The composites were fabricated by adding 30, 35, 40, 45[vol.%] Zirconium Diboride(hereafter, $ZrB_2$) powders as a second phase to Silicon Carbide(hereafter, SiC) matrix. $SiC-ZrB_2$ composites were sintered by Spark Plasma Sintering(hereafter, SPS) in vacuum or argon gas atmosphere. The relative density of SiC+40[vol.%]$ZrB_2$ composites reveal high 99.57[%] in argon gas atmosphere and pressure 50MPa.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.114.1-114.1
• /
• 2007

• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.285-290
• /
• 1999

The magnetic properties of sputtered amorphous $Fe_{86.7}Zr_{3.3}B_4Ag_6$ thin films, which contains an additional insoluble element Ag, have been investigated as a function of uniaxal field annealing temperature. The amorphous $Fe_{86.7}Zr_{3.3}B_4Ag_6$ thin films produced by relatively low temperature annealing at 40$0^{\circ}C$ for 1 hour was found to have very high permeability of 7800 at 50 MHz, 0.2 mOe, high magnetization of 1.7 T, low coercivity of 1.0 Oe and very low core loss of 1.4 W/cc at 1 MHz, 0.1 T, respectively. It is notable that the permeability and core loss values for various kinds of the soft magnetic thin films reported up to now. The reason for the appearance for the good soft magnetic properties is presumably due to the homogeneous formation of very fine bcc $\alpha$-Fe clusters with the size in the amorphous $Fe_{86.7}Zr_{3.3}B_4Ag_6$ thin films matrix, which can be deduced from the XRD results.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1099-1106
• /
• 1997

In the present study, the effect of TiB2 addition on the sintering behavior of ZrB2 ceramics was studied with hot pressing under Ar atmosphere. Hot pressing experiments were carried out in graphite dies at the 1$700^{\circ}C$, 180$0^{\circ}C$ under Ar atmosphere. The sintering density increased with increasing TiB2 contents. With the addition of 10wt% TiB2 almost theoretical density could be achieved by hot-pressing at 180$0^{\circ}C$. Zr-Ti-Fe-B compound in liquid phase was observed from the EDS and WDS analysis. It was considered that sinterability was enhanced due to the mass transfer through liquid phase formed at the sintering temperature. In addition of TiB2, transition metal of groups IV, substitutional solid solution could be formed.

• Journal of the Korean Ceramic Society
• /
• v.32 no.3
• /
• pp.385-393
• /
• 1995

Akali-resistant porous glass was prepared by phase separation in Na2O-B2O3-SiO2 system containing ZrO2 and MgO. ZrO2 was added for alkali-resistance and MgO for anti-cracking during leaching. Optimal content of ZrO2 for alkali-resistance was 7wt% and devitrification by heat treatment resulted from further addition. Pore size and pore volume were decreased and specific surface area was increased with ZrO2 addition due to depression in phase separation. Addition of 3mol% MgO to mother glass containing 7wt% ZrO2 was effective for anti-crack during leaching. In this case, with phase separation at 55$0^{\circ}C$ and 5$25^{\circ}C$ for 20 hrs. crack-free porous glasses could be prepared. The relation between pore size r and heat treatment time t at 55$0^{\circ}C$ was D=25.58＋18.16t. According to measurement of gas permeability, the mechanism of gas permeation was Knudsen flow. N2 and He permeability of porous glass which was prepared by heat treatment at 55$0^{\circ}C$ for 20 hrs. were 0.843$\times$10-7mol/$m^2$.s.Pa and 2.161$\times$10-7mol/$m^2$.s.Pa respectively.

• Journal of the Korean Chemical Society
• /
• v.49 no.4
• /
• pp.377-380
• /
• 2005

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1515-1516
• /
• 2011

Conductive SiC-$ZrB_2$ composites were produced by subjection a 40:60(vol%) mixture of zirconium diborided ($ZrB_2$) powder and ${\beta}$-silicon carbide (SiC) matrix to spark plasma sintering (SPS) under argon atmosphere. Inner diameters of graphite mold were $15mm{\varphi}$ and $20mm{\varphi}$, respectively. The relative densities of $15mm{\varphi}$ and $20mm{\varphi}$ sample were 99.4% and 97.88%, respectively. Reactions between ${\beta}$-SiC and $ZrB_2$ were not observed via x-ray diffraction (hereafter, XRD) analysis. The result of FE-SEM of fracture face of $15mm{\varphi}$ sample was intergranular fracture and that of $20mm{\varphi}$ sample was transgranular fracture. Because the fracture strength of $15mm{\varphi}$ sample was much higher than that of $20mm{\varphi}$ sample. The electrical resistivity, $9.37{\times}10^{-4}{\Omega}{\cdot}cm$ of $15mm{\varphi}$ sample was higher than that, $6.17{\times}10^{-4}{\Omega}{\cdot}cm$ of $20mm{\varphi}$ sample because of densification. Although sintering condition of SPS is same. the properties of sintered SiC-$ZrB_2$ compacts were changed according to inner diameter of graphite mold.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.61 no.7
• /
• pp.988-991
• /
• 2012

The computer simulation was performed to confirm distribution of current and power density according to inner diameter of graphite mold of SPS(Spark Plasma Sintering). When the inner diameters of a graphite mold are varied $10mm{\Phi}$, $20mm{\Phi}$, $30mm{\Phi}$ and $40mm{\Phi}$, the more the inner diameter of graphite mold is decreased, the more the current density of punch section is increased. Because the electrical resistivity of the SiC-$ZrB_2$ specimen section($7.77{\times}10^{-4}{\Omega}{\cdot}cm$) was lower than the electrical resistivity($6.00{\times}10^{-3}{\Omega}{\cdot}cm$) of graphite section, the current density and power density of specimen section was higher than those of graphite section. It is considered that a SiC-$ZrB_2$ composite is sintered by more Joule heat of specimen section than that of mold and punch section. The current and power density distribution of a SiC-$ZrB_2$ composite can be predicted through computer simulation when SPS is conducted, and an electrical resistivity of the SiC-$ZrB_2$ composite is main element of SPS.

• Korean Journal of Materials Research
• /
• v.32 no.12
• /
• pp.553-559
• /
• 2022

In this work, the ablation behavior of monolith ZrB₂-30 vol%SiC (Z30S) composites were studied under various oxy-acetylene flame angles. Typical oxidized microstructures (SiO₂/SiC-depleted/ZrB₂-SiC) were observed when the flame to Z30S was arranged vertically. However, formation of the outmost glassy SiO₂ layer was hindered when the Z30S was tilted. The SiC-depleted region was fully exposed to air with reduced thickness when highly tilted. Traces of the ablated and island type SiO₂ were observed at intermediate flame angles, which clearly verified the effect of flame angle on the ablation of the SiO₂ layer. Furthermore, the observed maximum surface temperature of the Z30S gradually increased up to 2,200 ℃ proving that surface amorphous silica was continuously removed while monoclinic ZrO₂ phase began to be exposed. A proposed ablation mechanism with respect to flame angles is discussed. This observation is expected to contribute to the design of complex-shaped UHTC applications for hypersonic vehicles and re-entry projectiles.

• Journal of Korea Foundry Society
• /
• v.13 no.2
• /
• pp.168-174
• /
• 1993

It has been known that the grain refinement of Cu base alloys greatly improved mechanical properties, castability, workability and hot shortness resistance etc. In this study CuZr50, CuP7, CuFe7, CuMg10 binary alloys were added as grain refiners in CuZn36 alloy. The alloys melted in vacuum and controlled in mixed gas conditions and casted at $1050^{\circ}C$. Zr-P-X compound has significantly grain refined but oxygen has been found detrimental to grain refinement. In the case of Zr /B ratio below 4, B acted as grain growth element in this alloy.