• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1240-1246
• /
• 1994

While sintering the Pb(Mg1/3Nb2/3)O3-PbTiO3-BaTiO3 system through solid-reaction route, pyrochlore(Pb3Nb4O13) phase while reduces the dielectric constant is inevitably formed. Substitution of Pb(Mg1/3Nb2/3)O3 with PbTiO3 and BaTiO3 can retard the occurrence of pyrochlore phase. The perovskite solid-solution without containing pyrochlore phase can be obtained when we consolidated the materials consisting of PbTiO3 and BaTiO3 at 1200℃ for 2 hours. The sintered body composed of 0.8Pb(Mg1/3Nb2/3)O3-0.1PbTiO3-0.1BaTiO3 composition showed the diffused phase transition(DPT) phenomena and the maximum value of dielectric constant at 0℃ (Tc') with the value of 1.3×104.

• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.743-754
• /
• 1996

In this study (Ba1-xPbx)TiO3 was synthesized by modified oxalate process in order to prevent vaporization of PbO through low temperature synthesis climinate Cl ion reproducibly substitute Pb for by and uniformly distribute ion (Ba1-xPbx)TiO3 was synthesized by coprecipitation of lead acetate barium acetate and ammonium titanyl oxalate have been used as starting materials. The substitution of Pb for Ba was reproducibly possible synthetic temperature of perovskite structure becomes lowed as the Pb concentration increases and fine partic-les (specific surface are :7.2 cm2/g) were obtained, BaTiO3 powders calcined at 90$0^{\circ}C$ for 3 hours were cubic from in XRD analysis and as Pb content was increases evident split of tetragonal peaks could be observed The optimum conditions to synthesize (Ba,Pb)TiO3 powder are the followings ; synthesis temperature (5$^{\circ}C$)

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.249-257
• /
• 1989

Dielectric properties and the stability of the perovskite phase in the Pb(Mg1/3Nb2/3)O3 system have been investigated as a function of amount of BaTiO3 and firing temperature. In the specimens fired at 120$0^{\circ}C$, the pyrochlore phase was eliminated by the addition of 10-15m/o BaTiO3 and also the dielectric constant increased. However, the dielectric constant decreased with further addition of BaTiO3 even though no pyrochlore phase was found to be present. The reducing tendency of the pyrochlore phase decreased with lowering the firing temperature in the system of Pb(Mg1/3Nb2/3)O3 with BaTiO3. Dielectric properties in PMN ceramics were affected by the character of the BaTiO3 rather than the pyrochlore phase.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05b
• /
• pp.57-59
• /
• 2005

Ploycrystalline $Pb(Zr_{0.5},Ti_{0.5})O_3$ and $BaTiO_3$ powder were prepared by sol-gel process. The alumina substrate were sintered at $1400^{\circ}C$ with bottom electrode of Pt for 2 hours. The Pb(Zr0.5,Ti0.5)O3 / BaTiO3 multilayered thick films with laminating times were fabricated on alumina substrate by screening printing method. The obtained thick films were sintered at $800^{\circ}C$ with upper electrode of Ag paste for 1 hour. Structural properties of Pb(Zr0.5,Ti0.5)O3 / BaTiO3 multilayered thick films were investigated. As a result of the Differential Thermal Analysis(DTA) of Pb(Zr0.5,Ti0.5)O3, exothermic peak was observed at around $650^{\circ}C$. The X-ray diffraction (XRD) patterns indicated that BaTi03 and Pb(Zr0.5,Ti0.5)O3 phases and porosities were formed in the interface of Pb(Zr0.5,Ti0.5)O3 / BaTiO3 multilayered thick films.

• Journal of the Korean Ceramic Society
• /
• v.28 no.5
• /
• pp.359-364
• /
• 1991

The effects of Pb5Ge3O11 on the sinterbility and lattice variation of the semiconducting 0.15 mol% Y2O3 doped BaTiO3 have been investigated as functions of additive contents (from 0.25 mol% to 2.5 mol%) and sintering temperatures (from 110$0^{\circ}C$ to 130$0^{\circ}C$). As the amount of Pb5Ge3O11 increases, the sinterbility of BaTiO3 increases abruptly at around 115$0^{\circ}C$. During the sintering, the most of Pb+2 ions in additives penetrate into BaTiO3 lattices and Ge+4 ions present at grain boundaries. Therefore the c lattice of the BaTiO3 increases largely and then the tetragonality increases due to the diffusion of the Pb+2 ions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1988.10a
• /
• pp.8-11
• /
• 1988

(1-x-y)Pb($Zn_{1/3}Nb_{2/3})0_3-BaTiO_3PbTiO_3(0.05{\leq}x{\leq}0.20, 0.05{\leq}y{\leq}0.15$) ternary compound ceramics were fabricated by the mixed oxide method. The dielectric properties with temperature and frequency of the specimens were investigated. Relative dielectric constants of the specimens were increased with $BaTiO_3$ contents. Increasing the $BaTiO_3$contents, the variation in the relative dielectric constant with frequency, the temperature coefficient of capacitance (TCC) and the dielectric loss were decreased.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.354-359
• /
• 1999

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.665-670
• /
• 1998

Ferroelectric anomaly in PbO-{{{{ { {B }_{2 }O }_{3 } }}-{{{{ {TiO }_{3 } }}-BaO glasses which is observed in DAT measurements was in-vestigated together with the effect of BaO content on the shift of Cuire temperature. The temperature where the ferroelectric anomaly apperars on cooling in DTA decreased in proportion with increasing BaO content,. For as-crystallized samples the ferroelectric anomaly was not observed on heating but on cooling whilist for powder samples leached chemically from the crystallized samples both endothermic and ex-otehrmic peaks were observed. This fact suggests that the appearance of the ferroelectric anomaly in DAT largely depends on glassy phases surrounding individual {{{{ {PbTiO }_{3 } }} crystals rather than effects of grain size and crystallinity.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.7
• /
• pp.2305-2308
• /
• 2012

Perovskite structured barium titanate particles ($BaTiO_3$) platelets were synthesized by molten salt synthesis and topochemical microcrystal conversion. As the precursors of $BaTiO_3$, plate-like $BaBi_4Ti_4O_{15}$ particles were first synthesized by the reaction of $Bi_4Ti_3O_{12}$, $BaCO_3$, and $TiO_2$ at $1080^{\circ}C$ for 3 h in $BaCl_2$-KCl molten salt. After the topochemical reactions, layer-structured $BaBi_4Ti_4O_{15}$ particles transformed to the perovskite $BaTiO_3$ platelets. $BaTiO_3$ particles with thickness of approximately $0.5{\mu}m$ and a length of $10-15{\mu}m$ retained the morphology feature of the $BaBi_4Ti_4O_{15}$ precursor. For <001> $Pb(Mg_{1/3}Nb_{2/3})O_3-32.5PbTiO_3$ (PMNT)-5 wt % PbO piezoelectric ceramics textured with 5 vol % of $BaTiO_3$ templates, the Lotgering factor reached 0.82, and $d_{33}$ was 870 pC/N.

• Proceedings of the KIEE Conference
• /
• 2005.11a
• /
• pp.189-190
• /
• 2005

Ploycrystalline $Pb(Zr_{0.5},Ti_{0.5))O_3$ and $BaTiO_3$ powder were prepared by sol-gel process. The alumina substrate were sintered at $1400^{\circ}C$ with bottom electrode of Pt for 2 hours. The Pb(Zr0.5,Ti0.5)O3 / BaTiO3 multilayered thick films with laminating times were fabricated on alumina substrate by screening printing method. The obtained thick films were sintered at $800^{\circ}C$ with upper electrode of Ag paste for 1 hour. Structural properties of Pb(Zr0.5,Ti0.5)O3 / BaTiO3 multilayered thick films were investigated. As a result of the Differential Thermal Analysis(DTA) of Pb(Zr0.5,Ti0.5)O3, exothermic peak was observed at around 650 $^{\circ}C$. The X-ray diffraction (XRD) patterns indicated that BaTiO3 and Pb(Zr0.5,Ti0.5)O3 phases and porosities were formed in the interface of Pb(Zr0.5,Ti0.5)O3 / BaTiO3multilayered thick films.