• Journal of the Korea Institute of Building Construction
• /
• v.15 no.3
• /
• pp.257-263
• /
• 2015

In this study, the quality of blast furnace slag and the engineering properties of recycled aggregate based mortar with variable replacement of blast furnace slag have been focused. Blast furnace slag(BS) manufactured in various areas in Korea were prepared for this study. For the investigation results, 4 types(among the all of 9 types) of the experimental results were identified as below the standard level when using blast furnace slag chosen from different factories. Especially the particle size of the blast furnace slag was considered as the largest problem. When using BS in the recycled aggregates based mortar, the increase amount of blast furnace slag, increased the fluidity but delayed the setting time and decreased strength at early age. Based on the relationship of the amount of BS and the engineering properties of mortar, this study found that the amount of $SO_3$ and L.O.I affect the setting time, 3 days strength and 91 days strength to the certain standard level.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.48-55
• /
• 2022

This study uses the recovered water as mixing water and artificial lightweight aggregate pre-wetting water as part of a study to increase the recycling rate and reduce greenhouse gas of the ready-mixed concrete recovered during the concrete transport process, and cement fine powder of blast furnace slag(BFS) and fly ash(FA). The engineering characteristics of the three-component lightweight aggregate mortar used as a substitute were reviewed. For this purpose, the flow, dry unit mass, compressive strength, drying shrinkage, neutralization depth, and chloride ion penetration resistance of the three-component lightweight aggregate mortar were measured. When used together with the formulation, when 15 % of BFS and 5 % of FA were used, it was found to be positive in improving the compressive strength and durability of the mortar.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.49-55
• /
• 2011

The distresses of alkali-silica reaction (ASR) was recently reported at highway cement concrete pavement in Korea, which showed typical cracking and spalling patterns of ARS. Korea is was no longer safe zone against ASR, needding to find a control methodology against ASR. The purpose of this research was to provide a control methodology against ASR using mineral admixtures through a series of laboratory test program. Laboratory works included the accelerated mortar bar test (AMBT) by ASTM C 1260 regulation with five types of aggregate and three types of mineral admixtures (fly ash, ground granulated blast-furnace slag and silica fume). The result of ASTM C 1260 test for five types of aggregates without mineral admixtures showed that Siltstone and Mudstone were found to be "reactive." Tuff and Andesite-1 were found to be "possiblely reactive." In case of concrete mixed with 10, 20, and 30% fly ash, all specimens except Mudstone mixed with 10% FA were found to be "non-reactive". In cases of concrete mixed with 30, 40, and 50% ground granulated blast-furnace slag and 5, 7.5, and 10% silica fume, all specimens were found to be "non-reactive." These results could be selectively applied in constructions in Korea.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.701-704
• /
• 2008

The case of failure of Alkali-silica reaction (ASR) on the cement concrete pavement was reported in Korea. In the United States America, the fly ash has less than 10 percent Cao reported that prevent expansion by ASR. Most of all fly ash in Korea have less than 10 percent CaO, therefore it is similar ASTM F fly ash in the USA. Crushed aggregates of the test section had expansion behavior by potential ASR that the ASTM C 1260 test method tested expansion 0.17 percent during 14 days. The test section of concrete pavement used crushed aggregate was constructed that fly ash have 20 percent weight of cementitious materials to prevent expansion by ASR. This study was performed flexural strength test for elapsed days and durability by freeze-thaw test. It was shown that flexural strength was increased elapsed days and good performed freeze-thaw test. This study shown that fly ash concrete pavement was good performance in the test section.

• The Journal of Engineering Geology
• /
• v.12 no.1
• /
• pp.95-109
• /
• 2002

A significant question is what role does newly-formed expansive mineral growth play in the premature deterioration of concrete. These minerals formed in cement paste as a result of chemical reactions involving cement paste and coarse/fine aggregate. Petrographic observations and SEM/EDAX analysis were conducted in order to determine chemical and mineralogical changes in the aggregate and cement paste of samples taken from lowa concrete highways that showed premature deterioration. Formation and expansive mechanisms involved in deterioration were Investigated. Brucite, Mg(OH)$_2$, is potentially expansive mineral that farms in cement paste of concretes containing reactive dolomite aggregate as a result of partial dedolomitization of the aggregate. No cracking was observed to be spatially associated with brucite, but most brucite was microscopic in size and widely disseminated in the cement paste of less durable concretes. Expansion stresses associated with its growth at innumerable microlocations may be retrieved by cracking at weaker locations in the concrete. Ettringite, 3CaO.Al$_2$O$_3$.3CaSO$_4$.32$H_2O$, completely fills many small voids and occurs as rims lining the margin of larger voids. Microscopic ettringite is common disseminated throughout the paste in many samples. Severe cracking of cement paste causing premature deterioration is often closely associated with ettringite locations, and strongly suggests that ettringite contributed to deterioration. Pyrite, FeS2, is commonly present in coarse/fine aggregates, and its oxidation products is observed in many concrete samples. Pyrite oxidation provides sulfate ions for ettringite formation.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.2
• /
• pp.161-168
• /
• 2012

The purpose of this study was to investigate the influence of recycled aggregates powder (RP) contents on recycled aggregates (RA) using fly-ash (FA) mortar in a condition of zero cement targeting earth filling materials, and the results can be summarized as follows. First, there was a tendency that as RP contents increased, W/B and air contents increased also. In the case of compressive strength, the strength was hardly developed at the early age, which was prior to 14 days; however, with the starting point of 14 days of age, strength of around 1.5~2.0 MPa was developed when it arrived at 28 days. At a curing temperature of $20^{\circ}C$, the more RP contents increased, the more the compressive strength increased in comparison with FA 100% at all levels except RP 100 %, showing the highest compressive strength at RP 25 %. At a curing temperature of $35^{\circ}C$, the temperature-dependence appeared to be large, as the RP contents were decreased compared to the curing temperature of $20^{\circ}C$. In addition, based on SEM analysis, this study was able to confirm that a pozzolanic reaction formed by an alkali stimulus of RA with the lapse of certain days even in 100 percent FA, causing the densification of tissues, and with RP 25%, hydrate was created the most densely by the hydration of unhydrated cement particles and pozzolanic reaction of FA.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.540-548
• /
• 2002

The purpose of this study is to analyze the application of oyster shells (OS) as aggregates for concrete. For this purpose, five reference mixes with W/C ratios of 0.4 ∼0.6 at intervals of 0.05 were used. The replacement proportion of OS was varied with ratios of 0, 10, 30, 50 and 100％ by volume of fine or coarse aggregate in the reference mixes. OS was washed and crushed for using as aggregates. New chemical reaction between crushed OS aggregate and cement paste was tested through XRD and SEM analysis. Two strength properties (compressive and flexural) were considered. Strength tests were carried out at the ages of 1, 3, 7, 14 and 28 days. The variations of workability, air content and density, drying shrinkage of the specimens with different proportions of OS were also studied. Finally, the hollow concrete block using OS as a substitute material for fine aggregate was made for testing the application of OS. Experimental results showed that my new chemical reaction did not occur due to mixing OS in concrete. The workability and strengths decreased with increase in proportion of OS. The same trend was observed in density and unit weight, but air content increased due to the inherent pores in OS, which showed a possibility to produce light weight concrete with low strength by using OS as coarse aggregates for concrete. Tests on hollow concrete block showed that the compressive strength and absorption ratio were satisfied with quality requirements when the fine aggregate was substituted with OS up to 50％ in volume.

• Journal of the Korea Concrete Institute
• /
• v.19 no.5
• /
• pp.577-584
• /
• 2007

The effect of steel microfibers (SMF) on alkali-silica reaction (ASR) was investigated using two types of reactive aggregates, crushed opal and a pyrex rod of constant diameter. Cracks are less visible in the SMF mortars compared with the unreinforced mortars. Due to crack growth resistance behavior in SMF mortar specimens, the strength loss is eliminated and the ASR products remained well confined within the ASR site. The expansion and the ASR products were characterized by microprobe analysis and inductively coupled plasma (ICP) spectroscopy. The confinement due to SMF resulted in a higher Na and Si ion concentration of the ASR liquid extracted from the reaction site. The higher concentration reduced the ASR rate and resulted in a lower reactivity of the reactive pyrex rods in SMF mortars.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1993.04a
• /
• pp.1-5
• /
• 1993

In the country, due to short comings of natural aggregates of good quality, it is common to use crushed stones. However, the investigation has not been done on the chemical reaction of crushed stones. This study tested and analyzed the aggregate chemical reaction by petrographic examination(ASTM C 295) for the test aggregates which had been tested by chemical method(ASTM C 289) in the first year. As a result, most of test aggregates didn't show any reaction but many have common deleterious mineral. Therefore, there exists the possibility of chemical reaction in petrogrphic point of view

• Proceedings of the Korea Concrete Institute Conference
• /
• 1989.10a
• /
• pp.1-4
• /
• 1989

Recently, as the natural aggregates are exhausted, using the crashed stones bring the possibility of the alkali-aggregate reactivity. In this study, the samples are collected from the stony moutains chosen by using a geoligical survey map and analyzed in terms of the amount and the shape of the reaction minerals by a polarization microscope and X-ray diffraction which beling to the petrographic examination of aggregates for concrete. From this study, most samples of the sedimentary rocks and the granitte of the ignious rocks show the possibility of the alkali-aggregate reactivity.