• Journal of the Korean Ceramic Society
• /
• v.33 no.11
• /
• pp.1223-1230
• /
• 1996

• Journal of the Korean institute of surface engineering
• /
• v.30 no.3
• /
• pp.183-190
• /
• 1997

Fabrication and crystallization characteristics of yttria($T_2O_3$) stabilized zirconia(YSZ) thin film by sol-gel process were studied. YSZ sol was synthesized with zirconium n-propoxide($Zr(OC_3H_7)_4)$) and yttrium nitrate pentahydrate ($Y(NO_3)_3.5H_2O$). YSZ film was prepared by depositing the polymeric sol on porous $Al_2O_3$ substrate by spin-coating, and the film characteristics were investigated by FRIR, TG-DTA, XRD, DSC, optical microscopy and SEM. The film topology was uniform and cracks were not found. It was found that the annealing temperature and the concentration of stabilizer affect the crystallization of YSZ film. The YSZ film began to crystallize from amorphous to tetragonal phase at 40$0^{\circ}C$, and it was not converted to cubic structure until $1100^{\circ}C$. It seemed that the grains were formed over $700^{\circ}C$and the average grain size was obtained about 0.2$\mu\textrm{m}$.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.111-117
• /
• 2004

3Y-TZP containing 0.3∼1.2 wt% of $Al_2$O$_3$ was prepared by slip-casting after attrition milling. The specimen was sintered at 1390∼151$0^{\circ}C$ and mechanical characterization and microstructure analysis were conducted. Monoclinic content of the specimen was calculated by XRD. The apparent density of specimen increased with increasing sintering temperature. While above 1470%, the formation of m-ZrO$_2$ degraded the density. The microhardness of specimen decreased with temperature because monoclinic phase increased wit the grain growth. The specimen containing $Al_2$O$_3$ below 0.9 wt% sintered at 143$0^{\circ}C$ showed the highest microhardness of 1360 Hv.

• Journal of Powder Materials
• /
• v.20 no.6
• /
• pp.445-452
• /
• 2013

Yttria-stabilized zirconia (YSZ) coatings are fabricated via suspension plasma spray (SPS) for thermal barrier applications. Three different suspension sets are prepared by using a planetary mill as well as ball mill in order to examine the effect of starting suspension on the phase evolution and the microstructure of SPS prepared coatings. In the case of planetary-milled commercial YSZ powder, a deposited thick coating turns out to have a dense, vertically-cracked microstructure. In addition, a dense YSZ coating with fully developed phase can be obtained via suspension plasma spray with suspension from planetary-milled mixture of $Y_2O_3$ and $ZrO_2$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.3
• /
• pp.127-132
• /
• 2014

$Y_2O_3$-BN ceramic composites were fabricated from the slurries of yttria powder with average particle size of 3~10 ${\mu}m$. The slurry was fabricated by mixing PVA binder, NaOH for Ph control, PEG, BN powder and $Y_2O_3$ powder. The mixed $Y_2O_3$ powders were obtained by spray drying process from the slurry. The $Y_2O_3$-BN composite specimen was shaped in size of ${\O}14mm$ and then sintered at $1550^{\circ}C$ and $1600^{\circ}C$, respectively. The characteristics, microstructure, purities, densities, bulk resistance, thermal expansion, hardness and plasma resistance of the $Y_2O_3$-BN composites were investigated with the function of BN contents and sintering temperature.

• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.549-555
• /
• 1991

Mullite-zirconia (0∼4 mol% yttria) composites were obtained by In-situ sintering of zircon and alumina mixture, and their mechanical properties were studied in conjuction with microstructure observation. Martensitic transformation temperature (Ms) of zirconia dispersed in the mullite matrix decreased with Y2O3 contents and was about 600$^{\circ}C$ for ZrO2 containing 4 mol% Y2O3. On cooling of this composites, tetragonal to monoclinic phase transformation induced microcracks at the grain boundary of mullite matrix. The microcracks seemed to absorb the fracture energy in stress field during mechanical tests. Therefore, toughening mechanisms of this composite were considered to nucleation and extension of microcrack, and crack deflection mechanism due to the difference of thermal expansion coefficient between matrix and dispersed phase.

• Journal of the Korean Ceramic Society
• /
• v.29 no.11
• /
• pp.851-854
• /
• 1992

It was grown ZrO2:10 mol% Y2O3 single crystals doped with 1 wt% of rare earth metal ion (Ce, Pr, Nd, Er, Eu) by Skull Method. Grown crystals showed Ce:orange-red, Pr:golden-yellow, Nd:lilac, Er:pink, Eu:light pink due to dopant effect. It was examined color centers in light absorption pattern of visible region (λ= 300~700 nm); in as grown samples, absorption by Ce4+, (Pr4+, Pr3+), Nd3+, Er3+, Eu3+ ions were important, and in samples after vacuum annealing, decrease of absorption by Pr4+ ion and increase of absorption by Pr3+ ion was important, and absorption by Ce3+, Eu2+ was important due to reduction of activator.

• Journal of the Korean Chemical Society
• /
• v.34 no.6
• /
• pp.555-560
• /
• 1990

High temperature superconducting films of $YBa_2Cu_3O_{7-x}$ were fabricated on the (100) single crystal faces of YSZ (yttria stabilized zirconia) and SrTi$O_3$ by aerosol spray using ultrasonic atomization. The superconducting phase was formed by a three-step process: (a) spraying of a stoichiometric solution of nitrates of yttrium, barium, and copper on heated substrates kept at 250$^{\circ}C$, (b) preheating of the sprayed films in air at 550$^{\circ}C$, and (e) sintering of the films in flowing oxygen at 950$^{\circ}C$, followed by furnace cooling. Resistances of the films were measured by the dc four-probe method and superconductivity was confirmed above the liquid nitrogen temperature.

• Journal of the Korean Ceramic Society
• /
• v.45 no.11
• /
• pp.707-712
• /
• 2008

Plasma resistant nanocrystalline $Y_2O_3$ films were deposited on alumina substrates through the electron-beam PVD technique. Increasing substrate temperature to $600^{\circ}C$ resulted in the textured microstructures with significantly enhanced adhesion force of the coating to the substrate. During the exposure to fluorine plasma, erosion rate of the coated specimen was higher than that of a sintered yttria specimen, but significantly lower than that of a single crystalline alumina. Considering the adhesion and erosion behaviors observed in the coated specimen prepared at $600^{\circ}C$, the deposition technique appears effective in reducing contamination particles generated from the ceramic parts in the plasma environment.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.10
• /
• pp.842-848
• /
• 1998

The stability of paraseodymium-based zinc oxide varistor consisting of Zn-Pr-Co-Cr-Y oxide was investigated according to yttria additives under different stress conditons, such as 0.8V\ulcorner\ulcorner/373K/12h and 0.85V\ulcorner\ulcorner/393K/12h. Wholly, all varistor after the stress showed nearly symmetric and stable I-V characteristics. Particularly, in the case of 2.0mol% and 4.0mol% yttria-added varistor showing a good I-V characteristics, the varation rate of varistor voltage were less 1% and that of nonlinear coefficient were about degree of 5%, and what is remarkable, leakage current with increasing stress time during the applied stress was almost constant. It the light of these facts, it is estimated that varistor constituents having 2.0mol% and 4.0mol% yittria, respectively, will be utilized to various application fields.