• Journal of Sensor Science and Technology
• /
• v.18 no.1
• /
• pp.48-53
• /
• 2009

$Eu^{2+}$-doped ${SrAl_2}{O_4}$ and $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors have been synthesized by conventional solid state method. Photocurrent properties of $Eu^{2+}$ doped ${SrAl_2}{O_4}$ and $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors, in order to elucidate $Dy^{3+}$ co-doping effect, during and after ceasing ultraviolet-ray (UV) irradiation have been investigated. The photocurrent of $Eu^{2+}$, $Dy^{3+}$ co-doped ${SrAl_2}{O_4}$ phosphors during UV irradiation was 4-times lower than that of $Eu^{2+}$-doped ${SrAl_2}{O_4}$ during UV irradiation, and 7-times higher than that of $Eu^{2+}$-doped ${SrAl_2}{O_4}$ after ceasing UV irradiation. The photocurrent results indicated that holes of charge carriers captured in hole trapping center during the UV irradiation and liberated after-glow process, and made clear that $Dy^{3+}$ of co-dopant acted as a hole trap. The photocurrent of ${SrAl_2}{O_4}$ showed a good proportional relationship to UV intensity in the range of $1{\sim}5mW/cm^2$, and $Eu^{2+}$-doped ${SrAl_2}{O_4}$ was confirmed to be a possible UV sensor.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.3
• /
• pp.493-497
• /
• 1998

The synthesis of $Sr_{1-x}Eu_xAl_2O_4$ (x=0.005~0.2;mol%) phosphors and its properties of both photoluminescence and long-phosphorescent were investigated as a function of $Eu_2O_3$ composition. The peak wavelengths (520 nm) of phosphorescence spectra were found not to vary with the $Eu_2O_3$ composition (x) of $Sr_{1-x}Eu_xAl_2O_4$ crystals. Single phase of $SrAl_2O_4$ which determined by XRD and PL was obtained with the compositions of x<0.05 mol%. After the removal of light excitation (360 nm), the excellent after-glow characteristics of the phosphorescence were obtained with the $Eu_2O_3$ compositions of x<0.05 mol%, although the after-glow intensities for all phosphors vary exponentially with the times.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.6
• /
• pp.225-228
• /
• 2005

We have grown the long persistent $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ phosphor single crystal by Verneuil method. The obtained single crystals were long persistent phosphorescence peaking at ${\lambda}=520nm$ with a size of about 5 mm diameter, 55 mm length. The melting temperature of $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ measured $T_{mp}=1968^{\circ}C$. The optimum composition was $SrCO_3:Al(OH)_3:Eu_2O_3:Dy_2O_3$ = 1 : 2 : 0.015 : 0.02. Flow rate of $H_2:O_2$ is about 4 : 1. Growthing rate is about 5 mm/hr. The spectra of the phosphorescence from the crystals are quite similar to those obtained with sintered powders used for luminous pigments. The crystalline structure of long persistent $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ phosphor single crystal was determined by X-ray diffraction.

• Korean Journal of Materials Research
• /
• v.17 no.11
• /
• pp.612-617
• /
• 2007

Both photoluminescence and thermal characteristics for $SrAl_2O_4:Eu^{+2},\;Dy^{+3}$ phosphors synthesized with various aluminum compounds (${\alpha}-Al_2O_3$, ${\gamma}-Al_2O_3$, amorphous-$Al_2O_3$ and $Al(OH)_3)$ were investigated in this study. The formation temperature of the host $SrAl_2O_4$ crystal is changed by these various aluminum compounds, as a result of the different thermal decomposition temperature of $SrCO_3$ phase. Among these compounds, the amorphous-$Al_2O_3$ phase shows the lowest formation temperature of the host $SrAl_2O_4$ crystal. The PL emission and excitation spectra of $SrAl_2O_4:Eu^{+2},\;Dy^{+3}$ phosphor are not affected by these aluminum compounds. After the removal of the Xenon lamp excitation (360 nm), however, the excellent longphosphorescent property of the phosphor is obtained by the amorphous-$Al_2O_3$ phase, although the decay time for all phosphors decrease exponentially.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.5
• /
• pp.193-200
• /
• 2016

Characteristics of $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ phosphorescent phosphors synthesized by solid state reaction and polymerized complex method were comparatively analyzed. In order to evaluate thermal stability of $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ phosphorescent phosphors at high temperature, phosphorescent properties of $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ were investigated with thermal treatment at $1250^{\circ}C$ under reducing atmosphere, which was the general heat treatment conditions for ceramic manufacturing process. The phosphorescent properties of thermally treated $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ phosphors synthesized by solid state reaction and polymerized complex method were investigated. The crystal structure and crystallite size were observed through XRD analysis. Microstructure and particle size of thermally treated $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ phosphors were analyzed by SEM and PSA. Photoluminescence and afterglow characteristics of thermally treated $SrAl_2O_4:Eu^{2+}$, $Dy^{3+}$ phosphorescent phosphors were measured by spectrofluorometer.

• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.364-369
• /
• 2010

A $SrAl_2O_4:Eu^{2+},Dy^{3+}$ phosphor powder with stuffed tridymite structure was synthesized by glycine-nitrate combustion method. The luminescence, formation process and microstructure of the phosphor powder were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence spectroscopy (PL). The XRD patterns show that the as-synthesized $SrAl_2O_4:Eu^{2+},Dy^{3+}$ phosphor was an amorphous phase. However, a crystalline $SrAl_2O_4 $ phase was formed by calcining at $1200^{\circ}C$ for 4h. From the SEM analysis, also, it was found that the as-synthesized $SrAl_2O_4:Eu^{2+},Dy^{3+}$ phosphor was in irregular porous particles of about 50 ${\mu}m$, while the calcined phosphor was aggregated in spherical particles with radius of about 0.5 ${\mu}m$. The emission spectrum of as-synthesized $SrAl_2O_4:Eu^{2+},Dy^{3+}$ phosphor did not appear, due to the amorphous phase. However, the emission spectrum of the calcined phosphor was observed at 520 nm (2.384eV); it showed green emission peaking, in the range of 450~650 nm. The excitation spectrum of the $SrAl_2O_4:Eu^{2+},Dy^{3+}$ phosphor exhibits a maximum peak intensity at 360 nm (3.44eV) in the range of 250~480 nm. After the removal of the pulse Xe-lamp excitation (360 nm), also, the decay time for the emission spectrum was very slow, which shows the excellent longphosphorescent property of the phosphor, although the decay time decreased exponentially.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.999-1004
• /
• 1998

$SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 축광성 형광체의 합성에 있어서 $B_2O_3$는 일반적으로 고상반응의 촉진을 위한 플럭스로서 첨가된다. 본 연구에서는 플럭스로 첨가되는 $B_2O_3$가 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 형광체의 결정구조 및 잔광 특성에 미치는 영향을 조사하였다. 합성된 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 형광체는 520nm에서 최대 피크를 갖는 폭넓은 발광 스펙트럼을 나타내었고, $B_2O_3$ 첨가량의 5wt%일 때 최대값을 나타내었다. $B_2O_3$의 첨가에 의해 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 결정 내부에는 균일 변형(uniform strain)이 발생하였고 이 결과로 결정격자의 a축과 c축의 길이 및 $\beta$각이 감소하여다. 그리고 $SrAl_2O_4$ 결정내부의 균일 변형은 $Eu^{2+}$이온의 여기과정에서 발생하는 정공(hole)의 포획 사이트인 음이온 결함(negative defect)을 다량 발생시키는 원인이 되고, 결과적으로 $SrAl_2O_4$:$Eu^{2+}, Dy^{3+}$ 결정의 잔광 특성을 향상시키는 것으로 생각되었다.

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.529-534
• /
• 2004

$Sr_{4}Al_{14}O_{25}$ was synthesized by solid state reaction with flux. $H_{3}BO_3$ was used to synthesize $SrO-Al_{2}O_{3}$ phosphor system as a flux. The effect of doping system such as Eu+Dy, Eu, and Ce on the luminescent properties of $Sr_{4}Al_{14}O_{25}$ was investigated. Both PL spectra of $Sr_{4}Al_{14}O_{25}$:Eu and $Sr_{4}Al_{14}O_{25}$:Eu+Dy excited at 390 nm showed greenish-blue emission at about 490 nm, while the emission wavelength was shifted to 400 nm by doping Ce. The reduction of $Eu^{3+}$ ions to $Eu^{2+}$ could be accomplished by the annealing process under $N_{2}^{+}$ vacuum atmosphere, and attributed to the emission at 490 nm. It is verified that $Sr_{4}Al_{14}O_{25}$:Eu phosphor is suitable for white LEDs became of a broad absorption band peaking at 390 nm.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.42-46
• /
• 2017

$SrAl_2O_4$ : $Eu^{2+}$,$Dy^{3+}$ phosphorescent phosphors were synthesized by skull melting method. The molar ratio of oxides in the phosphors synthesized by the skull melting technique was $SrCO_3$ : $Al(OH)_3$ : $Eu_2O_3$ : $Dy_2O_3$= 1 : 2 : 0.015 : 0.02. Crystal structure and surface morphology were investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. Optical properties of the synthesized $SrAl_2O_4$ : $Eu^{2+}$,$Dy^{3+}$ were measured by photoluminescence (PL) spectrometer for in-depth study on the excitation, emission and afterglow properties. From the PL measurements, it was found that excitation occurred in the wavelength range from 300 to 420 nm with peak position at 360 nm. The emission spectrum showed a broad curve in the wavelength from 450 to 600 nm with peak position at 530 nm. $SrAl_2O_4$ : $Eu^{2+}$,$Dy^{3+}$ phosphors exhibited afterglow properties with emission that lasted for a long period.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.8
• /
• pp.671-679
• /
• 2007

[ $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ ] phosphor was synthesized using the impregnation method, and its photoluminescence and long-afterglow properties were investigated, A mixture of $Sr(NO_3)_2,\;Al(NO_3)_2\;9H_2O,\;EuCl_3\;6H_2O,\;DyCl_3\;6H_2O,\;NdCl_3\;6H_2O$ salts were dissolved in distilled water and impregnating into the polymer precursor. After drying, the impregnated mixture was heat treated at $900-1400^{\circ}C$ for 2h in a $N_2-H_2$ reduction atmosphere. The microstructure and crystal structure of the $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ powders were examined by scanning electron microscopy and X-ray diffraction, respectively. The photoluminescence spectra showed an excitation band along over wide wavelength of 250-450nm, and a broaden emission with a maxima peak at 360nm. In addition, the spectra also showed a good long after glow that decayed over a 1000sec period after 10 min excitation illumination.