• Korean Journal of Materials Research
• /
• v.13 no.11
• /
• pp.737-741
• /
• 2003

Polycrystalline $Ti_{l-x}$ $Co_{x}$ $O_2$thin films on $SiO_2$ (200 nm)/Si (100) substrates were prepared using liquid-delivery metalorganic chemical vapor deposition. Microstructures and ferromagnetic properties were investigated as a function of doped Co concentration. Ferromagnetic behaviors of polycrystalline films were observed at room temperature, and the magnetic and structural properties strongly depended on the Co distribution, which varied widely with doped Co concentration. The annealed $Ti_{l-x}$ $Co_{x}$ $O_2$thin films with $x\leq$0.05 showed a homogeneous structure without any clusters, and pure ferromagnetic properties of thin films are only attributed to the X$l-x_{l-x}$ $Co_{x}$X$O_2$phases. On the other hand, in case of thin films above x = 0.05, Co-rich clusters formed in a homogeneous $Ti_{l-x}$ $Co_{x}$ $O_2$phase, and the overall ferromagnetic (FM) properties depended on both FMTCO and FMCo. Co-rich clusters with about 10-150 nm size decreased the value of Mr (the remanent magnetization) and increased the saturation magnetic field.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.280-286
• /
• 2001

10 이하의 저유전율을 갖는 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스의 미세구조와 고주파 유전특성을 조사하였다. (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스는 정방정(tetragonal) 구조를 가진다. 0.1BaWO$_4$-0.9Mg$_2$SiO$_4$세라믹스는 BaWO$_4$와 $Mg_2$SiO$_4$의 상들이 공존하는 혼합상을 보였으며, $Mg_2$SiO$_4$가 이차사으로 형성된 것이 관찰되었다. 120$0^{\circ}C$~140$0^{\circ}C$에서 2시간 동안 소결된 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스는 $\varepsilon$$_{r}$=6.37~8.21, Q.f=15000~99422 그리고 $ au$$_{f}$=73.9~48.9 ppm/$^{\circ}C$의 고주파 유전특성을 가졌다. $\tau$$_{f}$를 보정하기 위해, CaTiO$_3$(1,5 wt%)가 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x$\geq$0.9) 세라믹스에 첨가되었다. 135$0^{\circ}C$에서 2시간 동안 소결된 0.1BaWO$_4$-0.9Mg$_2$SiO$_4$+CaTiO$_3$(5 wt%) 세라믹스는 $\varepsilon$$_{r}$=7.3, Q.f=30532 그리고 $\tau$$_{f}$=-30 ppm/$^{\circ}C$의 고주파 유전특성을 얻었다. 얻었다.

• ETRI Journal
• /
• v.31 no.6
• /
• pp.675-679
• /
• 2009

$Ti_xSi_{1-x}O_y$ (TSO) thin films are fabricated using plasma-enhanced atomic layer deposition. The Ti content in the TSO films is controlled by adjusting the sub-cycle ratio of $TiO_2$ and $SiO_2$. The refractive indices of $SiO_2$ and $TiO_2$ are 1.4 and 2.4, respectively. Hence, tailoring of the refractivity indices from 1.4 to 2.4 is feasible. The controllability of the refractive index and film thickness enables application of an antireflection coating layer to TSO films for use as a thin film solar cell. The TSO coating layer on an Si wafer dramatically reduces reflectivity compared to a bare Si wafer. In the measurement of the current-voltage characteristics, a nonlinear coefficient of 13.6 is obtained in the TSO films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.131-134
• /
• 2002

The effect of the addition on the densification, low temperature sintering, and microwave dielectric properties of the Ca[($Li_{1/3}Nb_{2/3}$)$_{1-x}$$Ti_{x}$]$O_{3-{\delta}}$/(CLNT) was investigated. $Bi_2O_3$ additives improved the dencification and reduced the sintering temperature from $1150^{\circ}C$ to $900^{\circ}C$ of CLNT microwave dielectric ceramics. As increasing $Bi_2O_3$ contents, the dielectric constants and bulk density were increased. The quality factor, however, was decreased slighty. The temperature coefficients of the resonant frequency shifted positive value as increasing $Bi_2O_3$ contents. The dielectric properties of Ca[($Li_{1/3}Nb_{2/3}$)$_{1-x}$$Ti_{x}$]$O_{3-{\delta}}$ and Ca[($Li_{1/3}Nb_{2/3}$)$_{0.8}Ti_{0.2}$]$O_{3-{\delta}}$ with 5wt% $Bi_2O_3$ sintered at $900^{\circ}C$ for 3h were $\varepsilon_{r}$=20, 35 Q.$f_{0}$=6500, 11,000 GHz, $\tau_{f}$=4, 13 ppm/$^{\circ}C$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.40 no.4
• /
• pp.346-349
• /
• 2003

Microwave dielectric characteristics and physical properties of the new Zr$_{1-x}$ (Bn$_{1}$3/Nb$_{2/3}$)xTi $O_4$ (0.2$\leq$x$\geq$ 1.0) system have been investigated as a function of the amount of Bn$_{1}$3/Nb$_{2/3}$ $O_2$substitution. With increasing Bn$_{1}$3/Nb$_{2/3}$ $O_2$ content (x), two phase regions were observed: $\alpha$-Pb $O_2$ solid solution (x<0.4), mixture of the rutile type Zn$_{1}$3/Nb$_{2/3}$Ti $O_4$ and the $\alpha$-Pb $O_2$ solid solution (x$\geq$0.4). In the$\alpha$-Pb $O_2$solid solution region below x<0.4, the Q.f$_{0}$ value sharply increased and the Temperature Coefficient of the Resonant Frequency(TCF) decreased with increasing Bn$_{1}$3/Nb$_{2/3}$ $O_2$ contents while dielectric constant (K) showed nearly same value. In the mixture region above x$\geq$4, the dielectric constant and TCF increased with increasing Bn$_{1}$3/Nb$_{2/3}$ $O_2$ content. Zr$_{1-x}$ (Zn$_{1}$3/Nb$_{2/3}$)xTi $O_4$ materials have excellent microwave dielectric properties with K=44.0, Q.f$_{0}$ : 41000 GHz and TCF =-3.0 ppm/$^{\circ}C$ at x=0.35.=0.35. x=0.35.=0.35.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.2
• /
• pp.75-81
• /
• 1999

$CaTiO_3$-$ La(Mg_{2/3}Ta_{1/3})O_3$ solid solutions were prepared in order to improve the microwave dielectric properties of $CaTiO_3$. XRD analysis revealed that the crystal structure of the solid solution changed from orthorhombic to monoclinic as the amount of $ La(Mg_{2/3}Ta_{1/3})O_3$increased. When x=0.3 in (1-x)$CaTiO_3+xLa(Mg_{2/3}Ta_{1/3})O_3$, the dielectric constant was 49, the temperature coefficient of resonance frequency was +$14ppm/^{\circ}C$, and $Q \times f_0$ was 17000.

• Applied Microscopy
• /
• v.34 no.1
• /
• pp.61-69
• /
• 2004

The microwave dielectric properties and microstructures of the Complex Perovskite (1-x)$(Li_{1/2}Sm_{1/2})TiO_3-x (Na_{1/2}Sm_{1/2})TiO_3$(LNST) system were investigated using the X-ray diffraction (XRD) and scanning electron microscopy (SEM). LNST had not only the antiphase tilting of oxygen octahedron but also the inphase tilting of oxygen octahedron and the antiparallel shift of cations. Also, when $0.0{\leq}x{\leq}0.4$, LNST had the vacancy ordering of A-sites because of the evaporation of Li ions. From the observation of the microstructure, abnormal grain growth phenomena were observed over the whole range of x. The temperature coefficient of resonant frequency ($T_{cf}$) of the $({Li_{1/2}}^{+1}{Sm_{1/2}}^{+3})TiO_3$(LST) system has a large negative value ($-220ppm/^{\circ}C$) but the $({Na_{1/2}}^{+1}{Sm_{1/2}}^{+3})TiO_3$(NST) system which substituted $Na^{+1}$ has a large positive value ($+173ppm/^{\circ}C$). The dielectric properties of ${\varepsilon}_r=103,\;Q*f_{0}=3,700GHz$ and $T_{cf}=+50ppm/^{\circ}C$ at 4GHz were obtained when x =0.4.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.42 no.2
• /
• pp.163-170
• /
• 2022

The present study investigates NO_x-removal and sound-absorption performances of photocatalytic porous concrete prepared by various TiO₂ application methods. Photocatalytic porous concrete samples were prepared by one of the following: 1) mechanically mixing TiO₂ during casting; 2) mixing bottom ash aggregate pretreated with TiO₂ during casting; and 3) spraying TiO₂ solution to the normally fabricated porous concrete. The test results indicated that the mechanical mixing of TiO₂ decreased the compressive strength as the added TiO₂ content increased. The use of pretreated bottom ash aggregate reduced the porosity, yet the compressive strength of the concrete was similar to that measured from the former method. Porous concrete samples sprayed with the TiO₂ solution exhibited enhanced compressive strength, while the porosity was analogous to those measured from other methods. The NO_x-removal performance was the highest in the samples sprayed with the TiO₂ solution, followed by the samples using pretreated bottom ash aggregate and mechanically mixed TiO₂. The samples with mechanically mixed TiO₂ identified a relationship between soundabsorption performance and porosity. However, no particular tendency was observable in the samples with other TiO₂ application methods.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.3
• /
• pp.115-120
• /
• 2016

$CeO_2$ is used as a co-catalyst with $TiO_2$ to improve the catalytic activity of $MnO_x$ and characterization of nano-sized powder is identified with de-NOx efficiency. A comparison between $MnO_x-CeO_2/TiO_2$ and single $CeO_2$ was conducted in terms of microstructural analysis to observe the behavior of $CeO_2$ in the ternary catalyst. The $MnO_x-CeO_2/TiO_2$ catalyst was synthesized by sol-gel method and the average particle size of the single $CeO_2$ is about $285{\mu}m$ due to the low thermal stability, whereas the particle size $MnO_x-CeO_2/TiO_2$ is about 130 nm. The strong interaction between Ce and Ti was identified through the EDS mapping by transmission electron microscopy (TEM). The improvement about 20 % of $de-NO_x$ efficiency is observed in the low-temperature ($150^{\circ}C{\sim}250^{\circ}C$) and vigorous oxygen exchange by well-dispersed $CeO_2$ is the reason of catalytic activity improvement.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.171-171
• /
• 2003

공정기술의 향상으로 DRAM(dynamic random acess memory)의 고집적화가 이루어지고 있으며, 각 개별소자 및 셀 영역의 점유면적의 감소가 요구되어지고 있다. 따라서 기존에 사용하던 NO (Si$_3$N$_4$/SiO$_2$)박막보다 유전율이 높은 고유전물질에 대한 연구가 진행되고 있다. Ta$_2$O$_{5}$, $Y_2$O$_3$, HfO$_2$, ZrO$_2$,Nb$_2$O$_{5}$, BaTiO$_3$, SrTiO$_3$ 및 (BaSr)TiO등이 고유전물질로 연구되고 있는데 그 중 공정의 안정성, 누설전류의 우수성으로 인해 Ta$_2$O$_{5}$이 많이 연구되고 있다. 본 실험에서는 TiO$_2$가 8 mol%가 첨가된 Ta$_2$O$_{5}$의 열처리 온도에 따른 전기적, 유전특성을 살펴보려고 한다살펴보려고 한다