• Proceedings of the KIEE Conference
• /
• 2008.10a
• /
• pp.121-122
• /
• 2008

The films of the vanadium tungsten oxide, $V_{1.85}W_{0.15}O_5$, were grown on Pt/Ti/$SiO_2$/Si substrate by RF sputtering method. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the thin film thickness. As increasing of $V_{1.85}W_{0.15}O_5$ thickness, the grain size, morphology, and crystallinity increased. The dielectric constants of $V_{1.85}W_{0.15}O_5$ thin films deposited at 150nm were 71.11, with a dielectric loss of 0.015, respectively. Also, The $V_{1.85}W_{0.15}O_5$ thin films showed good TCR values of -3.45%/K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.237-238
• /
• 2008

The films of Vanadium tungsten oxide, $V_{1.85}W_{0.15}O_5$, were grown on Pt/Ti/$SiO_2$/Si substrate by RF sputtering method. The $V_{1.85}W_{0.15}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $300^{\circ}C$ were 55, with a dielectric loss of 1.435, respectively. Also, the TCR values of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $300^{\circ}C$ were about -3.6%/K.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1322_1323
• /
• 2009

The $V_{1.85}W_{0.15}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were 38.11, with a dielectric loss of 1%, respectively. Also, the TCR values of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were about -3.45%/K.

• Proceedings of the KIEE Conference
• /
• 2008.10a
• /
• pp.117-118
• /
• 2008

The $V_{1.85}W_{0.15}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were 38.11, with a dielectric loss of 1%, respectively. Also, the TCR values of the $V_{1.85}W_{0.15}O_5$ thin films annealed at $400^{\circ}C$ were about -3.45%/K.