• Electrical & Electronic Materials
• /
• v.1 no.2
• /
• pp.126-135
• /
• 1988

Acrylonitrile-Acrylic acid 공중합체와 이를 amidation시킬 공중합체에 구리착물을 형성시켜 IR spectrum분석, 점도측정, 전자현미경관찰, 열분석, 전기전도성등을 검토하였다. AN-AA 공중합체-Cu(II)와 아미드화 AN-AA 공중합체-Cu(II)착물은 pH9의 범위에서 가장 안정한 값을 가지며 착물이 형성되거나 Cu$_{x}$S가 도입된 공중합체는 그 구조가 ompact해짐을 알 수 있었다. 공중합체에 Cu(II)착물이 형성되면 열안정성이 감소되며 Cu(II)착물은 아세톤 용액에서 요오드로 dope 될 때 저항값이 $10^{5}$-$10^{6}$.OMEGA..cm를 나타냈다. 저항값은 CuCl$_{2}$와 I$_{2}$의 양에 영향을 받으며 20wt% 이상의 CuCl$_{2}$와 1.0wt% I$_{2}$로 처리하였을 때 반도체영역의 저항값을 보였다. 또 Cu$_{x}$S를 도입할 경우 CuSO$_{4}$의 농도가 30g/l로, 3시간 반응시켰을 때 가장 만족스러운 전도도값을 나타냈다. 공중합체-Cu(II)보다 구리이온을 도입한 Cu$_{x}$S공중합체의 전도도값이 $10^{4}$정도로서 공중합체-Cu(II)보다 높은 전도성을 나타냈다.다.

• Polymer(Korea)
• /
• v.25 no.1
• /
• pp.108-114
• /
• 2001

Crosslinked poly(glycerol-co-malate)s were synthesized from L-malic acid in Krebs cycle and glycerol. The synthesized polymer was identified by FT-IR spectroscopy. Swelling degrees of the copolymer hydrogels were increased with an increase in pH of the aqueous solution. Hydrolytic behaviors of the crosslinked copolymers were investigated in various pH buffer solutions at 37${\circ}C$. The Hydrolysis of the copolymers proceeded faster with increasing pH of the aqueous solution. Releasing behaviors of the model drug such as diclofenac monosodium salt were also measured in various pH aqueous solutions at 37${\circ}C$. The release concentration of diclofenac monosodium salt from the hydrogel systems was increased with increasing pH. These facts indicate that the unreacted carboxyl and hydroxyl groups in the copolymers are greatly affected by pH in the conditions.

• Polymer(Korea)
• /
• v.24 no.6
• /
• pp.787-793
• /
• 2000

The acrylonitrile copolymer/dimethylformamide (DMF) solutions were prepared to investigate the gelation behavior and critical gel concentration (c＊). Gelation is rapidly progressed with the increase of molecular weight of copolymer, but significantly delayed with supercooling temperature and comonomer contents. The c＊ behavior showed contrary trend against gelation behavior. In dynamic viscoelastic test, two glass-transition region were observed in film obtained from gelled solution whereas one glass-transition in film obtained from true solution. This result supports the idea that an ordered junction zone is formed by the dipole-dipole interaction of intermolecularly neighboring stereo-regular parts of atactic acrylonitrile copolymer chains due to a nucleation process in the solution.

• Membrane Journal
• /
• v.31 no.4
• /
• pp.268-274
• /
• 2021

One of the chronic problems in the issue of global warming is the emission of greenhouse gases. Carbon dioxide (CO₂), which accounts for the highest proportion of various greenhouse gases, has been continuously researched by humans to separate it. From this point of view, a poly(vinyl alcohol) (PVA)-based copolymer with acrylic acid monomer was utilized in a gas separation membrane in this study. We employed a free radical polymerization to fabricate PVA-g-PAA (VAA) graft copolymer. It was utilized in the form of a composite membrane on a polysulfone substrate. The proper amount of acrylic acid reduced the crystallinity of PVA and increased CO₂ solubility in separation membranes. In this perspective, we suggest the novel approach in CO₂ separation membrane area by grafting and solution-diffusion.

• Proceedings of the Korean Fiber Society Conference
• /
• 1998.10a
• /
• pp.21-24
• /
• 1998

흡수성 고분자는 주로 기저귀, 생리대, 농업용 뿌리 덮개 등에 사용되며, PAN(폴리아크릴 로니트릴) 그라프트 전분으로 대표되는 그라프트 공중합체와 가교된 아크릴레이트 고분자로 대표되는 수용성 단량체의 단중합체 또는 공중합체 등에 대한 연구가 가장 활발히 이루어져 왔다. 이들 고흡수성 재료들은 염용액에 대한 흡수도가 낮다는 단점이 있으며, 보다 강한 이온기를 도입하거나, 고흡수성 재료가 양쪽성을 나타낼 경우, 염에 대한 흡수도가 개선된다는 연구결과가 보고된바 있다. (중략)

• Journal of Industrial Technology
• /
• v.18
• /
• pp.277-287
• /
• 1998

In this work continuous thermodynamics was adopted for describing the influence of copolymer polydispersity on phase separations in random copolymer solutions. Continuous themodynamic frameworks were formulated using the Flory-Huggin's excess Gibbs free energy model in which the concentration- and temperature-depentent terms of interaction parameter x were modified. Cloud-point curves and coexistence curves of poly(ethylene-vinylactate)/methylacetate solutions and poly(ehtylene-vinylacetate)/ethylacetate solutions were measured, and experimental data were fitted with theoretical relations formulated in this work. Calculated could-point curves were more good ageeable with experimental data than the modified Flory-Huggins's relations. Coexistence curves which were evaluated by using parameters of x estimated from experimental cloud-point curves, were found to coincide with experimental data.

• Polymer(Korea)
• /
• v.24 no.3
• /
• pp.431-436
• /
• 2000

To improve the thermal and mechanical properties of homo poly(L-lactic acid), DL-mandelic acid, one of the natural $\alpha$-hydroxy acid with aromatic ring as the side-chain residue was used as the comonomer. Copolymers with different contents of mandelic acid were prepared and characterized. The resulting copolymers were mostly amorphous. As the amount of mandelic acid in the monomer feed increased, the molecular weight of the resulting polymers tended to decrease linearly. T$_{g}$ and T$_{d}$ of the copolymer, however, were found to shift toward higher temperature, suggesting the improved thermal stability by increasing content of mandelic acid moiety. Tensile measurements of cast films showed somewhat improved values in the copolymers with mandelic acid content of 5 and 10 wt%.%.%.

• Polymer(Korea)
• /
• v.32 no.6
• /
• pp.580-586
• /
• 2008

Copolyimides were synthesized from 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) and 1,3-bis(3-aminophenoxy)benzene (BAPB) with different mole ratios of 2,2-bis[4-(4-aminophenoxy)pheny1]hexafluoropropane (BAPP). The solution cast film of poly(amic acid) (PAA) was heat treated at different temperatures to create copolyimide films. The PI copolymer films were found to exhibit good optical transparencies. The thermomechanical properties, morphology, and optical transparency of PI films were examined using fourier transform infrared spectroscopy (FT-IR), wide-angle X-ray diffraction (XRD), scanning electron microscopes (SEM), differential scanning calorimeter(DSC), thermo-gravimetric analyzer (TGA), universal tensile machine (UTM), and IN - Vis. spectrometer. The glass transition temperature ($T_g$), ultimate strength, and initial modulus linearly increased with increasing BAPP mole fraction. However, thermal stability($T_D{^i}$) of the copolyimide remains constant regardless of BAPP loadings. It was found, however, that the optical transparency decreases slightly upon increasing the BAPP content because of the formation of the charge transfer complexes.

• Polymer(Korea)
• /
• v.37 no.6
• /
• pp.736-743
• /
• 2013

Novel carbazole based copolymers were synthesized by Suzuki coupling polymerization. (Diphenylene)vinylene and n-octyl was introduced to carbazole as pendants for reducing band gap and improving solubility, respectively. Thermal, photoluminescence and electro-luminescence of copolymers were studied for applying the emitting layer of polymer light emitting diode (PLED). Maximum UV-vis absorption and photoluminescence (PL) emission wavelength of copolymers showed 333~340 nm and 409~464 nm in solution state, respectively. The relative quantum yield using 9,10-diphenylanthracene as a reference was 25.8%. These copolymers exhibited high thermal stability ($T_d$ = $350^{\circ}C$) and good film forming ability. Good luminance was obtained at voltages lower than 8 V and the onset voltage was observed at 4.0 V.

• Polymer(Korea)
• /
• v.27 no.1
• /
• pp.17-25
• /
• 2003

Using atom transfer radical polymerization (ATRP), polystyrene macroinitiators and polystyrene-b-poly(t-butyl acrylate) (PS-b-P(tBA) block copolymers were synthesized by CuBr/PMDETA catalyst system in solution. After hydrolysis, polystyrene-b-poly(acrylic acid), amphiphilic block copolymers, were formed. Subsequent neutralization of polyacid block led to the block ionomers. The molecular weight of the synthesized PS-b-P(tBA) block copolymers was easily-controlled to 5000-10000 and their distributions were less than 1.2. The chemical structures of the synthesized block copolymers were characterized by $^1$H-NMR and FT-IR. In the DSC thermograms, $T_g$ appeared in the vicinity of 100 $^{\circ}C$ because of higher styrene content. In addition, the phase separation of the block ionomers was observed by TEM.