• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.291-294
• /
• 1999

The effect of AI$_2$O$_3$+Y$_2$O$_3$additives on fracture toughness of $\beta$-SiC-ZrB$_2$composites by hot-pressed sintering were Investigated. The $\beta$-SiC-ZrB$_2$ ceramic composites were hot-presse sintered and annealed by adding 1, 2, 3wt% AI$_2$O$_3$+Y$_2$O$_3$(6:4wt%) powder as a liquid forming additives at 195$0^{\circ}C$ for 4h. In this microstructures, no reactions were observed between $\beta$-SiC and ZrB$_2$, and the relative density Is over 90.79% of the theoretical density and the porosity decreased with increasing AI$_2$O$_3$+Y$_2$O$_3$ contents. Owing to crack deflection and crack bridging of fracture toughness mechanism, the fracture toughness showed the highest of 5.5328MPa . m$^{1}$2/ for composites added with 2wt% AI$_2$O$_3$+Y$_2$O$_3$ additives at room temperature. But the standard deviation of fracture toughness of specimens decreased with increasing AI$_2$O$_3$+Y$_2$O$_3$ contents and showed the highest of 0.8624 for composite tilth 1wt%, AI$_2$O$_3$+Y$_2$O$_3$additives.

• 한국분말재료학회지
• /
• 제26권6호
• /
• pp.455-462
• /
• 2019

ZrB₂ ceramic and ZrB₂ ceramic composites with the addition of SiC, WC, and SiC/WC are successfully synthesized by a spark plasma sintering method. During high-temperature oxidation, SiC additive form a SiO₂ amorphous outer scale layer and SiC-deplete ZrO₂ scale layer, which decrease the oxidation rate. WC addition forms WO₃ during the oxidation process to result in a ZrO₂/WO₃ liquid sintering layer, which is known to improve the anti-oxidation effect. The addition of SiC and WC to ZrB₂ reduces the oxygen effective diffusivity by one-fifth of that of ZrB₂. The addition of both SiC and WC shows the formation of a SiO₂ outer dense glass layer and ZrO₂/WO₃ layer so that the anti-oxidation effect is improved three times as much as that of ZrB₂. Therefore, SiC- and WC-added ZrB₂ has a lower two-order oxygen effective diffusivity than ZrB₂; it improves the anti-oxidation performance 3 times as much as that of ZrB₂.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 추계학술대회 논문집 학회본부 C
• /
• pp.894-896
• /
• 1999

The $\beta$-SiC+$ZrB_2$ ceramic composites were pressureless-sintered and annealed by adding 4, 8, 12wt% $Al_{2}O_{3}+Y_{2}O_{3}$(6 : 4wt%) powder as a liquid forming additives at $1800^{\circ}C$ for 4h. The relative density is over 79.3% of the theoretical density and phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H, 4H), $ZrB_2$, $Al_{5}Y_{2}O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest of 301.33MPa for composites added with 8wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. Owing to crack deflection and crack bridging of fracture toughness mechanism, the fracture toughness showed the highest of $3.6979MPa{\cdot}m^{1/2}$ for composites added with 8wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. The electrical resistivity was measured by the Pauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity).

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2011년도 제42회 하계학술대회
• /
• pp.1515-1516
• /
• 2011

Conductive SiC-$ZrB_2$ composites were produced by subjection a 40:60(vol%) mixture of zirconium diborided ($ZrB_2$) powder and ${\beta}$-silicon carbide (SiC) matrix to spark plasma sintering (SPS) under argon atmosphere. Inner diameters of graphite mold were $15mm{\varphi}$ and $20mm{\varphi}$, respectively. The relative densities of $15mm{\varphi}$ and $20mm{\varphi}$ sample were 99.4% and 97.88%, respectively. Reactions between ${\beta}$-SiC and $ZrB_2$ were not observed via x-ray diffraction (hereafter, XRD) analysis. The result of FE-SEM of fracture face of $15mm{\varphi}$ sample was intergranular fracture and that of $20mm{\varphi}$ sample was transgranular fracture. Because the fracture strength of $15mm{\varphi}$ sample was much higher than that of $20mm{\varphi}$ sample. The electrical resistivity, $9.37{\times}10^{-4}{\Omega}{\cdot}cm$ of $15mm{\varphi}$ sample was higher than that, $6.17{\times}10^{-4}{\Omega}{\cdot}cm$ of $20mm{\varphi}$ sample because of densification. Although sintering condition of SPS is same. the properties of sintered SiC-$ZrB_2$ compacts were changed according to inner diameter of graphite mold.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.839-842
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta$-SiC-ZrB$_2$ electroconductive ceramic composites were investigated as function of the liquid forming additives of $Al_2$O$_3$+Y$_2$O$_3$. Phase analysis of composites by XRD revelled $\alpha$ -SiC(6H), ZrB$_2$, and YAG(Al$_{5}$ Y$_3$O$_{12}$ ). Owing to crack deflection, crack bridging, phase transition and YAG of fracture toughness mechanism, the fracture toughness showed the highest value of 6.3MPa.m$^{1}$2/ for composites added with 24wt% $Al_2$O$_3$+Y$_2$O$_3$additives at room temperature. The resistance temperature coefficient respectively showed the value of 2.46$\times$10$^{-3}$ , 2.47$\times$10$^{-3}$ , 2.52$\times$ 10$^{-3}$ $^{\circ}C$ for composite added with 16, 20, 24wt% A1$_2$O$_3$+Y$_2$O$_3$additives. The electircal resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $25^{\circ}C$ to 90$0^{\circ}C$.

• 한국재료학회지
• /
• 제32권12호
• /
• pp.553-559
• /
• 2022

In this work, the ablation behavior of monolith ZrB₂-30 vol%SiC (Z30S) composites were studied under various oxy-acetylene flame angles. Typical oxidized microstructures (SiO₂/SiC-depleted/ZrB₂-SiC) were observed when the flame to Z30S was arranged vertically. However, formation of the outmost glassy SiO₂ layer was hindered when the Z30S was tilted. The SiC-depleted region was fully exposed to air with reduced thickness when highly tilted. Traces of the ablated and island type SiO₂ were observed at intermediate flame angles, which clearly verified the effect of flame angle on the ablation of the SiO₂ layer. Furthermore, the observed maximum surface temperature of the Z30S gradually increased up to 2,200 ℃ proving that surface amorphous silica was continuously removed while monoclinic ZrO₂ phase began to be exposed. A proposed ablation mechanism with respect to flame angles is discussed. This observation is expected to contribute to the design of complex-shaped UHTC applications for hypersonic vehicles and re-entry projectiles.

• Composites Research
• /
• 제35권4호
• /
• pp.261-268
• /
• 2022

ZrB₂, ZrC, HfB₂, HfC 및 SiC 등의 초고온 세라믹스(UHTC, ultra-high temperature ceramics)들은 최근 주목 받고 있는 극초음속 체계 및 차세대 우주왕복선 등에 적용하기 위하여 최근 활발한 연구가 진행되고 있다. 본 논문에서는 한국, 중국, 미국, 일본 및 EU 등지에서 최근 5년간 발표된 주요 연구 결과들을 위주로 간략히 소개하였다. 또한 초고온 세라믹스의 단점인 취성 문제를 극복하기 위한 세라믹 섬유강화 복합재료 제조를 목적으로 Horizon 2020 프로그램의 일환으로 범 유럽차원에서 공동연구로 수행된 C³HARME 프로젝트의 내용 및 결과를 간략히 보고하였다.

• 전기학회논문지
• /
• 제57권5호
• /
• pp.808-815
• /
• 2008

The composites were fabricated 61[vol.%] ${\beta}$-SiC and 39[vol.%] $TiB_2$ powders with the liquid forming additives of 8, 12, 16[wt%] $Al_2O_3+Y_2O_3$ as a sintering aid by pressureless annealing at 1650[$^{\circ}C$] for 4 hours. The present study investigated the influence of the content of $Al_2O_3+Y_2O_3$ sintering additives on the microstructure, mechanical and electrical properties of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Reactions between SiC and transition metal $TiB_2$ were not observed in the microstructure and the phase analysis of the pressureless annealed SiC-$TiB_2$ electroconductive ceramic composites. Phase analysis of SiC-$TiB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), ${\beta}$-SiC(3C), $TiB_2$, and In Situ YAG($Al_2Y_3O_{12}$). The relative density of SiC-$TiB_2$ composites was lowered due to gaseous products of the result of reaction between SiC and $Al_2O_3+Y_2O_3$. There is another reason which pressureless annealed temperature 1650[$^{\circ}C$] is lower $300{\sim}450[^{\circ}C]$ than applied pressure sintering temperature $1950{\sim}2100[^{\circ}C]$. The relative density, the flexural strength, the Young's modulus and the Vicker's hardness showed the highest value of 82.29[%], 189.5[Mpa], 54.60[Gpa] and 2.84[Gpa] for SiC-$TiB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. The electrical resistivity showed the lowest value of 0.0117[${\Omega}{\cdot}cm$] for 16[wt%] $Al_2O_3+Y_2O_3$ additives at 25[$^{\circ}C$]. The electrical resistivity was all negative temperature coefficient resistance (NTCR) in the temperature ranges from $25^{\circ}C$ to 700[$^{\circ}C$]. The resistance temperature coefficient of composite showed the lowest value of $-2.3{\times}10^{-3}[^{\circ}C]^{-1}$ for 16[wt%] additives in the temperature ranges from 25[$^{\circ}C$] to 100[$^{\circ}C$].

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2000년도 하계학술대회 논문집 C
• /
• pp.1474-1476
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta$-Sic-$ZrB_2$ electroconductive ceramic composites were investigated as function of the liquid forming additives of $Al_{2}O_{3}+Y_{2}O_{3}$. Phase analysis of composites by XRD revealed $\alpha$-SiC(6H), $ZrB_2$, and YAG($Al_{5}Y_{3}O_{12}$). The relative density of composites were increased with increasing $Al_{2}O_{3}+Y_{2}O_{3}$ contents. The flexural strength showed the highest value of 390.6MPa for composites added with 20wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. Owing to crack deflection, crack bridging. phase transition and YAG of fracture toughness mechanism. the fracture toughness showed the highest value of 6.3MPa${\cdot}m^{1/2}$ for composites added with 24wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives at room temperature. The electrical resistivity of the composites was all positive temperature coefficient resistance (PTCR) in the temperature range of 25$^{\circ}C$ to 900$^{\circ}C$.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1104-1105
• /
• 2006

Several boride sintered bodies such as $TiB_2$, $ZrB_2$, and $SiB_6$ were previously reported. In the present study, the sinterability and physical properties of chromium boride $(CrB_2)$ containing chromium carbide $(Cr_3C_2)$ sintered bodies were investigated in order to determine its new advanced material. The samples were sintered at desired temperature for 1 hour in vacuum under a pressure by hot pressing. The relative density of sintered bodies was measured by Archimedes' method. The relative densities of $CrB_2$ addition of 0, 5, 10, 15 and 20 mass% $Cr_3C_2$ composites were 92 to 95%. The Vickers hardness of the $CrB_2$ with 10 and 15 mass% $Cr_3C_2$ composites were about 14 and 15 GPa at room temperature, respectively. The Vickers hardness at high temperature of the $CrB_2$ addition of 10 mass% $Cr_3C_2$ composite decreased with increasing measurement temperature. The Vickers hardness at 1273 K of the sample was 6 GPa. The Vickers hardness of $CrB_2$ addition of $Cr_3C_2$ composites was higher than monolithic $CrB_2$ sintered body. The powder X-ray diffraction analysis detected CrB and $B_4C$ phases in $CrB_2$ containing $Cr_3C_2$ composites.