• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.8
• /
• pp.449-455
• /
• 2016

This study is a part of research to develop a steel-concrete hybrid girder using ultra high-performance concrete with a compressive strength of 80 MPa. To this end, the Eurocode design formula for the shear resistance developed in a concrete-to-concrete interface was examined for the interface between concrete layers of different strengths. To examine the effect of the surface roughness on the shear resistance, a push-out test was conducted on specimens while considering the parameters of the Eurocode design equation. The actual behavior was evaluated with respect to the compressive strength of the concrete, the reinforcement ratio of the shear rebar, and the interfacial surface condition. The specimen with a rough interface shows 20-50% higher shear strength than that estimated by the design equation. In the case of failure mode, abrupt failure tends to occur at the interface of the concrete layer for the specimen with a low reinforcement ratio. It is expected that the shear strength of the concrete layer will increase according to the strength differential in the concrete layers.

• Journal of the Korea Concrete Institute
• /
• v.28 no.6
• /
• pp.637-646
• /
• 2016

In this study, slant shear tests for the prism specimens strengthened with ultra-high performance fiber reinforced concrete (UHPFRC), normal- and high-strength concrete were performed to evaluate the interfacial shear strength between old and new concrete substrate. Test parameters are the roughness of surface, concrete strength, and fiber volume fraction of UHPFRC. The surface of the concrete was roughened by shot blasting. Test results showed that the adhesion bond resistance of the specimen with a roughened surface was very large compared to that of the specimen with a smooth surface. In addition, the interfacial shear strength appeared to be affected by the concrete strength rather than the fiber volume fraction. For the roughened surface by shot-blasting method, interfacial shear resistance exceeded the upper limit which is presented in current design codes even if the shear-friction reinforcements are not provided. Based on the test results, it is applicable to use the current concrete design codes to achieve the shear-friction design for the interface between conventional concrete and UHPFRC. However, for the surface which is not processed, it would be appropriate to provide additional shear-friction reinforcement.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.4
• /
• pp.400-413
• /
• 2016

The horizontal shear capacity when the flange of a steel girder is replaced with 80 MPa concrete is important for its structural safety. In this study, 6 specimens with different interface conditions were designed and fabricated based on the Limit State Design Code on Korean Highway Bridges and static tests were performed to measure the horizontal shear capacity. Not only the resistance factors of the stud shear connector, concrete and reinforcement, but also the surface conditions of the casing concrete and spacing of the horizontal shear reinforcements were used as the experimental variables. The experiments showed that the interfaces between the steel girder and the concrete flange have stronger joint performance than those between the concrete flange and deck slab. To ensure the composite action in the plastic zone, the conservative horizontal shear reinforcement is more important than the roughness in the concrete face.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.45-51
• /
• 2013

Short beam tests of GFRP and CFRP specimens exposed to high temperature were conducted to measure the inter-laminar shear strength. For the phase I test, the exposure time and temperature were varied to measure reduction in the strength due to the applied conditions. As a results, the critical temperature was found to $270^{\circ}C$ for the both FRP reinforcements. The high temperature, which causes 50% loss of inter-laminar shear strength, is defined as the critical temperature in this study. It should be noted that the critical temperature for the inter-laminar shear strength is mainly dependent on resin properties not on fiber type. In the phase II test, the effect of exposure time was investigated at intervals of 0.25hour for the critical temperature. All test results demonstrate that the exposure time effect is not significant compared to the maximum exposure temperature, but it is not negligible and, moreover, is significant at the critical temperature.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.108-115
• /
• 2014

Mechanical properties of GFRP rebars significantly decrease due to high temperature as well as alkalinity of concrete. This study focuses on the long-term reduction of inter-laminar shear strength of pre-damaged GFRP rebars by high temperature. For this investigation, bare GFRP rebar specimens were exposed to $270^{\circ}C$ for 1hour and then immerged in alkali solution for several months and tested in shear. No thermally conditioned specimens were immerged and tested for the comparisons. In results, the reduction of thermally damaged GFRP rebars was greater than that of no thermally damaged ones. Based on the accelerated experimental test data, an polynomial equation is presented for prediction of long-term residual inter-laminar shear strength of GFRP rebars previously damaged by high temperature.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.3
• /
• pp.137-147
• /
• 1997

Interface shear strength of' concrete under static loading and deterioratiion of interface strength by fatigue loading in shear were experimentally investigated using composite beam test specimens. Thirteen beams were constructed. Five composite beams were tested statically until interface delaminations were observed in the static tests. Seven composite beam and one monolithically cast beam were subjected to two to three million cycles of fatigue load. Test variables were interface roughness, interface shear reinforcement, and presence of interface bond. The average interface shear strength of the composite beams with bonded-rough interface was 6, 060 kPa. No interface delamination was observed after cycling for the composite beams with bonded - rough interface and interface bond was not influenced by repeated application of the shear stress of 2.000 kPa(about 1/3 of the static interface shear strength). Smooth interface and unbonded-rough interface with shear reinforcement deteriorated under repeated shear loading.

• Composites Research
• /
• v.24 no.4
• /
• pp.11-16
• /
• 2011

Retention of interfacial shear strength (IFSS) of polymer composites at cryogenic temperature application is very important. In this work, single carbon tiber reinforced epoxy compositc was used to evaluate IFSS and apparent modulus under room and cryogenic temperatures. The property change of carbon and selected epoxy for particularly cryogenic temperature application were tested in tension and compression. Tensile strength and elongation of carbon fiber decreased at cryogenic temperature, whereas tensile modulus was almost same. On the other hand, epoxy matrix showed the increased tensile strength but decreased elongation. It can be due to maximum thermal contraction existing free volume in cryogenic temperature. IFSS increased up to $-10^{\circ}C$ and then decreased steadily. However, IFSS at cryogenic temperature was still similar to that at room temperature. This result is very useful to cryogenic application since selected epoxy toughness and interfacial adhesion can keep at such low temperature.

• Journal of the Korea Concrete Institute
• /
• v.28 no.4
• /
• pp.407-417
• /
• 2016

In this study, concrete composite beams were tested under two-point loading to evaluate horizontal shear strength. The test variables were a type of composite members (PC+RC, PSC+RC, SFRC+RC), area ratio of high-strength (60MPa) to low-strength concrete (24 MPa), and transverse reinforcement ratio. The test results showed that the contribution of transverse reinforcements and interface conditions had influence on horizontal shear strength. Existing and previous test results were classified according to test methods and the interface conditions and were compared with the predictions of current design codes. On the basis of test results, an improved design method was proposed.

• Journal of the Korea Concrete Institute
• /
• v.27 no.3
• /
• pp.299-309
• /
• 2015

Ultra High Performance Fiber Reinforced Concrete (UHPFRC) is distinguished from the normal concrete by outstanding compressive and tensile strength. Cracked normal concrete resists shear by aggregate interlocking while clamped by transverse reinforcement, which is called as shear friction theory. Cracked UHPFRC is expected to have a different shear transfer mechanism due to rather smooth crack face and post-cracking behavior under tensile force. Twenty-four push-off specimens with transverse reinforcement are tested for four different fiber volume ratio and three different ratio of reinforcement along the shear plane. The shear friction strength for monolithic concrete are suggested by limit analysis of plasticity and verified by test results. Plastic analysis gives a conservative, but reasonable estimate. The suggested shear friction factor and effectiveness factor of UHPFRC can be applied for interface shear transfer design of high-strength concrete and fiber reinforced concrete with post-cracking tensile strength.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.6
• /
• pp.791-796
• /
• 2013

In this study, the mechanical properties of a carbon fiber/polypropylene composite were evaluated according to the carbon fiber surface treatment. Carbon fiber surface treatments such as silane coupling agents and plasma treatment were performed to enhance the interfacial strength between carbon fibers and polypropylene. The treated carbon fiber surface was characterized by XPS, SEM, and single-filament tensile test. The interlaminar shear strength (ILSS) of the composite with respect to the surface treatment was determined by a short beam shear test. The test results showed that the ILSS of the plasma-treated specimen increased with the treatment time. The ILSS of the specimen treated with a silane coupling agent after plasma treatment increased by 48.7% compared to that of the untreated specimen.