• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1061-1069
• /
• 1998

The thermal instability of Al2TiO5 Ceramics was contrlled by solid solution with MgO SiO2 and ZrO2 through electrofusion in an arc furnace. The thermal expansion properties of Al2TiO5 composites show the hysteresis due to the strong anisotropy of The crystal axes of these material. These phenomena are ex-plained by the opening and closing of microcracks. The difference in microcracking temperatures e.g 587.6(ATG2), 405.9(ATG3) and 519.7$^{\circ}C$(ATG4) is caused by the difference in grain size and stabilizer type. The thermal shock behaviour under cyclic conditions between 750-1400-75$0^{\circ}C$ show no change in mi-crostructure and phase assemblage for all three stabilized specimens. After the thermal loading test at 110$0^{\circ}C$ for 100hrs. ATG1 and ATG2 materials decomposes completely to its components corundum and ru-tile in both cases. However with approximatelly 20% retention of the Al2TiO5 Thus in order to prevent decomposition of the stabilized material in the critical temperature range 800-130$0^{\circ}C$ it must be traversed within a short period of time.

• 멤브레인
• /
• 제20권3호
• /
• pp.210-216
• /
• 2010

IS (요오드-황)프로세스의 HI 분해반응 공정에서의 적용을 목적으로 지르코니아 코팅 지지체를 이용하여 CVD법에 의해 수소분리막을 제작하였으며, 분리막으로서의 가능성을 평가하였다. 제작한 막의 형상 및 Si의 분포를 파악하기 위해 SEM 및 EPMA를 이용하여 분석하였다. 지르코니아를 코팅한 지지체를 이용하여 제작한 막에 Zr-Si-O층이 존재한다는 것을 알 수 있었다. 제작한 막의 수소와 질소가스의 단일 성분 투과속도를 $300{\sim}600^{\circ}C$에서 측정하였다. $600^{\circ}C$에서 Z-1막에서의 수소투과속도는 $1{\times}10^{-7}\;mol{\cdot}Pa^{-1}{\cdot}m^{-2}{\cdot}s^{-1}$를 나타냈다. 질소에 대한 수소의 선택성은 Z-1 막에서 5.0, Z-2막에서 5.75를 나타냈다.

• 한국세라믹학회지
• /
• 제36권4호
• /
• pp.391-402
• /
• 1999

Characteristics of composite electrolytes which were prepared by coating a thin film of YSZ (yttria sta-bilized zirconia : (ZrO2)0.92 (Y2O3)0.08) on YDC (yttria doped ceria : Ce0.8Y0.2O1.9) with mixed conductivity have been investigated in order to develop the low-temperature solid oxide fuel cell. The thickness (t) of spin-coated YSZ thin films after the heat-treatment at 600$^{\circ}C$ was increased proportionally to the sol con-centrations (C) while the decrease in its thickness with the spin rate ($\omega$) could be expressed in the e-quation of ln t=9.49-0.53 ln $\omega$(0.99mol//s sol conc.) When the sol concentration and the spin rate being less than 0.99 mol/l and higher than 1000 rpm respectively reliable YSZ/YDC composite electrolytes could be obtained by multi-coating although several micro-cracks were observed in singly coated YSZ film surfaces. The dense YSZ film with a 1$\mu\textrm{m}$ thickness was prepared by coating of 0.99 mol/l YSZ sol five-times at 2000 rpm followed by heat-treatment at 1400$^{\circ}C$ for 2h, The adhesion between YSZ film and YDC substrate was found to be very good. The open circuit voltages of H2/O2 single cell with YSZ/YDC composite electrolytes were 0.79∼0.82 V at 800$^{\circ}C$ and 0.75∼0.77V at 900$^{\circ}C$ The open circuit voltage was inversely proportioned to the thickness ratio of YSZ thin film (1$\mu\textrm{m}$) to YDC substrate(0.28-2.22 mm)

• 암석학회지
• /
• 제4권1호
• /
• pp.31-48
• /
• 1995

관악산 암주는 지금까지 단순히 흑운모 화강암으로만 구성된 것으로 알려져 왔으나 실제로는 석영+K-장석+사장석+흑운모$\pm$석류석의 광물군으로 보인다. 모드자료와 $An_5$ 미만의 사장석 성분을 고려하면 이 암주는 알칼리 장석화강암으로 명명된다. 서브솔버스 장석, 비교적 초기의 흑운모 정출, Q-Ab-Or 그림에서 유출된 은 관입깊이 등은 관악산 암주를 만든 마그마가 물을 함유하고 있었음을 지시하는데, 이는 아래에 설명하는 무수의 A-형 화강암과 유사한 지화학 성분을 가지는 것과는 대조된다. 관악산 암주의 주성분과 미량성분원소는 서울 화강암질 저반의 것과 뚜렷이 구분되며 이는 두 암체간의 성인적 차이를 시사한다. 관악산 암주의 주성분 및 미량원소 함량은 우리나라의 대부분 중생대 화강암과는 달리 A-형 화강암 특징을 보인다. 즉, $SiO_2$(73~78 wt%), $Na_2O+K_2O$,Ga(27~47 ppm), Nb(22~40 ppm), Y(48~95 ppm) 함량과, Fe/Mg and Ga/Al 비는 높은 반면, CaO(<0.51 wt%), Ba(9~75 ppm)과 Sr(2~23 ppm) 함량은 낮다. 그러나 전형적인 A-형 화강암과 비교했을때, Zr과 LREE는 낮은 함양을 Rb(386~796 ppm)은 높은 함량을 갖는 차이점을 보인다. 이 연구에서는 기존의 연구에서 보고되었던 LREE가 결핍되고 큰 부의 Eu이상을 가지는 회토류 원소 패턴이 근원 마그마의 특성을 가지는 것으로 재해석하였다. 즉 부분용융동안의 잔류물질로 다량의 사장석이 남아야 하는 반면, 휘석, 각섬석, 석류석은 남을 수 없다. 관악산 암주와 A-형 화강암의 지구화학적 유사성은 이 암주의 기원이 A-형 화강암의 기원과 밀접한 관련이 있음을 시사한다.