In this study, the microwave dielectric property variations of (1-x)$BiNbO_4-(x)ZnNb_2O_6$ composites (x=0.3, 0.5 and 0.7) with 10wt% zinc borosilicate(ZBS) glass was investigated as a function of the substitution of $ZnNb_2O_6$ with a view to applying thes system to LTCC technology. The all composition addition of 10wt% ZBS glass ensured a successful sintering below $900^{\circ}C$. In addition, a small amount of $Bi_2SiO_5$ as the secondary phase was observed in the all composition. The substitution of $ZnNb_2O_6$ on the $BiNbO_4$ composites increased the $Q{\times}f$ values, but it decreased the sinterability and dielectric constant due to the high sintering temperature and low dielectric constant of $ZnNb_2O_6\;than\;BiNbO_4$ ceramics. The increasing of $ZnNb_2O_6$ content from 0.3 to 0.7 in the (1-x)$BiNbO_4-(x)ZnNb_2O_6$ composites with 10wt% ZBS glass sintered at $900^{\circ}C$ demonstrated 28.1~15.6 in the dielectric constant$({\varepsilon}_r)$, 5,500~8,700GHz in the $Q{\times}f$ value.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.260-260
• /
• 2007

Low-temperature sintering and dielectric properties of the $1-xBiNbO_4-xZnNb_2O_6$ ceramics (x=0.3, 0.5, and 0.7) with 10 wt% zinc borosilicate (ZBS) glass was investigated as a function of the substitution of $ZnNb_2O_6$ with a view to applying this system to LTCC technology. The all composition addition of 10 wt% ZBS glass ensured a successful sintering below $900^{\circ}C$. The the amount of $ZnNb_2O_6$ on $ZnNb_2O_6$ ceramics increased the $Q{\times}f$ values, but it decreased the sinterability and dielectric constant due to the higher $Q{\times}f$ value and sintering temperature of $ZnNb_2O_6$ than that of $ZnNb_2O_6$ ceramics. The increase of $ZnNb_2O_6$ content from 0.3 to 0.7 in the $1-xBiNbO_4-xZnNb_2O_6$ ceramics with 10 wt% ZBS glass sintered at $900^{\circ}C$ demonstrated 30~20 in the dielectric constant (${\varepsilon}_r$), 3,500~4,500 GHz in the $Q{\times}f$ value.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 춘계총회 및 연구발표회 초록집
• /
• pp.42.2-42
• /
• 2003

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.245-245
• /
• 2007

본 연구는 $Bi_2O_3$, ZnO 및 $Nb_2O_5$로 이루어진 두 가지의 $Bi_2(Zn_{1/3}Nb_{2/3})_2O_7$와 $(Bi_{1.5}Zn_{0.5})(Zn_{0.5}Nb_{1.5})O_7$ pyrochlore를 제조한 후, ZBS 및 BZBS 유리를 각각 첨가하여 저온 소결 및 마이크로파 유전 특성을 고찰하였다. 두 가지의 pyrochlore에 대하여 하소 온도에 따른 상 합성 유무를 고찰한 결과 $900^{\circ}C$에서 단일 상을 갖는 pyrochlore를 제조할 수 있었다. 두 가지의 pyrochlore에 ZnO-rich ZBS 유리와 $Bi_2O_3$-rich BZBS 유리를 3, 5 wt%로 첨가한 후 $800{\sim}950^{\circ}C$에서 소결한 결과 ZBS 및 BZBS 유리를 5wt%를 첨가하였을 때 $900^{\circ}C$에서 소결이 가능하였다. 또한 마이크로파 유전 특성을 고찰한 결과, $(Bi_{1.5}Zn_{0.5})(Zn_{0.5}Nb_{1.5})O_7$의 pyrochlore는 고주파에서 유전 특성 측정이 되지 않았다. $Bi_2(Zn_{1/3}Nb_{2/3})_2O_7$의 pyrochlore의 경우 5 wt% ZBS 및 BZBS 유리를 첨가하여 $900^{\circ}C$에서 소결한 시편의 마이크로파 유전 특성은 ${\varepsilon}_r$= 62.8~68.3, $Q{\times}f$ value= 3,500~2,700 GHz을 나타내었다.