Effect on the Residual Stress of Cure Profiles, Fillers and Mold Constraints in an Epoxy System

  • Moon, Chang-Kwon;Nam, Ki-Woo
    • 한국해양공학회지
    • /
    • 제23권4호
    • /
    • pp.1-5
    • /
    • 2009
  • A dilatometer was used to investigate the effect of cure conditions, mold types and the presence of filler in an epoxy system. These studies showed shrinkage in the cured epoxy when heating it through the glass transition temperature region. The magnitude of the shrinkage, related to stress build up in the epoxy during curing, was influenced by the processing conditions, filler presence and the nature of the mold used to contain the resin. Cure and cyclic cure at a lower temperature, prior to a post cure, decreased the magnitude of observed shrinkage. Cure shrinkage decreased with the number of cyclic cures. Post cured samples outside the mold led to less shrinkage compared with samples in the mold. Sample cured in a silicon mold represented less shrinkage than sample cured in an aluminum mold. Sample containing kaolin filler showed less shrinkage than unfilled sample.

수압보증시험시의 음향방출에 의한 복합재 연소관의 파괴거동 예측 (Prediction of Failure Behavior in Composite Motor Cases by Acoustic Emission during Hydroproof Testing)

  • 송성진;오치환;정현조;이상호;임수용;김호철
    • 비파괴검사학회지
    • /
    • 제18권2호
    • /
    • pp.92-102
    • /
    • 1998
  • 섬유강화 복합재 연소관은 복합재료의 사용, 필라멘트 와인딩 및 경화공정 등으로 인하여 제작 중 다양한 결함이 발생할 수 있으며, 또한 사용 도중에도 예기치 않은 손상을 받아 기계적 성질이 저하될 수 있다. 따라서 제작 완료된 연소관의 품질 보증을 위해 수압보증시험이 사용되고 있으나 이를 위해 가한 수압이 오히려 연소관에 예기치 않은 손상을 가하여 실제 사용시 그 성능을 저하시키는 요인으로 작용하는 경우도 있다. 이러한 문제를 해결하기 위해 본 연구에서는 수압보증시험시의 음향방출을 감지하여, 그 신호의 특성으로부터 복합재 연소관의 파손 거동을 예측하는 체계적인 기법의 개발을 시도하였다. 음향방출을 이용하여 연소관에 발생한 손상의 개략적 위치를 결정할 수 있었으며, 또한 파괴모드의 식별도 가능하였다. 다만, 시료의 부족으로 최종파열압력의 변화와 충격손상의 영향에 대한 신뢰성 있는 분석은 불가능하였다.