• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.93-98
• /
• 2001

YMnO$_3$ films are excellent gate dielectric materials of ferroelectric random access memories (FRAMs) with MFSFET (metal -ferroelectric-semiconductor field effect transistor) structure because YMnO$_3$ films can be deposited directly on Si substrate and have a relatively low permittivity. Although the patterning of YMnO$_3$ thin films is the requisite for the fabrication of FRAMs, the etch mechanism of YMnO$_3$ thin films has not been reported. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ film is 285$\AA$/min under Cl$_2$/(Cl$_2$+Ar) of 1.0, RF power of 600 W, dc-bias voltage of -200V, chamber pressure of 15 mTorr and substrate temperature of $25^{\circ}C$. The selectivities of YMnO$_3$ over CeO$_2$ and $Y_2$O$_3$ are 2.85, 1.72, respectively. The selectivities of YMnO$_3$ over PR and Pt are quite low. Chemical reaction in surface of the etched YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS) surface of the selected YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry (SIMS). The etch profile was also investigated by scaning electron microscopy(SEM)

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.314-318
• /
• 2002

The etching behaviors of the ferroelectric $YMnO_3$ thin films were studied by an inductively coupled plasma (ICP). The maximum etch rate of $YMnO_3$ thin film is 300 ${\AA}/min$ at Ar/$Cl_2$of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of $30^{\circ}C$. Addition of $CF_4$ gas decrease the etch rate of $YMnO_3$ thin film. From the results of XPS analysis, nonvolatile $YF_x$ compounds were found on the surface of $YMnO_3$ thin film which is etched in Ar/$Cl_2$/CF$_4$plasma. The etch profile of YMnO$_3$film is improved by addition of $CF_4$ gas into the Ar/$Cl_2$ plasma. These results suggest that YF$_{x}$ compound acts as a sidewall passivants which reduce the sticking coefficient of chlorine on $YMnO_3$.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.21-24
• /
• 2000

Ferroelectric YMnO$_3$thin films are excellent dielectric materials for high integrated ferroelectric random access memory (FRAM) with metal-ferroelectric-silicon field effect transistor (MFSFET) structure. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$thin films is 285 $\AA$/min under Cl$_2$/Ar of 10/0, 600 W/-200 V and 15 mTorr. The selectivities of YMnO$_3$over CeO$_2$and $Y_2$O$_3$are 2.85, 1.72, respectively. The results of x-ray photoelectron spectroscopy (XPS) reflect that Y is removed dominantly by chemical reaction between Y and Cl, while Mn is removed more effective by Ar ion bombardment than chemical reaction. The results of secondary ion mass spectrometer (SIMS) were equal to these of XPS. The etch profile of the etched YMnO$_3$film is approximately 65$^{\circ}$and free of residues at the sidewall.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.665-672
• /
• 2000

The ferroelectric YMnO3 thin films were prepared by MOD(metal-organic decomposition) method with Y- and Mn-acetylacetonate as starting materials. Thin films were grown on various substrates by spin-coating technique. The crystalline phases of the thin films were identified by X-ray diffractometer as a function of heat-treatment temperature, pH of coating solution and substrate. In addition, the effect of Mn/Y molar ratio(0.8~1.2) on the formation of hexagonal-YMnO3 phase was investigated. In forming highly c-axisoriented hexagonal-YMnO3 single phase, the Pt coated Si substrate was more effective than the bare Si substrate, and the optimum heat-treatment condition was at 82$0^{\circ}C$ for 30 min. Higher Mn/Y molar ratio within 0.8~1.2 and pH of YMnO3 precursor solution within 0.5~2.5 favored formation of ferroelectric hexagonal phase rather than orthorhombic phase. Leakage current density of the hexagonal-YMnO3 thin film formed on Pt(111)/TiO2/SiO2/Si substrate was low enough as 0.4~4.0$\times$10-8(A/$\textrm{cm}^2$) at 5 V and its remanent polarization(Pr), calculated from the P-E hysteresis loop, was 3 nC/$\textrm{cm}^2$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05b
• /
• pp.12-16
• /
• 2001

We investigated the etching characteristics of $YMnO_3$ thin films in high-density plasma etching system. In this study. $YMnO_3$ thin films were etched with $CF_{4}/Ar$ gas chemistries in inductively coupled plasma (ICP). Etch rates of $YMnO_3$ were measured according to gas mixing ratios. The maximum etch rate of $YMnO_3$ is 18 nm/min at $CF_{4}/(CF_{4}+Ar)$ of 20%. In optical emission spectroscopy (OES) analysis, F radical and Ar* ions in plasma at various gas chemistries decreased with increasing $CF_4$ content. Chemical states of $YMnO_3$ films exposed in plasma were investigated with x-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometry (SIMS). There is a chemical reaction between metal (Y, Mn) and F and metal-fluorides were removed effectively by Ar ion sputtering. $YF_x$, $MnF_x$ such as YF, $YF_2$, $YF_3$ and $MnF_3$ Were detected using SIMS analysis. The etch slope is about $65^{\circ}C$ and free of residues.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.425-428
• /
• 1999

In this paper, the electrical properties of Pt/YMnO$_3$/Si(100) structures with difference rapid thermal annealing (RTA) treatment were investigated. YMnO$_3$films were obtained without buffer layers, introducing oxygen. A typical value of the dielectric constant was about 20 derived from 1MHz capacitance-voltage (C-V) measurement and the resistivity of the film at the field of 150kV/cm was about 1.34$\times$10$^{12}$ $\Omega$ . cm. The minimum interface state density around midgap was estimated to be about 5$\times$10$^{11}$ cm$^2$. eV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.21-24
• /
• 2000

Ferroelectric YMnO$_3$ thin films are excellent dielectric materials for high integrated ferroelectric random access memory (FRAM) with metal-ferroelectric-silicon field effect transistor (MFSFET) structure. In this study, YMnO$_3$ thin films were etched with C1$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ thin films is 285 $\AA$/min under C1$_2$/Ar of 10/0, 600 W/-200 V and 15 mTorr. The selectivities of YMnO$_3$ over CeO$_2$ and $Y_2$O$_3$ are 2.85, 1.72, respectively. The results of x-ray photoelectron spectroscopy (XPS) reflect that Y is removed dominantly by chemical reaction between Y and Cl, while Mn is removed more effective by Ar ion bombardment than chemical reaction. The results of secondary ion mass spectrometer (SIMS) were equal to these of XPS. The etch profile of the etched YMnO$_3$ film is approximately 65$^{\circ}$and free of residues at the sidewall.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.168-173
• /
• 2000

YMnO3 thin films were prepared on Pt/Ti/SiO2/Si substrate by chemical solution deposition method. The films were crystallized by heat-treatment at 85$0^{\circ}C$ for 1 hour. Effects of an annealing atmosphere(O2, Ar, vacuum) on the crystallization behavior and electridcal properties were investigated. YMnO3 thin films annealed under Ar atmosphere showed a superior crystallinity and a very strong c-aix preferred-orientation which was a polar axis. Leakage current density of the films decreased with lowering oxygen partial pressure of the annealing atmosphere. C-V and P-E ferroelectric hysteresis were observed only in the thin film heat-treated under Ar atmosphere.In order to prepare YMnO3 thin films having both low leakage current and ferroelectricity, the annealing atmsphere should be kept under a proper oxygen partial pressure which was about 1 Pa in this work. Leakage current density at 1 volt, dielectric constant($\varepsilon$r), remanent polarization(Pr), and coercive field(Ec) were 1.7$\times$10-8 A/$\textrm{cm}^2$, 25, 1.08$\mu$C/$\textrm{cm}^2$, and 100 kV/cm, respectively.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.201.1-201
• /
• 2000

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.05a
• /
• pp.105-105
• /
• 2001