum value in the range of 3∼5 Oe applied field at forming pressure 12 ton/cm$^2$, sintering temperature 1200$^{\circ}C$, and frequency 1 kHz. Power loss of the sintered Fe-l7Cr-2Nb alloy is 40 mW/cc at applied field, H$\sub$a/=5 Oe, and frequency, f=1 kHz. The power loss of the sintered Fe-l7Cr-2Nb alloy is a half of that of the sintered Fe-l7Cr-2Si and Fe-l7Cr-2Mo alloy.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.100-105
• /
• 2005

$Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by DTA/TGA, XRD, SEM, and $M\ddot{o}ssbauer$ spectroscopy, VSM. $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ has spinel structure and behaved superparamagnetically. The estimated size of superparammagnetic Ni-Zn ferrite nanoparticle is around 10 nm. The hyperfine fields at 13 K for the A and B patterns were found to be 533 and 507 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle is about 250 K. The magnetic anisotropy constant and relaxation time constant of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle were calculated to be $1.6\times10^6\;ergs/cm^3$ and ${\tau}_0=5.0{\times}10^{-13}$ s, respectively. Also, Temperature increased up to $43^{\circ}C$ within 10 minutes under AC magnetic field of 7 MHz. It is considered that $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ is available for biomedicine application such as hyperthermia, drug delivery system and contrast agents in MRI.