• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.516-524
• /
• 1995

In this study, to prepare the dielectric (Ba, Sr)TiO3 thin films by the sol-gel process, Titaminum (IV) sio-propoxide (Ti[OCH(CH3)2]4), Ba and Sr acetate were used for sol and thin films were prepared by dip-coating process. Stability of sol decreased with the increase of Sr, and thickness of thin films were obtained 0.13~0.17${\mu}{\textrm}{m}$ by 1 coating cycle. Transmittance of amorphous thin films heated at 500 and 55$0^{\circ}C$ was very good, and crystallization tendency of thin films according to heat-treatment temperature and crystallization characteristics of thin films heated at 11$0^{\circ}C$ for 3 hrs were analysed. As a result, good perovskite structure was obtained higher than 100$0^{\circ}C$, and tetragonality of thin film was decreased but pyrochlore was formed with increasing Sr. In case of addition to substitute 0.4mol% Sr for Ba, dielectric constant was 288 and loss factor (tan $\delta$) was 0.04.

• Electrical & Electronic Materials
• /
• v.10 no.6
• /
• pp.541-547
• /
• 1997

(Pb$_{1-x}$ La$_{x}$)Ti$_{1-x}$ $_4$O$_3$(x=0, 0.02, 0.04, 0.08) ceramic thin films were fabricated by Sol-Gel method. A stock solution of (Pb, La)TiO$_3$ with excess Pb 10 mol% was made and spin-coated on the Pt/Ti/SiO$_2$/Si substrate at 400rpm for 30 seconds. Coated specimens were dried on the hot-plate at 35$0^{\circ}C$ for 10 min and sintered at 500~75$0^{\circ}C$ for 1 hour. The dielectric constant, remanent polarization and coercive field of the PLT(6at.%) thin films sintered at $650^{\circ}C$ were 884, 13.95$\mu$C/$\textrm{cm}^2$ and 8.7kV/cm, respectively. Pyroelectric coefficient, figure of merit of pyroelectric current, voltage responsivity and detectivity of PLT(6at.%) thin films were 3.2$\times$10$^{-8}$ C/$\textrm{cm}^2$K, 1.02$\times$10$^{-8}$ C.cm/J, 2.9 $\times$10$^{-11}$ C.cm/J, 0.29$\times$10$^{-8}$ C.cm/J, respectively.ely.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.357-366
• /
• 1992

Residual organics were considered as impurity in Sol-Gel method. The purpose of this study was to find the conditions to contain as much residual organics as possible in silica gel prepared from TEOS(tetraethylortho-silicate) by Sol-Gel method. Residual organics are to be expected to have reduction effect on synthesizing Si3N4 from silica gel. The results of this study are follows: 1) The maximum content of entrapped carbon was 19.8 wt.%(C/SiO2=0.25 wt.ratio) in silica gel synthesized under the conditions 1.5 fold mole water for incomplete hydrolysis, 2.5 fold mole phenol as a solvent and 0.1 fold mole HCl as a catalyst to TEOS. 2) Silica gel with organics entrapped by Sol-Gel method had a positive effect on the formation of Si3N4 compared with commercial silica gel. 3) Sintered body of synthesized $\alpha$-Si3N4 with Y2O3 and Al2O3 as additives at 175$0^{\circ}C$ in N2 atmosphere showed bending strength, 602$\pm$20 MPa and frature toughness 4.45$\pm$0.15 MPa.m1/2.

• Journal of the Korean Ceramic Society
• /
• v.31 no.8
• /
• pp.911-919
• /
• 1994

As the study for preparation of single-layer anti-reflective coating on glass, the conditions of synthesis of sol for coating and of reproducible coating procedure were investigated. In case of water-based sol, coating was impossible because of poor wettability of sol. The Substitution of solvent with ethanol improved the wettability of sol on the glass surface, and optimum amount of ethanol for substitution was 70 vol%. Maximum specific surface area and total pore volume of water-based sol were 268.7$m^2$/g and 0.315 cc/g, but after substitution, those values increased to 404.1 $m^2$/g and 0.376 cc/g, respectively. The upper limit withdrawl speed of coating in order to get clean coated films without aggregations or stains was 7 cm/min. In case of addition of 0.1 mol HNO3 and substitution with 70 vol% ethanol and heat-treatment at 40$0^{\circ}C$ for 1 hour, thin film with thickness of 94 nm was obtained at withdrawl speed of 4 cm/min. The thickness of thin film was independent of drying time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.94-98
• /
• 2000

Polycrystalline SBTN ferroelectric thin films were prepared by sol-gel method with various Nb mole ratios on Pt/ $SiO_2$/Si (100) substrates. The films were annealed at different temperatures and characterized in terms of phase and microstructure. Relatively a well saturated hysteresis pattern was obtained at x =0.2 in S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin films. At an applied voltage of 5V, the dielectric constant ($\varepsilon$$_{r}$) and dissipation factor (tan $\delta$) of typical S $r_{0.8}$B $i_{2.3}$(T $a_{1-x}$ N $b_{x}$)$_2$ $O_{9+}$$\alpha$/ thin film (x=0.2) were about 236.2 and 0.034. Measured remanent polarization (2Pr) and coercive field (Ec) were 4.28C/c $m_2$, and 38.88kv/cm respectively. No fatigue was observed up to 6$\times$10$_{10}$ switching cycles at 5V and the normalized polarization reduced by a factor of only 4%.%. 4%.%. 4%.%.%.%.%.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.37-44
• /
• 1997

Barium ferrite thin films on the thermal oxidized Si substrate were prepared by using sol-gel method (dip coating) from the sol of composition ratio of 5.25, designated by mole ratio 2Fe/Ba. The gelation process was largely divided into 4 step, and the sol prepared by reaction for 90 minutes at 8$0^{\circ}C$ was the suit-able for coating. Needle shaped particles formed on the coating layer were placed parallel to substrate and the inclination was increased with film thickness. The easy-direction of magnetization of needle shaped par-ticles was long-axis direction.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1079-1088
• /
• 1996

Discontinuous ${\gamma}$-LiAlO2 fibers for fiber-reinforcing MCFC matrixes have been produced by the sol-gel process using the centrifugal spinning apparatus of the Rotary type. Gel fibers could be obtained through spinning of stable LiAlO2 complex polymetric sols under the optimum spinning conditions (hollow-disc rotating velocity 9000 rpm sol feeding rate of 4ml/min flowing N2 temperature of 4$0^{\circ}C$ and flowing N2 pressure of 4 bar). It was found that defect free and densified ${\gamma}$-LiAlO2 fibers with the relative density of 98% and the mean diameter of 4.7${\mu}{\textrm}{m}$ were prepared when the spinned fibers were heat-treated to 100$0^{\circ}C$ on the specified heating schedule. in particular the mean diameter and length of fibers could be controlled by the pressure of flowing N2 and the chopping-sieving method respectively.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.391-402
• /
• 1999

Characteristics of composite electrolytes which were prepared by coating a thin film of YSZ (yttria sta-bilized zirconia : (ZrO2)0.92 (Y2O3)0.08) on YDC (yttria doped ceria : Ce0.8Y0.2O1.9) with mixed conductivity have been investigated in order to develop the low-temperature solid oxide fuel cell. The thickness (t) of spin-coated YSZ thin films after the heat-treatment at 600$^{\circ}C$ was increased proportionally to the sol con-centrations (C) while the decrease in its thickness with the spin rate ($\omega$) could be expressed in the e-quation of ln t=9.49-0.53 ln $\omega$(0.99mol//s sol conc.) When the sol concentration and the spin rate being less than 0.99 mol/l and higher than 1000 rpm respectively reliable YSZ/YDC composite electrolytes could be obtained by multi-coating although several micro-cracks were observed in singly coated YSZ film surfaces. The dense YSZ film with a 1$\mu\textrm{m}$ thickness was prepared by coating of 0.99 mol/l YSZ sol five-times at 2000 rpm followed by heat-treatment at 1400$^{\circ}C$ for 2h, The adhesion between YSZ film and YDC substrate was found to be very good. The open circuit voltages of H2/O2 single cell with YSZ/YDC composite electrolytes were 0.79∼0.82 V at 800$^{\circ}C$ and 0.75∼0.77V at 900$^{\circ}C$ The open circuit voltage was inversely proportioned to the thickness ratio of YSZ thin film (1$\mu\textrm{m}$) to YDC substrate(0.28-2.22 mm)

• Proceedings of the Korean Magnestics Society Conference
• /
• 2001.04a
• /
• pp.154-155
• /
• 2001

• Journal of the Korean Ceramic Society
• /
• v.36 no.9
• /
• pp.893-900
• /
• 1999

Silica films were prepared on Si single crystal substrates by sol-gel process using TEOS as starting materials. Films were fabricated by a spin coating technique. Sol solutions were prepared by varying the compositions of CH3OH, H2O and DMF with fixed molar ratio of TEOS=1, HCl=0.05(mol). Wetting behavior viscosity of solutions gelation time thickness of films and cracking behavior were investigated with the various solution compositions. Wetting behaviors of solutions depended on the solution compositions mixing method and mixing rate. The optimum composition of sol was TEOS : DMF ; CH3OH: H2O :HCl=1:2:4:4:0.05(mol) and the mixing rate of solution was optimized at 1 ml/min. Viscosity of solutions were controlled by choosing a reaction time(elapsed time after mixing) at a room temperature so that we could get up to 800nm thick film The surface roughness was getting poor when thickness of films was thicker than 500nm. Thickness of coated films were increased with decreasing amount of CH3OH. The best surface roughness was obtained at the content of CH3OH 4 mol. The shortest gelation time was obtained with the content of CH3OH 8 mol. Crack-free filkms were fabricated when sintered at 500$^{\circ}C$ for 1 hr with heating rate of 0.6$^{\circ}C$/min.