• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권2호
• /
• pp.98-102
• /
• 2000

Ferroelectric PZT heterolayered thin films were fabricated by spin coating method on the Pt/Ti/SiO2/Si substrate using PZT(10/90) and PZT(90/10) m7etal alkoxide solutions. All PZT heterolayered films showed a homogeneous grain structures without presence of rosette structure. It can be assumed that the lower PZT layers played a role of nucleation site for the formation of the upper PZT layer. Pb-deficient PZT phase was formed at PZT/Pt interface due to the diffusion of Pb element into a Pt bottom electrode. The relative dielectric constant and the dielectric loss of the PZT-6 film were 567 and 3.6%, respectively. Increasing the number of coatings, remanent polarization and coercive field were decreased and the values of the PZT-6 heterolayered film were $7.18\muC/cm^2$ and 68.5kV/cm, respectively. Leakage current densities were increased with increasing the number of coatings, and the value of the PZT-4 film was about $7\times10-8A/cm^2$ at 0.05MV/cm.

• 한국재료학회지
• /
• 제12권3호
• /
• pp.211-214
• /
• 2002

Properties of 52/48 PZT films with various thicknesses for piezoelectric micro-electro mechanical systems (MEMS) devices fabricated by multi-coating method on $Pt(3500{\AA})/Ti(400{\AA})/SiO_2(3000{\AA})/Si$(525$\mu\textrm{m}$) substrates were investigated. PZT films were deposited by spin-coating process at 3500 rpm for 30 sec, followed by pyrolysis at 45$0^{\circ}C$ for 10 min producing the thickness of about 120nm. These processes were repeated 4, 8, 12, 16 and 20 times in order to have various thicknesses, respectively. Finally, they were crystallized at $650^{\circ}C$ for 30 min. All thick PZT films showed dense and homogeneous surface microstructures. Thick PZT films showed crystalline structures of random orientations with increasing thickness. Dielectric constants of thick PZT films were increased with increasing film thickness and reached 800 at 100kHz for 2.3$\mu\textrm{m}$ thick PZT film. $P_r\; and\; E_c$ of 2.3$\mu\textrm{m}$ thick PZT films were about 20$\mu$C/$\textrm{cm}^2$ and 63kV/cm. Depth profile analysis by Auger Electron Spectroscopy (AES) of 4800 $\AA$ thick PZT film showed the formation of the perovskite phase on Pt layer by Pb diffusion behavior. It was considered that Pb-Pt intermediate layer promoted PZT (111) columnar structures.

• 대한전자공학회논문지SD
• /
• 제39권3호
• /
• pp.1-8
• /
• 2002

Sol-gel 법으로 제작한 (Pb/sub 0.9/La/sub 0.1/)Ti/sub 0.975/O₃(PLT (10)) 박막의 구조적 및 전기적 특성에 대한 과잉 Pb 첨가량이 미치는 영향을 조사하였다. DTA 와 X-선 회절분석 결과, 과잉 Pb 첨가량이 7.5 에서 15㏖%로 증가함에 따라, PLT(10) 박막의 결정화 온도는 감소하였으며, (100) 우선 배향성은 증가하였다. 또한, PLT(10) 박막의 과잉 Pb 첨가량에 따른 전기적 특성을 조사한 결과, 12.5㏖% 의 과잉 Pb 를 첨가한 박막이 가장 우수한 전기적 특성을 나타내었다. 이때, 비유전률과 유전손실은 각각 350 과 0.02 이었고, 100㎸/㎝ 에서 누설전류밀도는 1.27×10/sup -6/A/㎠ 이었다. 또한 이력곡선으로부터 구한 잔류분극(p) 과 항전계 (Ec) 는 각각 6.36μC/㎠ 와 58.7㎸/㎝ 이었으며, ±5V 의 사각펄스를 10/sup 9/회 인가한 후에도 잔류 분극값이 초기값의 약 15% 감소하는 비교적 우수한 피로특성을 나타내었다. 이상의 결과로부터, 과잉 Pb 첨가량이 12.5㏖% 인 PLT(10) 박막은 비휘발성 메모리에 응용될 수 있는 매우 유망한 재료임을 알 수 있었다.

• 한국진공학회지
• /
• 제15권2호
• /
• pp.173-179
• /
• 2006

Pulsed laser deposition 방법으로 증착한 $PbZr_{0.3}Ti_{0.7}O_{3}$ (PZT)박막의 구조적, 전기적 성질에 대한 연구를 하였다. PZT 박막은 $LaAlO_3$ 기판위에 동일한 조건으로 증착된 $LaMnO_3$ (LMO) 산화물을 하부 전극으로 하여 증착시간을 변화시키며 증착하였다. High-resolution x-ray diffraction 결과를 통해 LMO 하부 전극과 PZT 박막이 방향성 있게 자란 것을 확인할 수 있었고 박막의 두께는 field-emission scanning electron microscope을 통하여 측정할 수 있었다. 또한 우리는 atomic force microscopy을 이용하여 박막의 표면 거칠기를 구하였고 국소적인 범위의 전기적 특성은 piezoelectric force microscopy 모드를 이용하여 측정하였다. 그 결과 PZT/LMO 구조는 나노 스토리지의 미디어로 쓰이기 위해 필요한 성질들을 갖추었음을 알 수 있었다.

• 대한금속재료학회지
• /
• 제50권7호
• /
• pp.539-544
• /
• 2012

Thermal shock behavior of TiN-coated SUS 304 substrate was investigated using a laser ablation method. By short surface ablation with a pulse Nd-YAG laser, considerable surface crack and spalling were observed, whereas there were few oxidation phenomena, such as grain growth of TiN crystallites, nucleation and growth of $TiO_2$ crystallites, which were observed from the coatings quenched from $700^{\circ}C$ in a chamber. The oxygen concentration of the ablated coating surface with the pulse laser also had a lower value than that of the quenched coating surface by Auger electron spectroscopy and electron probe micro analysis. These results were attributed to the fact that the properties of the pulse laser method have a very short heating time and so the diffusion time for oxidation was insufficient. Consequently, it was verified that the laser thermal shock test provides a way to evaluate the influence of the thermal shock load reduced oxidation effect.

• 한국산학기술학회논문지
• /
• 제4권3호
• /
• pp.199-203
• /
• 2003

In this study plastic optical fibers (POFs) were considered as light-transmitting media and substrates for the potential use in photocatalytic environmental purification system. After the characteristics of POFs in terms of light transmittance and absorption were determined at the beginning, the further investigation was performed through the photocatalytic degradation of trichloroethylene (TCE), iso-propanol and etc. with TiO$_2$-coated optical fiber reactor systems (POFR). It is concluded that the use of POFs is preferred to quartz optical fibers (QOFs) since the advantages such as ease of handling, lower cost, relatively reasonable light attenuation at the wavelength of near 400nm can be obtained. Various geometrical reactor shapes have been constructed and applied for the last one and half years. For the use of POF in water phase treatment, however, more detailed scientific and engineering aspects should be envisaged. This case requires a suitable mixture to obtain more stable and innocuous immobilization of photocatalyst on POF. To overcome this disadvantage, metal-organic chemical vapor deposition (MOCVD) was conducted in a fluidized bed to deposit thin films of titania on glass and alumina beads. Those can be used as photocatalysis for the removal of pollutants especially in liquid phases.

• 한국재료학회지
• /
• 제19권7호
• /
• pp.349-355
• /
• 2009

Metal thin film patterns on a LTCC substrate, which was connected through inner via and metal paste for electrical signals, were formed by a screen printing process that used electric paste, such as silver and copper, in a conventional method. This method brought about many problems, such as non uniform thickness in printing, large line spaces, and non-clearance. As a result of these problems, it was very difficult to perform fine and high resolution for high frequency signals. In this study, the electric signal patterns were formed with the sputtered metal thin films (Ti, Cu) on an LTCC substrate that was coated with protective oxide layers, such as $TiO_2$ and $SiO_2$. These electric signal patterns' morphology, surface bonding strength, and effect on electro plating were also investigated. After putting a sold ball on the sputtered metal thin films, their adhesion strength on the LTCC substrate was also evaluated. The protective oxide layers were found to play important roles in creating a strong design for electric components and integrating circuit modules in high frequency ranges.

• 한국정밀공학회지
• /
• 제33권5호
• /
• pp.409-417
• /
• 2016

It is well known that Morpho butterflies show distinctive, brilliant and iridescent colors and have micro-nano scale structures, instead of dyes and pigments, on their wings. This structural coloration is regarded as a novel technique to express color with a long lifetime, ease and precise tenability. Here, we studied optical multilayer thin films with thickness of several tens of nm ($TiO_2$ and $SiO_2$) and lens-shape micro-patterns. Fabrication and characterization of the multilayer stacking structure and the micro-pattern structure were performed and the films were analyzed via several optical measuring techniques. Finally, we discussed how the micro-pattern structure could enhance independence with color changes according to the viewing angle.

• 대한전자공학회논문지SD
• /
• 제39권10호
• /
• pp.35-42
• /
• 2002

Modulation frequency dependences of the pyroelectric properties of PLT (P $b_{1-x}$ L $a_{x}$ $Ti_{1-x}$ 4/ $O_3$) thin films with La concentrations of 5, 10 and 15㏖% have been investigated by using the dynamic method. The PLT thin film with 10㏖% of the La concentration (PLT(10) thin film) shows the most excellent pyroelectric properties among the films. For PLT(10) thin film, the pyroelectric coefficient shows the maximum value of 6.6$\times$10$^{-9}$ C/$\textrm{cm}^2$ㆍK without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are 1.03$\times$10$^{-11}$ Cㆍcm/J and 1.46$\times$10$^{-9}$ Cㆍcm/J, respectively. Voltage responsivity corresponding to the pyroelectric voltage is almost constant at low modulation frequency and decreases in proportional to frequency at high modulation frequency. Voltage responsivity is 5.15 V/W at 8Hz. Noise equivalent power (NEP) and specific detectivity ( $D^{*}$) of the PLT(10) thin film are 9.93$\times$10$^{-8}$ W/H $z^{1}$2/ and 1.81$\times$10$^{6}$ cmH $z^{1}$2/W at the frequency of 100Hz, respectively. The results indicate that PLT(10) thin film is very suitable for pyroelectric IR sensors.s.s.

• 한국표면공학회지
• /
• 제29권5호
• /
• pp.415-423
• /
• 1996

Thin film technologies for fabricating SQUIDs involve etching and deposition procedures with the proper substrate materials and $YBa_2Cu_3O_{7-d}$ (YBCO) as the high $T_c$ superconductor. YBCO were prepared on various substrates of MgO, $SrTiO_3$, and $LaAlO_3$ by using off-axis magnetron sputtering methods and annealing in-situ. The parameters of film fabrication processes had been optimized to yield good quality films in terms of the critical temperature $T_c$ and the critical current density $J_c$. The optimized processes yielded $T_C$>90K along with $J_c$>$10_6A$$extrm{cm}^2$ at 77K and>$2\times10_7A/Cm^2$ at 5K. We fabricated step-edge type dc-SQUIDs and directly coupled magnetometers, producing step edges on MgO(100) substrates by etching with Ar-ion beam, depositing YBCO material on them, then patterning them by using ion-milling technique. Circuitizing washer-shape SQUIDs to possess a pair of step-edge junctions of 2-5$\mu$ line width with a high angle>$50^{\circ}C$ , we examined their I-V characteristics thoroughly and Shapiro steps clearly as we irradiate microwaves of 8-20 GHz frequency.