• 한국세라믹학회지
• /
• 제30권12호
• /
• pp.1007-1014
• /
• 1993

YBa2Cu3Ox(YBCO) thick films were prepared by a screen printing of the powders, obtained by a coprecipitation in oxalic acid, on the Y2O3-stabilized zirconia substrates and their superconducting properties were determined. TC, JC and the orientation factor of the thick films increased with increasing temperature up to 103$0^{\circ}C$ and then the superconducting properties disappeared with further heat treatments. The optimization of JC was achieved by heating thick films at 103$0^{\circ}C$ for 7min. In this case the TC of the thick film was determined to be 87.5K. It was observed that TC of thick films depends on the orthorhombicity and JC is likely governed by a microstructure of YBCO rather than by the orientation factor.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 기술교육위원회 창립총회 및 학술대회 의료기기전시회
• /
• pp.1-4
• /
• 2001

In electrophoresis, it is studied to get best condition of suspension media with alcoholic system for superconducting film. High-temperature superconductor films of $YBa_{2}Cu_{3}O_{7-x}$ were fabricated by electrophoretic deposition(EPD) from alcohol-based suspension. Maximum stability is observed for the suspension containing iso-alcohol as dispersion medium. However, for the formation of a dense and adherent coating of YBCO on a silver substrate by EPD. the best results were obtained in mixing PrOH and BuOH suspension. The superconducting critical current density($J_c$) was $1,200A/cm^2$ for the films deposited in 30% iso-PrOH and 70 % iso-BuOH suspension.

• 비파괴검사학회지
• /
• 제35권5호
• /
• pp.314-320
• /
• 2015

본 연구에서는 펨토초의 펄스폭을 갖는 극초단 레이저를 이용하여 나노 스케일 초전도 재료의 열전도율을 측정하였다. 95 nm 두께의 이트륨바륨구리산화물($YBa_2Cu_3O_7-x$)을 티탄산스트론튬($SrTiO_3$) 기판 위에 펄스레이저 증착법으로 적층하여 시편을 제작하였으며, 유한차분법으로 1차원 과도 열전도 방정식의 해를 구하여 측정결과와 비교하였다. 곡선맞춤을 통하여 1.2 W/mK의 열전도율을 얻었으며, 이는 동일 재료의 벌크(bulk) 물성치에 비하여 낮은 값으로 확인된다. 본 연구는 마이크로/나노소자의 열설계를 위한 초전도 나노재료의 특성을 규명한다.

• 한국산학기술학회논문지
• /
• 제7권5호
• /
• pp.801-804
• /
• 2006

[ $YBa_2Cu_3O_{7-{\delta}}(YBCO)$ ]계 초전도 선재용 $GdAlO_3(GAO)$ 버퍼층을 졸-겔(sol-gel) 공정에 의해 제조하였다. 전구체 용액은 Gd 질산염과 Al 질산염을 1:1 화학양론비로 하여 메탄올에 용해하여 준비하였다. 전구체 용액을 $SrTiO_3(STO)$ (100) 단결정 기판위에 스핀 코팅하고, 수분이 포함된 $N_2-5%\; H_2$ 분위기에서 $1000^{\circ}C$에서 2시간 열처리 하였다. 열처리 후 GAO 층의 표면에 대한 주사전자현미경 관찰에 의해 GAO 층이 에피택셜의 특징인 각면 형상을 갖는 것을 알 수 있었다. X-선 회절분석에 의하면 GAO 버퍼층은 c-축으로 우선 배향된 에피택셜 박막으로써 반가폭이 각각 (002)면에서 $0.29^{\circ}(out-of-plane)$, {112}지면에서 $1.10^{\circ}(in-plane)$의 우수한 배향성을 나타내었다.

• 한국재료학회지
• /
• 제9권1호
• /
• pp.86-91
• /
• 1999

(001) $\textrm{SrTiO}_3$(STO) 기판위에 고온초전도 $\textrm{YBa}_{2}\textrm{Cu}_{3}\textrm{O}_{7-x}$(YBCO)박막을 이용한 계단형 모서리 임계접합을 제조하였다. STO (100) 단결정 기판위에 계단형 모서리(step-edge)를 제작하기 위한 이온밀링 마스크로 plasma enhanced chemical vapor deposition방법으로 증착된 diamond-like carbon (DLC) 박막을 사용하였고, oxygen reactive ion etch 방법으로 건식식각하였다. 이렇게 제작된 계단형 모서리 기판위에 c-축 수직한 YBCO 박막과 STO박막을 pulsed laser deposition방법으로 에피텍셜하게 증착하였다. 계단의 상층과 하층에서 모두 임계가 형성되었으며 이 접합의 임계온도는 77 K 이상이었고 16K에서 $\textrm{I}_{c}\textrm{R}_{n}$products가 7.5mV, 77 K에서 0.3mV의 값을 나타내었다. 이들 전류-전압 특성은 two noisy resistively shunted Josephson junction 모델을 잘 만족하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1995년도 추계학술대회 논문집
• /
• pp.148-151
• /
• 1995

Excimer laser has been used to fabricate superconducting YBa$_2$Cu$_3$O$\sub$7-x/(YBCO) thin films on various substrates. An XeCl excimer laser with an wavelength of 308 nm was used to deposit both buffer layer and superconducting thin film on sapphire substrate. The characterizations of the interface between thin film and substrate were performed. The interfacial properties of thin films on buffered sapphire and on bare sapphire were compared. With a 20 nm PrBa$_2$Cu$_3$O$\sub$7-x/(PBCO) buffer layer, no diffusion layer was observed between film and substrate while the diffusion layer with about 30 nm thickness was observed between film and sapphire without buffer layer.

• Journal of Magnetics
• /
• 제16권2호
• /
• pp.186-191
• /
• 2011

[ $YBa_2C_3O_{7-x}$ ]films were fabricated on a $SrTiO_3$ (100) substrate using a trimethylaceate propionic acid (TMAP)-based MOD process by controlling the precursor solution viscosity, firing temperature, and by using various coatings. The viscosity of the precursor solution was controlled by the addition of Xylenes. The films were heat treated with different temperatures from 750 to $800^{\circ}C$. c-axis oriented films were obtained. After adding 9 ml of Xylene into the precursor solution, the $T_c$ of the YBCO film, which was coated 2 times and heat treated at $800^{\circ}C$, was 86 K and the measured $J_c$ was above 2.5 MA/$cm^2$ at 77 K in a zero-field.

• ETRI Journal
• /
• 제18권4호
• /
• pp.339-346
• /
• 1997

Good quality a-axis oriented thin films of $YBa_2Cu_3O_{7-x}$ may be grown by the use of a $PrBa_2Cu_3O_{7-x}$ (PBCO) layer as a template. Here we present a detailed study of the nucleation of the PBCO layer, explaining the orientations observed. It is determined that the wavy surface of a $LaSrGaO_4$ (LSGO) (100) substrate consists of the {101} planes by observing cross-sectional transmission electron microscopy images of the interface between the PBCO film and the substrate. The images and selected area diffraction patterns show that a mixed c-and b-axis oriented PBCO layer was initially grown on the substrate, followed by pure b-axis oriented PBCO growth. We explain that the c-axis oriented growth is the result of the growth of the PBCO (019) planes on the LSGO (101) planes. We conclude that the nucleation and growth of the PBCO films at the initial stages depends on the crystallographic plane of the substrate surfaces, however, as the film grows further, the kinetics of the deposition process favors b-axis oriented growth.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2009년도 Korea Superconductivity Society Meeting 2009
• /
• pp.43-43
• /
• 2009

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2005년도 High Temperature Superconductivity Vol.XV
• /
• pp.77-77
• /
• 2005