• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.335-341
• /
• 2011

Continuous SiC fiber-reinforced SiC-matrix composites ($SiC_f$/SiC) had been fabricated by electrophoretic infiltration combined with ultrasonication. Nano-sized ${\beta}$-SiC added with 12 wt% of $Al_2O_3-Y_2O_3$ additive and Tyranno$^{TM}$-SA3 fabric were used as a matrix phase and fiber reinforcement, respectively. After hot pressing at 5 different conditions, the density, microstructure and mechanical properties of $SiC_f$/SiC were characterized. Hot pressing at relatively severe conditions, such as $1750^{\circ}C$ for 1 and 2 h, resulted in a brittle fracture behavior due to the strong fiber-matrix interface in spite of their high flexural strength. On the other hand, toughened $SiC_f$/SiC composite could be achieved by hot pressing at milder condition because of the formation of weak interface in spite of the decreased flexural strength. These results proposed the importance of weak fiber-matrix interface in the fabrication of ductile $SiC_f$/SiC composite.

• Journal of Powder Materials
• /
• v.12 no.5 s.52
• /
• pp.345-350
• /
• 2005

In this study the nanostructured ${\alpha}-Al_{2}O_3$ ceramics have been fabricated by the combined application of magnetic pulsed compaction (MPC) and subsequent spark plasma sintering (SPS), and their density and hardness properties were investigated. The ${\alpha}-Al_{2}O_3$ prepared by the combined processes showed an increase by $8.4\%$ in density, approaching the value close to the true density, and an enhancement by $210\~400\;Hv$ in hardness, compared to those fabricated by MPC or static compaction method followed by sintering treatment.

• Korean Journal of Metals and Materials
• /
• v.46 no.6
• /
• pp.390-401
• /
• 2008

The objective of this study is to evaluate various machining characteristics of AlN-hBN machinable ceramics in micro end-milling process for its further application. First, AlN based machinable ceramics with hBN contents in the range of 10 to 20vol% were prepared by hot-pressing. Material properties of the composites, such as relative density, Vickers hardness, flexural strength, Young's modulus and fracture toughness were measured and compared. Then, micro end-milling experiments were performed to fabricate micro channels using prepared system. During the process, cutting forces, vibrations and AE signals were measured and analyzed using applied sensor system. Machined micro channel shapes and surface roughness were measured using 3D non-contact type surface profiler. From the experimental results, it can be observed that the cutting forces, vibrations and AE signal amplitudes decreased with increasing hBN contents. Also, measured surface roughness and profiles were improved with increasing hBN contents. As a result of this study, optimum machining conditions can be determined to fabricate desired products with AlN-hBN machinable ceramics based on the experimental results of this research.

• Journal of Powder Materials
• /
• v.28 no.5
• /
• pp.381-388
• /
• 2021

Zirconia has excellent mechanical properties, such as high fracture toughness, wear resistance, and flexural strength, which make it a candidate for application in bead mills as milling media as well as a variety of components. In addition, enhanced mechanical properties can be attained by adding oxide or non-oxide dispersing particles to zirconia ceramics. In this study, the densification and mechanical properties of YSZ-TiC ceramic composites with different TiC contents and sintering temperatures are investigated. YSZ - x vol.% TiC (x=10, 20, 30) system is selected as compositions of interest. The mixed powders are sintered using hot pressing (HP) at different temperatures of 1300, 1400, and 1500℃. The densification behavior and mechanical properties of sintered ceramics, such as hardness and fracture toughness, are examined.

• Journal of Sensor Science and Technology
• /
• v.30 no.3
• /
• pp.148-153
• /
• 2021

During the manufacture of a ZnS lens with excellent transmittance in the mid-infrared region (3-5 ㎛) by the hot-press process, a single-layer sintering method is used in which one lens is manufactured in one process. Additional research is required to improve this single-layer sintering method because of its low manufacturing efficiency. To solve this problem, the variation in optical properties of ZnS lenses with change in sintering temperature was investigated by introducing a Stack sintering method that can sinter multiple lenses simultaneously. A carbon paper was placed between the molded lenses and sintered into five layers. The average permeability of 67% at medium infrared wavelengths of 3-5 ㎛ was excellent under the following sintering conditions: pressure of 50 MPa and temperature of 850℃. This value is 1% less than the average permeability in the case of single-layer sintering of the ZnS lens. It was confirmed that the stack sintering method developed in this study can be used to manufacture a large number of lenses with excellent characteristics in a single process.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.1
• /
• pp.7-13
• /
• 2007

We synthesized and investigated $La_{0.75}Sr_{0.25}FeO_3$ by Glycine Nitrate Process(GNP) method used as cathode materials for SOFC(solid oxide fuel cell). Optimized amount of glycine is 3.17 mol. ICP elemental composition analysis indicated that the stoichiometry of the synthesized powders have nearly nominal values. SEM images and XRD patterns reveal that the synthesized powder has uniform size distribution and high degree of crystallinity. The sample powders were isostatically pressed to form a pellet. The green body was sintered at $1200^{\circ}C$ and the relative density of the sintered specimens were measured by Archimedes mettled. We measured electrochemical performance of LSF by AC impedance spectroscopy. Resistance of LSF shows lower value than that of LSM throughout all temperature region. The anode-supported solid oxide fuel cell showed a performance of $342mW/cm^2(0.7V,\;488mA/cm^2)$ at $750^{\circ}C$. The electrochemical characteristics of the single cell were examined by at impedance method.

• Journal of the Korean Ceramic Society
• /
• v.41 no.6
• /
• pp.456-463
• /
• 2004

To enhance the performance of anode-supported SOFC, single cell fabrication procedure was changed for better and resulting power generating characteristics of single cell were investigated. Liquid condensation process was employed for the granulation of NiO/YSZ powder mixture and the produced powder granules were compacted into anode green substrate by uni-axial pressing. YSZ electrolyte was printed on green substrate via screen-printing method and co-fired at 1400$^{\circ}C$ for 3 h. LSM/YSZ composite cathode of which the composition and heat treatment condition was adjusted to minimize the polarization#resistance with AC-impedance spectroscopy, was screen printed. The final single cell size from this multi-step procedure was 5${\times}$5 $\textrm{cm}^2$ and 10${\times}$10 $\textrm{cm}^2$. The maximum power densities of 5${\times}$5 and 10${\times}$10 single cells were about 0.45 W/$\textrm{cm}^2$ and 0.22 W/$\textrm{cm}^2$ at 800$^{\circ}C$, which are two times superior than those from single cells fabricated by the conventional process in previous our work.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.503-510
• /
• 2002

Silicon carbide candle filters for the pressurized fluidized bed combustion system were fabricated by extrusion process. Carbon black was added to control the porosity. Inorganic additives such as clay and calcium carbonate were added to exhibit appropriate strength. Silicon carbide layer with a finer pore size (mean pore diameter ~$10{\mu}m$) was coated on the silicon carbide support layer (mean pore diameter ~$47{\mu}m$, porosity ∼40%). After that, the filter was sintered at 1400${\circ}C$ in air. We evaluated the filtration performances of the filter at 500${\circ}C$ and $5kgf/cm^2$ of pressure. As a result, high separation efficiency, >99.999% was measured. It is expected that silicon carbide candle filter can be successfully used for the pressurized fluidized bed combustion system.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.867-873
• /
• 2003

$Si_{3}N_{4}$-BN based machinable ceramics were fabricated by hot-pressing at $1800^{\circ}C$ for 2 h under a pressure of 25 MPa. The microstructure, mechanical properties, and machinability were investigated. With increasing h-BN content from 5 vol% to 30 vol%, three point flexural strength decreased from 1000 MPa of monolithic S $i_3$ $N_4$ to 720～400 MPa. The fracture toughness, $K_{IC}$ , was decreased from 7.6 MPaㆍ$m^{1/2}$ of monolithic S $i_3$ $N_4$ to 6.5～4.1 MPaㆍ$m^{1/2}$. The grain size and aspect ratio of $\beta$-S $i_3$ $N_4$ slightly decreased with increasing h-BN content. S $i_3$ $N_4$ monolith could not be machined due to brittle fracture, but S $i_3$ $N_4$-BN based machinable ceramics could be machined without fracture, showing excellent machinability. With increasing h-BN content, the thurst force during cutting and micro-drilling process was decreased.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.7
• /
• pp.4835-4841
• /
• 2015

The effect of particle size and compaction pressure on the thermoelectric properties of n-type $FeSi_2$ was investigated. The starting powders with various particle size were pressed into a compact (compaction pressure; $70{\sim}220kg/cm^2$). The compact specimens were sintered at 1473 K for 7 h and annealed at 1103 K for 100 h under Ar atmosphere to transform to the semiconducting ${\beta}$-phase. The microstructure and phases of the specimens were observed by SEM, XRD and EDS. The electrical conductivity and Seebeck coefficient were measured simultaneously for the same specimen at r.t.~1023 K in Ar atmosphere. The electrical conductivity increased with decreasing particle size and hence the increases of relative density of the sintered body and the amount of residual metallic phase ${\varepsilon}$-FeSi due to a increase of the electrical conductivity. The Seebeck coefficient exhibited the maximum value at about 700~800 K and decreased with decreasing particle size. This must be due to a increase of residual metallic phase ${\varepsilon}$-FeSi. On the other hand, the change of compaction pressure appeared to have little effect on the thermoelectric properties. Consequently, the power factor would be affected more by particle size than compaction pressure.