• Korean Journal of Materials Research
• /
• v.15 no.5
• /
• pp.306-312
• /
• 2005

The hydrogen sorption properties of $Ti_{0.3}Zr_{0.2}V_{0.5}$ NEC(non-evaporable getter) alloy and its hydrides were evaluated at room temperature. The alloy and hydride powders were prepared by the Hydride-DeHydride(HDH) method. The hydrogen sorption speed of $Ti_{0.3}Zr_{0.2}V_{0.5}$ alloy was measured to increase with the amounts of hydride phase in the getter. The hydrogen sorption speeds of $Ti_{0.3}Zr_{0.2}V_{0.5},\;(Ti_{0.3}Zr_{0.2}V_{0.5})H_{1.52},\;and\;(Ti_{0.3}Zr_{0.2}V_{0.5})H_{1.94}$ were 2.22, 3.14 and 5.08 liter/sec, respectively. The unexpected enhancement of hydrogen sorption speed with the presence of the hydride phase is considered to be due to the pre-saturation of hydrogen trap sites which can retard the diffusion of hydrogen in the alloy.

• Journal of Powder Materials
• /
• v.17 no.5
• /
• pp.385-389
• /
• 2010

Titanium powders have been usually produced by de-hydrogenating treatment in vacuum with titanium hydride ($TiH_2$) powders prepared by milling of hydrogenated sponge titanium, $TiH_x$. The higher stoichiometry of x in $TiH_x$, whose maximum value is 2, is achieved, crushing behavior is easier. $TiH_x$ powder can be, therefore, easy to manufactured leading to obtain higher recovery factor of it. In addition, contamination of the powder can also minimized by the decrease of milling time. In this study, the hydrogenation behavior of sponge titanium was studied to find the maximum stoichiometry. The maximum stoichiometry in hydride formation of sponge titanium could be obtained at $750^{\circ}C$ for 2 hrs leading to the formation of $TiH_{{\sim}1.99}$ and the treating temperatures lower or higher than $750^{\circ}C$ caused the poor stoichiometries by the low hydrogen diffusivity and un-stability of $TiH_x$, respectively. Such experimental behavior was compared with thermodynamically calculated one. The hydrogenated $TiH_{1.99}$ sponge was fully ball-milled under -325 Mesh and the purity of pure titanium powders obtained by de-hydrogenation was about 99.6%.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.969-970
• /
• 2006

In present work, manufacturing technologies of titanium hydride powder were studied for recycling of titanium tuning chip and for this, attrition ball milling was carried out under $H_2$ pressure of 0.5 MPa. Ti chips were completely transformed into $TiH_2$ within several hundred seconds. Dehydrogenation process $TiH_2$ powders is consist of two reactions: one is reaction of $TiH_2$ to $TiH_x$ and the other decomposition of $TiH_x$ to Ti and $H_2$. The former reaction shows relatively low activation energy and it is suggested that the reaction is caused by introduction of defects due to milling.

• Resources Recycling
• /
• v.32 no.2
• /
• pp.19-32
• /
• 2023

A novel method for the synthesis of titanium hydride powder from titanium tetrachloride via the magnesiothermic reduction in an hydrogen gas atmosphere was investigated. To examine the influence of temperature on the formation of titanium hydride, the reduction was conducted at 1023~1123 K under 1 atm of hydrogen gas atmosphere for approximately 30 min. Subsequently, the titanium hydride powder was sintered by maintaining the temperature for 0~120 min, and the decrease in the oxygen concentration of the powder was investigated. The experimental results showed that TiH_1.924 was produced at 1023 K, whereas mixtures of TiH_1.924 and TiH_1.5 were produced at 1073 K and 1123 K. In addition, the hydrogen concentration in the powder decreased with increasing temperature. The concentration of oxygen in the powder decreased with increasing temperature and sintering time owing to the decrease in the specific surface area of the powder. The minimum concentration of oxygen was 0.246 mass% when the mixture of TiH_1.924 and TiH_1.5 was obtained at 1073 K and a sintering time of 120 min.

• Journal of Powder Materials
• /
• v.24 no.1
• /
• pp.29-33
• /
• 2017

Titanium carbide (TiC) powders are successfully synthesized by carburization of titanium hydride ($TiH_2$) powders. The $TiH_2$ powders with size lower than $45{\mu}m$ (-325 Mesh) are optimally produced by the hydrogenation process, and are mixed with graphite powder by ball milling. The mixtures are then heat-treated in an Ar atmosphere at $800-1200^{\circ}C$ for carburization to occur. It has been experimentally and thermodynamically determined that the de-hydrogenation, "$TiH_2=Ti+H_2$", and carburization, "Ti + C = TiC", occur simultaneously over the reaction temperature range. The unreacted graphite content (free carbon) in each product is precisely measured by acid dissolution and by the filtering method, and it is possible to conclude that the maximal carbon stoichiometry of $TiC_{0.94}$ is accomplished at $1200^{\circ}C$.

• Journal of Powder Materials
• /
• v.23 no.4
• /
• pp.282-286
• /
• 2016

A sintered body of $TiB_2$-reinforced iron matrix composite ($Fe-TiB_2$) is fabricated by pressureless-sintering of a mixture of titanium hydride ($TiH_2$) and iron boride (FeB) powders. The powder mixture is prepared in a planetary ball-mill at 700 rpm for 3 h and then pressurelessly sintered at 1300, 1350 and $1400^{\circ}C$ for 0-2 h. The optimal sintering temperature for high densities (above 95% relative density) is between 1350 and $1400^{\circ}C$, where the holding time can be varied from 0.25 to 2 h. A maximum relative density of 96.0% is obtained from the ($FeB+TiH_2$) powder compacts sintered at $1400^{\circ}C$ for 2 h. Sintered compacts have two main phases of Fe and $TiB_2$ along with traces of TiB, which seems to be formed through the reaction of TiB2 formed at lower temperatures during the heating stage with the excess Ti that is intentionally added to complete the reaction for $TiB_2$ formation. Nearly fully densified sintered compacts show a homogeneous microstructure composed of fine $TiB_2$ particulates with submicron sizes and an Fe-matrix. A maximum hardness of 71.2 HRC is obtained from the specimen sintered at $1400^{\circ}C$ for 0.5 h, which is nearly equivalent to the HRC of conventional WC-Co hardmetals containing 20 wt% Co.

• Korean Journal of Metals and Materials
• /
• v.50 no.5
• /
• pp.375-381
• /
• 2012

Magnesium prepared by mechanical grinding under $H_2$ (reactive mechanical grinding) with transition elements or oxides showed relatively high hydriding and dehydriding rates when the content of additives was about 20 wt%. Ni was chosen as a transition element to be added. $Fe_2O_3$ was selected as an oxide to be added. Ti was also selected since it was considered to increase the hydriding and dehydriding rates by forming Ti hydride. A sample $Mg-14Ni-3Fe_2O_3-3Ti$ was prepared by reactive mechanical grinding, and its hydrogen storage properties were examined. This sample absorbs 4.02 wt% H for 5 min, and 4.15 wt% H for 10 min, and 4.42 wt% H for 60 min at n = 2. It desorbs 2.46 wt% H for 10 min, 3.98 wt% H for 30 min, and 4.20 wt% H for 60 min at n = 2. The effects of the Ni, $3Fe_2O_3$, and Ti addition, and hydriding-dehydriding cycling were discussed.

• Journal of Powder Materials
• /
• v.16 no.1
• /
• pp.43-49
• /
• 2009

Titanium carbides are widely used for cutting tools and grinding wheels, because of their superior physical properties such as high melting temperature, high hardness, high wear resistance, good thermal conductivity and excellent thermal shock resistance. The common synthesizing method for the titanium carbide powders is carbo-thermal reduction from the mixtures of titanium oxide($TiO_2$) and carbon black. The purpose of the present research is to fabricate nano TiC powders using titanium salt and titanium hydride by the mechanochemical process(MCP). The initial elements used in this experiment are liquid $TiCl_4$(99.9%), $TiH_2$(99.9%) and active carbon(<$32{\mu}m$, 99.9%). Mg powders were added to the $TiCl_4$ solution in order to induce the reaction with Cl-. The weight ratios of the carbon and Mg powders were theoretically calculated. The TiC and $MgCl_2$ powders were milled in the planetary milling jar for 10 hours. The 40 nm TiC powders were fabricated by wet milling for 4 hours from the $TiCl_4$+C+Mg solution, and 300 nm TiC particles were obtained by using titanium hydride.

• Journal of Hydrogen and New Energy
• /
• v.2 no.1
• /
• pp.39-46
• /
• 1990

In order to improve the power of hydride heat pump, prototype heat pump was constructed using $Zr_{0.95}Ti_{0.05}Cr_{0.9}Fe_{1.1}$-$Zr_{0.9}Ti_{0.1}Cr_{0.6}Fe_{1.4}$ which had very good hydrogenation properties. The power changed with operating parameter such as cycle time, air flow rate, and temperature of hot air was investigated. The power shows maximum value with cycle time. The power increased with air flow rate and temperature of hot air. The power of the heat pump was $65-72 Kcal/Kg-alloy{\cdot}h$ under optimum operating condition, which was superior to that the system using $LaNi_{0.9}Al_{0.3}-MmNi_{4.15}Al_{0.66}Fe_{0.2}$ alloy pairs.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.7
• /
• pp.1631-1633
• /
• 2009