• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.5
• /
• pp.644-648
• /
• 1995

Transparent xBa(La$_{1}$2/Nb$_{1}$2/)O$_{3}$-(1-x)Pb(Zr, Ti)O$_{3}$ (x=8.5, 9.0[mol.%], Zr/Ti=70/30~40/60) ceramics were fabricated by the two-stage sintering method, the electrooptic properties were investigated with Ba(La$_{1}$2/Nb$_{1}$2/)O$_{3}$ content and Zr/Ti composition ratio. Decreasing the Zr/Ti ratio, the electrooptic property was changed from a quadratic electrooptic effect to a linear electrooptic effcet. In the BLN-PZT 9.0/50/50 specimen having the tetragonal structure, the linear electrooptic coefficient had the highest value of 6.01*10$^{-10}$ [m/V] and in the BLN-PZT 9.0/55/45 specimen which located near the MPB region, the quadratic electrooptic coefficient had the highest value of 10.53*10$^{-16}$ [m$^{2}$/V$^{2}$].

• Journal of the Mineralogical Society of Korea
• /
• v.19 no.2 s.48
• /
• pp.81-88
• /
• 2006

The Yttria Partially Stabilized Zirconia powder was prepared by spontaneous precipitation method using $ZrOCl_2{\cdot}8H_O-YCl_33{\cdot}6H_2O$ solution as a starting materials. The optimal experimental conditions such as concentration and pH of starting solutions, the amounts of stabilizer $Y_2O_3$ used, and sintered temperature were carefully studied. The best condition for synthesizing $ZrO_2$ was experimentally selected and applied throughout this study for the preparation of the 3 mole% $Y_2O_3$ partially stabilized zirconia, 3YSZ. The physical properties of 3YSZ was examined by XRD, Raman, DT A, and SEM. The structural transition from pure monoclinic high temperature $ZrO_2$ to tetragonal room temperature 3YSZ was made possible by the added amount of $Y_2O_3$ in the $ZrO_2+Y_2O_3$ system. All Raman Spectrum band appeared in the lower wave numbers rather than in higher wave numbers as structure changes from monoclinic to tetragonal.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.454-460
• /
• 2001

장석, 석영, 점토와 17 wt% $Al_2$O$_3$를 함유한 알루미나질 자기 애자를 제조하였다. 분말을 ball milling으로 6시간 분쇄하였으며 성형체를 압출법으로 제조한 후 터널가마에서 130$0^{\circ}C$, 50분 동안 소결하였다. 터널가마에서 소결한 시편의 소결밀도는 이론밀도의 97%에 도달하였고, 3점 꺾임강도는 1658kgf/$ extrm{cm}^2$ 이었으며 ICL(indentation crack length) 방법으로 측정한 파괴인성은 2.3 MPa.m$^{1}$2/이었다. 기계적 성질을 향상시키기 위하여 ZrO$_2$를 첨가하여 15 wt% $Al_2$O$_3$-2 wt% ZrO$_2$와 12 wt% $Al_2$O$_3$-5 wt% ZrO$_2$를 복합체를 제조하였다. ZrO$_2$를 첨가한 시편의 꺾임강도는 1740kgf/$\textrm{cm}^2$이고 파괴인성은 2.4 MPa.m$^{1}$2/로 약 10% 기계적 성질이 향상되었다.

• Journal of the Korean Ceramic Society
• /
• v.30 no.9
• /
• pp.717-722
• /
• 1993

Effects of microstructures on the electrical properties of ZrO2 based ceramics were analyzed by modeling layer arrangements and mixed phase structures. Single layers and alternating multilayers were made from 3mol% and 8mol% Y2O3 doped ZrO2 powders, while mixed specimen was made by blending and compacting these raw powders. After sintering at 150$0^{\circ}C$ for 2hr in air, AC impedance characteristics were measured. Contributiion of bulk comonent to total resistivity and its temperature-dependence were larger in 8Y-ZrO2 single layer than in 3Y-ZrO2 single layer. The multilayered specimen connected in serial to electrodes showed partial characteristics of both 3Y-ZrO2 and 8Y-ZrO2 single layers. The multilayered specimen connected in parallel to electrodes and the mixed specimen exhibited characteristics mainly of 8Y-ZrO2 single layer. The multilayered specimen connected in parallel to electrodes revealed the highest electrical conductivity near the operating temperature of solid oxide fuel cell. However, it is expected that the mixed specimen is appropriate for the applications because of its relatively high electrical conductivity with high strength expected.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.513-519
• /
• 1994

Alumina composite was fabricated by introducing tetragonal ZrO2 in alumina composite of $\alpha$-alumina reinforced with in-situ formed La-$\beta$-aluminate (LaAl11O18). The powder mixture of composition (100-x)[88 Al2O3+(La2O3+11 Al2O3)]+x vol% ZrO2 was prepared with x from 0 to 40. Dense composites fabricated by hot-pressing exhibited bending strength up to 1200 MPa. The gain growth inhibiting effect of ZrO2 grains and La-$\beta$-aluminate platelets, and possibly the stress-induced phase transformation of ZrO2 have resulted in the high bending strength. The fracture toughness of the composite also increased up to 8.5 MPa.m1/2. The enhancement in toughness can be explained by transformation and microcrack toughening of ZrO2 and by crack deflection and bridging of La-$\beta$-aluminate platelets and ZrO2.

• Journal of the Korean Ceramic Society
• /
• v.27 no.2
• /
• pp.201-210
• /
• 1990

The mullite-15v/o ZrO2 composites were prepared by dispersing ZrO2-3m/o Y2O3 powders into the mullite matrix in order to improve the mechanical properties of the mullite. The densification and retention of t-ZrO2 in the matrix of synthetic mullite were also investigated. From IR spectroscopic analysis, the obtained amorphous SiO2-Al2O3 powder was observed to have Si-O-Al chemical bond in its structure which might result in the homogeneous mullite composition. The lattice parameter of the mullite powder calcined above 130$0^{\circ}C$ (a0=7.5468$\AA$) is nearly close to the value of stoichiometric mullite (71.8wt% Al2O3, a0=7.5456$\AA$). The sintering behavior, microstructure, flexural strength and fracture toughness of the mullite and mullite-15v/o ZrO2 composites have been studied. The mullite-15v/o ZrO2(+3m/o Y2O3) ceramics with relative densities of 96% were obtained when sintered at 1$600^{\circ}C$. The flexural strength and fractrue toughness of the composites sintered at 1$600^{\circ}C$(calcination temperature of mullite powders ; 125$0^{\circ}C$) had maximum values of 307MPa and 2.50MPa.m1/2, respectively. The fracture toughness improvement in the mullite-ZrO2 cmoposite is assumed to be resulted from the combined effect of the stress-induced phase transformation of tetragonal ZrO2 and the crack deflection due to microcracking by the monoclinic ZrO2 formation.

• Journal of the Korean Ceramic Society
• /
• v.32 no.5
• /
• pp.617-625
• /
• 1995

In order to reduce reflectance of soda-lime glass having average reflectance of 7.35% and refractive index of 1.53, single (SiO2), double (SiO2/20SiO2-80ZrO2), and triple (SiO2/ZrO2/75SiO2-25ZrO2) layers were designed and fabricated on the glass substrate by Sol-Gel method. Stble sols of SiO2-ZrO2 binary system for antireflective (AR) coatings were synthesized with tetraethyl orthosilicate (TEOS) and zirconium n-butoxide as precursors and ethylacetoacetate (EAcAc) as a chelating agent in an atmosphere environment. Films were deposited on soda-lime glass at the withdrawal rates of 3~11 cm/min using the prepared polymeric sols by dip-coating and they were heat-treated at 45$0^{\circ}C$ for 10 min to obtain homogeneous, amorphous and crack-free films. In case of SiO2-ZrO2 binary system, refractive index of film increased with an increase of ZrO2 mol%. Designed optical constant of films could be obtained through varying the withdrawal rate. In the visible region (380~780nm), reflectance was measured with UV/VIS/NIR Spectrophotometer. Average reflectances of the prepared single-layer [SiO2 (n=1.46, t=103nm)], double-layer [SiO2 (n=1.46, t=1-4nm)/20SiO2-80ZrO2 (n=1.81, t=82nm)], and triple-layer [SiO2 (n=1.46, t=104nm)/ZrO2 (n=1.90, t=80nm)/75SiO2-25ZrO2 (n=1.61, t=94 nm)] were 4.74%, 0.75% and 0.38%, respectively.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06b
• /
• pp.55-85
• /
• 1996

지르코니아 분말은 ZrO2 결정상이 온도변화에 따라 부피변화를 수반하는 상전이변태를 나타낸다. 단사정 ZrO2가 110$0^{\circ}C$에서는 정방정으로, 2$700^{\circ}C$ 내외에서는 입방정으로 결정구조가 가역적으로 변한다. 이 ZrO2에 금속산화물을 고용시키면 형석 (CaF2:Florite)형의 입방정 결정구조가 실온에서도 안정하게 존재하게 된다. 안정화제 산화물은 caO, MgO등 2가 산화물외에 3가 또는 4가의 금속산화물로서 Sc2O3, Y2O3, Sm2O3, Nd2O3, Gd2O3, Y2O3, CeO2 등이며 이들은 금속이온의 원자가가 변하기 쉬운 희토류 산화물이다. 안정화 지르코니아는 형석형 결정구조이며 결정화학적으로 보면 금속양이온이 산소이온에 대해서 정육면체형의 8배위를 하고 있다. 이때 이온반경비(양이온/음이온)에 따라 Zr+4자리와 O-2자리의 격자위치와 모양이 형성되므로 비틀어진 정육면체구조이건 이상적인 정육면체 형석구조를 이룬다. 이는 지르코니아의 결정상의 2상-3상인 부분안정화 지르코니아다결정체(PSZ : partially stabilized zirconia)이거나 단일상-2상인 정방정 지르코니아다결정체(TZP : tetragonal zirconia polycrystal)의 결정구조를 가지는데 기인한다. PSZ는 주로 MgO, CaO를 안정화제로 고용시켜 입방정 영역에서 소결하고 이를 다시 입방정과 정방정의 상 영역에서 열처리하여 입방정 입자내부에 정방정을 석출 형성시킨 것이며 TZP는 Y2O3 및 CeO2를 고용시켜 PSZ와 다르게 일반적인 상압소결한 정방정 결정상의 미립자이다. 산화지르코늄 분말은 지르콘사에서 열분해시킨 지르코늄소결.융해괴(caustic fusion clinker)를 산처리하여얻어진 지르코늄산용액(zirconyl acid solution : cloride, sulfide, nitride 등)으로부터 제조된다. 고순도 산화지르코늄은 용액 결정석출법에 의해 ZrOCl2.8H2O, 5ZrO2.3SO3.15H2O, ZrO(NO3)2.xH2O 등의 지르코늄 수화물만을 재결정화시킨 것으로부터 얻을 수 있으며 이 지르코늄염 수용액으로부터 입자미세구조를 효과적으로 제어하여 산화지르코늄 및 안정화 지르코니아 분말제조가 가능하다. 안정화 지르코니아 분말은 ZrO2와 안정화산화물의 고용을위하여 가열처리를 필요로 하며 일정온도에서 최적상태로 숙성하므로서 2가지 상(phase) 이상의 고용체를 가지게 된다. 안정화 지르코니아 분말은 고용처리온도를 낮추고 효과적으로 생성시키기 위해서는 지르코늄 및 안정화제염을 혼합하고 습식 직접합성하여 저온에서 고용체의 합해진상 영역을 생성시키는 것이다. 이는 지르코니아 원료분말의 미세구조를 제어하므로서 가능하며 이때 화학성분조성과 크기형태가 균일하게 분포된 입자분말을 얻을 수 있다.

• Korean Journal of Materials Research
• /
• v.24 no.5
• /
• pp.259-265
• /
• 2014

$ZrO_2$ films were coated on aluminum etching foil by the sol-gel method to apply $ZrO_2$ as a dielectric material in an aluminum(Al) electrolytic capacitor. $ZrO_2$ films annealed above $450^{\circ}C$ appeared to have a tetragonal structure. The withdrawal speed during dip-coating, and the annealing temperature, influenced crack-growth in the films. The $ZrO_2$ films annealed at $500^{\circ}C$ exhibited a dielectric constant of 33 at 1 kHz. Also, uniform $ZrO_2$ tunnels formed in Al etch-pits $1{\mu}m$ in diameter. However, $ZrO_2$ film of 100-200 nm thickness showed the withstanding voltage of 15 V, which was unsuitable for a high-voltage capacitor. In order to improve the withstanding voltage, $ZrO_2$-coated Al etching foils were anodized at 300 V. After being anodized, the $Al_2O_3$ film grew in the directions of both the Al-metal matrix and the $ZrO_2$ film, and the $ZrO_2$-coated Al foil showed a withstanding voltage of 300 V. However, the capacitance of the $ZrO_2$-coated Al foil exhibited only a small increase because the thickness of the $Al_2O_3$ film was 4-5 times thicker than that of $ZrO_2$ film.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.377-383
• /
• 1997

Yttria-stabilized TZP alloyed with pentavalent oxides $(Ta_2O_5,\;Nb_2O_5)$ were fabricated by the conventional sintering method at $1500^{\circ}C$ in air to construct the simplified ternary phase diagram. The phase stability of tetragonal -$ZrO_2$ from the quasi-binary system $ZrO_2-YTa(Nb)O_4$, which do not transform to monoclinic-$ZrO_2$ even for a wide range of grain size and annealing temperature, was investigated to determine composition region of the non-transformable $t-ZrO_2$ solid solution$(NT_{ss})$. Phase stability of $NT_{ss}$ was probably due to the enhanced stability of $_YTa(Nb)O4$ having the tetragonal fergusonite structure. It was experimentally found that mixtures having $NT_{ss}$ alloyed with $T_{ss}$ by weight%% showed both excellent phase stability of $t-ZrO_2$ and fracture toughness even though the calculated composition of the mixture /was located outside $NT_{ss}$ composition region.