In this study, initial crack index was evaluated by FEM analysis to find the crack propagation from hydration heat in precast concrete. As results, as the usage of hardening accelerator increased, initial compressive strength increased and setting time was shortened. Additionally, as amounts of hardening accelerators increased, the central temperature of concrete increased and the time to reach the highest temperature was shortened. It was demonstrated that the hardening accelerators accelerated the hydration reaction of cement, and caused the increase of hydration heat within the short period of time. Furthermore, the crack index for evaluating the heat level was performed by FEM. As results, there was no problem about the cracks, despite of the growth of initial high hydration heat. This is because of the increased tensile strength that is large enough to sustain the thermally induced-stress.

• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.359-366
• /
• 2001

Isothermal physical aging of a glass fiber/epoxy composite was examined at different aging temperatures ($T_a$) and degrees of conversion (monitored by the glass transition temperature, $T_g$) by means of the TBA torsion pendulum technique. The range of aging temperature was from 10 to $130^{\circ}C$ : the conversion was systematically changed from $T_g$=$76^{\circ}C$ to $T_g$=$177^{\circ}C$ (fully crosslinked). The effect of isothermal physical aging was manifested as perturbations of the modulus and mechanical loss vs. temperature in the vicinity of $T_a$ for all conversions. The rate of isothermal physical aging determined from the change of modulus with aging time at fixed aging temperature decreased and then increased with increasing conversion below T$_{a}$=9$0^{\circ}C$. There exists a superposition in aging rate vs. ($T_g$ -$T_a$) by shifting horizontally and vertically. This implies that the physical aging process is independent of the change of chemical structure as conversion proceeds. It has been found that water absorbed at the aging temperature below $70^{\circ}C$ during isothermal physical aging lowers the apparent aging rate. It is due to the absorbed water molecules forming strong polar interactions with hydroxyl group on network chain and reducing the segmental mobility during the physical aging.g.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.557-562
• /
• 2013

The thermal expansion and mechanical properties of diglycidyl ether of bisphenol A (DGEBA) with mercaptan hardeners were studied by a comparative method with an amine-adduct type hardener. Thermal expansion and dynamic mechanical properties were measured by thermo mechanical analysis (TMA) and dynamic mechanical ananlysis (DMA), respectively. The $T_g$ and the coefficient of thermal expansion (CTE) of epoxy/amine-adduct type hardener system were $82.6^{\circ}C$ and 71.2 $ppm/^{\circ}C$, respectively. As the number of -SH functional group of mercaptan hardener increased, the $T_g$ rapidly decreased and gradually increased up to ca. $80^{\circ}C$ and the CTE under the $T_g$ rapidly increased to ca. 200 $ppm/^{\circ}C$ from 80 $ppm/^{\circ}C$ and decreased to ca. 100 $ppm/^{\circ}C$. The crosslinking density of epoxy with amine-adduct type hardener was ca.1.5 $mol/cm^3$, while that of epoxy with mercaptan hardeners increased from 1.0 to 1.7 $mol/cm^3$, as the number of -SH functional group increased. The storage modulus can increase up to 2700MPa at $30^{\circ}C$.

• Journal of Adhesion and Interface
• /
• v.2 no.3
• /
• pp.16-24
• /
• 2001

The curing behavior of a phenolic resin (F/p: 1.3, 1.9, 2.5 for resol resin, F/P: 0.5, 0.7, 0.9 for novolac resin) has been studied by FT-IR spectroscopy. In this study is to synthesis of resol and novolac type phenolic resin with different F/P molar ratios and to compare the level of cure at different curing temperature conditions ($130^{\circ}C$, $160^{\circ}C$, $180^{\circ}C$ for resol resin, $160^{\circ}C$, $170^{\circ}C$, $180^{\circ}C$ for novolac resin) for 3, 5, 7, 10, 20, and 60 (min.), respectively. The conversion (${\alpha}$) was determined by the ratio of the peak area with time to the peak area of non-baked phenolic QH ($3300cm^{-1}$) at spectra. It is concluded that the initial curing rate of resol and novolac resin was increased as the molar ratio of formaldehyde/phenol increased and as the curing temperature of resin increased. According to the analysis was by the homogenous first-order model, the initial curing rate of resol and novolac resin was increased as the molar ratio of formaIdehyde/phenol increased at specific curing temperature.

• Korean Journal of Materials Research
• /
• v.6 no.5
• /
• pp.494-503
• /
• 1996

에폭시/산무수물계의 등온 경화거동을 새로이 제작된 Torsion Pendulum(TP)으로 다양한 온도에서 조사하였으며 경화반응을 촉진시키기 위하여 두 종류의 경화촉진제를 사용하였다. 새로이 제작된 TP는 개인용 컴퓨터를 이용하여 모든 기계\ulcorner인 작동과 date 수집 및 분석이 자동으로 처리될 수 있도록 하였다. 이 기기로부터 얻어진 결과인 경화 동안의 상대전단강성율(RSR, relative shear rigidity)과 log decrement(LD)의 변화로부터 제작된 TP가 잘 작동한다는 것을 알 수 있었다. 두 종류의 촉진제가 전체적인 경화과정에 미치는 촉진효과는 비슷하였으나 각 촉진제로부터 얻어진 LD 곡선을 보면 서로 다른 모양을 나타내었다. 이것은 경화촉진제가 반응 촉진효과 이외에도 경화거동에 영향을 미친다는 것을 의미하며, 따라서 이러한 경화거동의 차이는 경화물의 성질에 영향을 줄 수 있다.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.731-736
• /
• 1994

Cure kinetics of DGEBA/MDA/MN system with and without HQ were studied by Fractional life method and Kissinger equation. And the effect of HQ as a catalyst was studied. As cure temperature increased, the reaction rate increased and reaction order was almost constant. The activation energy of the system with HQ was lower about 13% and the reaction rate was higher than that of the system without HQ. It was because hydroxyl group of HQ formed a transition state with epoxide group and amine group and opened the epoxide ring easily and rapidly.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.37 no.2
• /
• pp.119-124
• /
• 2013

In this study, the two-dimensional transient temperature of printed Ag nanoparticle ink during continuous wave laser sintering was calculated. Ag nanoparticle ink was printed on a glass substrate by inkjet printing. Then, a 532-nm continuous wave laser with different laser intensities was irradiated on the printed Ag nanoparticle ink for 60 s. During laser irradiation, the in-situ specific resistance of the sintered ink was measured. To obtain the transient temperature of the sintered ink during the laser sintering process, a two-dimensional transient heat conduction equation was derived by applying the Wiedemann-Franz law. It was found that the specific resistance of the sintered ink decreased with an increase in the sintering temperature of the printed ink.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2011.11a
• /
• pp.470-473
• /
• 2011

본 연구에서는 산업현장에서 에폭시 강화촉진제, 도로용 첨가제 등으로 많이 사용되고 있는 경화제(M.E.K)의 혼합비에 따른 자연발화 위험성을 알아보고 산업 현장의 화재 예방을 위한 기초자료로 제공하고자 하였다. M.E.K와 에포비아 수지를 각기 다른 비율로 혼합한 상태에서 시간경과에 따른 시료의 온도변화 와 유증기 발생 및 자연발화 여부를 관찰한 결과 합성수지와 경화제의 혼합시 경화제가 5% 이상으로 혼합될 경우 혼합 수지의 내부온도가 약 $40^{\circ}C$ 이상으로 상승하면서 발포 현상과 함께 다량의 유증기가 발생하였고, 유증기가 발생된 모든 조건에 대하여 자연발화 여부는 확인할 수 없었다.

• Composites Research
• /
• v.16 no.1
• /
• pp.34-41
• /
• 2003

A cure process control model was proposed to optimize the curing process of thick filament wound structure. There are two types of smart cure, one is that the boundary conditions of the hollow cylinder are same between inner surface and outer surface, and the other is that inner surface temperature is slightly higher than outer surface to initiate cure reaction from the inner side to the outer side to reduce residual stress.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.138-138
• /
• 2016

의료용 공구로 사용되는 합금은 마르텐사이트계 스테인리스강의 대표 강종인 420스테인리스강이 사용되며, 이 합금은 고온의 오스테나이트 상태에서 ?칭하면 마르텐사이트 조직으로 변태하여 현저하게 경화하는 특징을 가지고 있으며, 오스테나이트화 후 템퍼링시 우수한 기계적 성질이 얻어진다. 그러나 템퍼링 온도의 영향으로 석출탄화물이 형성되어 기계적 성질이나 내식성이 저하되는 단점이 있다. 본 연구에서는 STS 420스테인리스강의 템퍼링 온도에 의한 내식성 문제점을 개선시키기 위해 STS630 합금을 사용하여 다양한 석출 열처리 조건 및 플라즈마 질화공정을 연구하였다. 구입한 소재의 균일한 성분 조정을 통한 미세 편석 및 물성부여를 위한 균질화 조건 도출 열처리를 실시하였으며, STS630의 고용화열처리는 오스테나이트 균일조직이 되는 온도영역으로 가열하여 급냉하는 것으로 마르텐사이트 변태시키는 열처리를 진행하였으며, 열처리온도는 $1020{\sim}1060^{\circ}C$로 설정하였다. 석출경화 열처리는 $460{\sim}480^{\circ}C$와 $500{\sim}520^{\circ}C$의 온도에서 실시, 제품에 따른 인성을 부여하였으며, 질화공정은 플라즈마 장비를 이용하여 플라즈마 가열 ${\rightarrow}$플라즈마 이온질화를 통하여 가장 최적의 공정을 도출하였다.- 질화가 마무리 된 시료는 내식성 및 물성 평가를 통해 제품으로서의 특성을 평가하였다. 석출경화 열처리에 의해 STS420합금에 버금가는 인장강도 및 경도값이 나타났으며, 플라즈마 질화에 따라 물성 값의 향상이 나타났다. 용출실험결과 STS420합금의 경우 Fe, Cr원소의 용출이 나타나며 변색이 형성되었으나 STS630합금의 경우 그 현상이 미미하였다.