• 한국건설순환자원학회논문집
• /
• 제3권1호
• /
• pp.80-86
• /
• 2007

In this study we experimented setting time and basic properties as waste wood fiber and sodium silicate substitution rate to reuse waste wood fiber produced in construction field to wood chip board. To do this construction waste woods were crushed with the size less than 10mm, mixed with the rate of 1:2, 2.5, 3, and added sodium silicate with the rate of 0, 5% of cement content. The results are as follows. As the substitution rate of construction waste wood was increased delay of setting time was also increased, and the batch of adding 5% accelerator had a 13~17 hours faster setting time than non accelerator batch. The compressive strength was lower as wood substitution rate was higher, and as the specific gravity was higher, the strength was also higher. As wood substitution rate was higher, heat conductivity was lower, and as specific gravity was higher, heat conductivity also was higher.

• 대한환경공학회지
• /
• 제30권11호
• /
• pp.1102-1110
• /
• 2008

본 연구는 폐목재 발생원별 삼성분, 발열량, 그리고 중금속 및 Cl 함량을 분석하여 폐목재 특성을 평가함으로써 향후 폐목재 등급화를 위한 품질근거 기준을 마련하는데 필요한 기초자료를 제시하고자 하였다. 임목부산물, 생활계폐목재, 건설폐목재, 그리고 사업장폐목재의 4가지로 분류한 폐목재에서 수분함량은 대부분 5$\sim$10%를 나타내었으며, 이를 수분함량을 제외한 건조기준으로 환산하였을 때 가연분함량은 95% 이상이었고, 회분함량은 5% 이하를 나타내었다. 폐목재는 수분함량이 55%로 높았던 버섯재배폐목을 제외하고는 '건설폐기물의재활용촉진에관한법률'의 고형연료제품의 품질기준 중 발열량 기준(저위발열량 $\geq$ 3,500 kcal/kg)을 만족하였다. CCA (Cr, Cu, As)로 처리된 벤치목, 폐선박, 철도침목 등 방부목에서 CCA가 매우 높게 나타나 방부목의 사용과 관리, 폐기처분에 대한 엄격한 관리가 필요한 것으로 나타났다. Cl 함량은 목재 어(魚)상자에서만 약 1.3%로 가장 높게 나타났고 나머지 폐목재 및 재활용제품에서는 0.2% 이하의 낮은 값을 보였으나 고형연료제품의 염소함량 품질기준 (건조기준 2wt.%)을 모두 만족시켰다. 발생원별 폐목재를 유해물질 함유량을 기준으로 3등급화할 경우 대부분의 폐목재가 1등급에 해당하였으며, 합판류, MDF (medium density fiber), 표면도색된 전선드럼은 2등급에 해당하였다. 3등급에 해당하는 폐목재는 벤치목, 재활용공장목재분진, 폐선박과 철도침목으로 나타났다.