• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.2
• /
• pp.83-87
• /
• 2003

$(Nd/Y)_{1.8}Ba_{}2.4Cu_{3.4}O_{7-x}$high $T_c$ superconductor was directionally grown by floating Bone melt growth process with a large temperature gradient in air. Cylindrical green rods of (Nd/Y)1.8 oxides were fabricated by cold isostatic pressing (CIP) method using rubber mold. Microstructures were observed by SEM and TEM and superconducting properties were measured by a SQUID magnetometer. Nonsuperconducting $(Nd/Y)_2BaCuO_5$ inclusions were uniformly distributed within the superconducting $(Nd/Y)Ba_2Cu_3O_x$ matrix. The directionally melt-textured (Nd/Y) 1.8 superconductor showed an onset Tc $\geq$ 90 K and a sharp superconducting transition.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.21 no.5
• /
• pp.199-204
• /
• 2011

$(YSmNd)_{1.8}Ba_{2.4}Cu_{3.4}O_{7-x}$ [(YSN)1.8] high $T_c$ superconductor was directionally grown by zone melt growth process, in air atmosphere. In this study, optimum melting temperature and growth rate were $1100^{\circ}C$ and 3.5 mm/hr, respectively. The microstructure of well-textured (YSN)1.8 samples were examined by XRD, optical microscopy, TEM and SQUID magnetometer. The critical current density of these samples were measured by the direct transporting current method. In the observation using an optical microscopy, nonsuperconducting $(YSmNd)_2BaCuO_5$[(YSN)211] inclusions of (YSN)1.8 superconductor uniformly distributed within the superconducting (YSmNd)$Ba_2Cu_3O_x$[(YSN)123] matrix. The directionally melt-textured (YSN)1.8 superconductor showed an onset $T_c{\geq}90\;K$ and sharp superconducting transition. The transport $J_c$ values were 830 A and $3.93{\times}10^4$ (A/$cm^2$) at 77 K self-field, respectively.