• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.388-388
• /
• 2010

In this study, Ferroelectric vinylidene fluoride-trifluoroethylene (VF2-TrFE) copolymer films were directly deposited on degenerated Si (n+, $0.002\;{\Omega}{\cdot}cm$) using by spin coating method. A 1~5 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene (VF2:TrFE = 70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers at a spin rate of 2000 ~ 4000 rpm for 2 ~ 30 seconds. After annealing in a vacuum ambient at 100 ~ $200^{\circ}C$ for 60 min, upper aluminum electrodes were deposited by vacuum evaporation for electrical measurement. X-ray diffraction results showed that the VF2-TrFE films on Si substrates had $\beta$-phase of copolymer structures. The capacitance on highly doped Si wafer showed hysteresis behavior like a butterfly shape and this result indicates clearly that the copolymer films have ferroelectric properties. The typical measured remnant polarization ($P_r$) and coercive filed ($E_c$) values were about $5.7\;{\mu}C/cm^2$ and 710 kV/em, respectively, in an applied electric field of ${\pm}$ 1.5 MV/em. The gate leakage current densities measured at room temperature was less than $7{\times}10^{-7}\; A/cm^2$ under a field of 1 MV/cm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.315.2-315.2
• /
• 2013

본 논문에서는 반사방지 VF2-TrFE 박막을 이용한 MIS Solar cell을 제작하여 전기적, 구조적 특성을 평가하였다. ALD법을 이용하여 고유전율의 화학적 안정성이 우수한 산화알루미늄을 절연층으로 한 Al/Al2O3/Si(100)을 제작하였으며 cell의 효율을 향상시키기 위해 spin coating법을 이용하여 VF2-TrFE 반사방지막을 증착시켰다. 제작된 반사방지 VF2-TrFE 박막 MIS solar cell은 MIS 커패시터의 전류밀도-전계 특성, 커패시턴스-전압 특성과 반사방지막 열처리 조건에 따른 태양전지 효율을 Solar simulator 및 Quantum Efficiency system으로 측정하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.115-116
• /
• 2008

The ferroelectric vinylidene fluoride-trifluoroethylene ($VF_2$-TrFE) and $Al_2O_3$ passivation layer for the Metal/Insulator/Ferroelectric/Semiconductor (MIFS) structure were deposited using spin coating and remote plasma atomic layer deposition (RPALD), respectively. A 2.5 ~ 3 wt % diluted solution of purified vinylidene fluoride-trifluoroethylene ($VF_2$: TrFE=70:30) in a DMF solution were prepared and deposited on silicon wafer at a optimized spin speed. After annealing in a vacuum ambient at 150 ~ $200^{\circ}C$ for 60 min, upper insulator layer were deposited at temperature ranging from 100 ~ $150^{\circ}C$ by RPALD. We described electrical and structural properties of MIFS fabricated by spin coating and RPALD methods.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.169-170
• /
• 2006

In this study, ultra thin films of ferroelectric vinylidene fluoride-trifluoroethylene (VF2-TrFE) copolymer were fabricated on degenerated Si (n+, $0.002\;{\Omega}{\cdot}cm$) using by spin coating method. A 1~5 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene (VF2:TrFE=70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers at a spin rate of 2000~5000rpm for 30 seconds. After annealing in a vacuum ambient at $200^{\circ}C$ for 60 min, upper gold electrodes were deposited by vacuum evaporation for electrical measurement. X-ray diffraction results showed that the VF2-TrFE films on Si substrates had $\beta$-phase of copolymer structures. The capacitance on $n^+$-Si(100) wafer showed hysteresis behavior like a butterfly shape and this result indicates clearly that the dielectric films have ferroelectric properties. The typical measured remnant polarization (2Pr) and coercive filed (EC) values measured using a computer controlled a RT-66A standardized ferroelectric test system (Radiant Technologies) were about $0.54\;C/cm^2$ and 172 kV/cm, respectively, in an applied electric field of ${\pm}0.75\;MV/cm$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.20-21
• /
• 2008

Ferroelectric vinylidene fluoride-trifluoroethylene ($VF_2$-TrFE) copolymer films were directly deposited on degenerated Si ($n^+$, 0.002 $\Omega{\cdot}cm$) using by dip coating method. A 1 ~ 3 wt% diluted solution of purified vinylidene fluoride-trifluoroethylene ($VF_2$:TrFE=70:30) in a dimethylformamide (DMF) solvent were prepared and deposited on silicon wafers using dip coating method for 10 seconds. After Post-Annealing in a vacuum ambient at 100~200 $^{\circ}C$ for 60 min, upper aluminum electrodes were deposited by thermal evaporation through the shadow mask to complete the MFS structure. The ferroelectric $\beta$-phase peak of films, depending on the annealing temperature, started to show up around $125^{\circ}C$, and the intensity of the peak increased with increasing annealing temperature. Above $175^{\circ}C$, the peak started to decrease. The C-V characteristics were measured using a Precision LCR meter (HP 4284A) with frequency of 1MHz and a signal amplitude of 20 mV. The leakage-current versus electric-field characteristics was measured by mean of a pA meter/DC voltage source (HP 4140B).