• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.4
• /
• pp.747-754
• /
• 1988

High strength steels (HS) of dual phase and monogalvanized steel sheets (GA ; plated plane, GAB ; bare plane0 were used to investigate the fatigue strengths of four kinds of single-spot-welded joint specimen under tensile-shear repeated load. The specimen is classified as the same mating metal specimen (HS*HS, GA*GAB) and different mating metal specimen (HS*GA, HS*GAB). Some of the results are ; (1) Static tensile load of single-spot-welded joint specimens is proportional to tensile strength of metal and rigidity of mating metal sheet. (2) Fatigue life of HS*HS specimens increased about 20% longer than that of GA*GAB specimens in low cycle range. (3) In different mating metal specimens, the fatigue life of HS*GA specimens increased about 84% more that of HS*HS specimens in high cycle range.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.23 no.5
• /
• pp.471-477
• /
• 2015

In this study, the property of crack propagation and growth at high tension steel plate existed with center crack is investigated. The behaviors of fracture mechanics due to existence or not of hole near the center crack in specimen and the length of crack length are investigated when the load is applied at the one side end of specimen. Stress, deformation and deformation of this specimen are evaluated through simulation analysis. By the analysis results at this study, stress intensity factors are obtained. The damage happened at machine or structure with crack or defect can be estimated on the basis of study results.

• Journal of the Society of Naval Architects of Korea
• /
• v.29 no.4
• /
• pp.214-226
• /
• 1992

In this paper, the characteristics of fatigue crack growth in the spot welded joint of the same kinds of specimens($HS{\times}HS,\;GA{\times}GAB$) and different kinds of specimens($HS{\times}GA,\;HS{\times}GAB$) which consist of dual phase high strength steel(HS) and monogalvanized steel(GA) were examined with static tension tests and axial tension fatigue tests. Some of the important results are as follows : 1. The divergence of tensile strengths among the same and different kinds of spot welds under the same conditions is comparatively low regardless of the difference of stiffness. 2. At the low load bevel and long life legion, the fatigue crack is initiated near the nugget. However, in the high load level and short life region, it occurs a tittle far from the nugget. 3. It has shown a linear relation between maximum stress Intensity factor, Kmax and fatigue life, $N_f$ among each of the spot welds and has gathered in a narrow band on the log-log graph paper. $Kmax=H{\cdot}{N_f}^{P}$ where H and P are a material constant.