• Current Photovoltaic Research
• /
• 제3권2호
• /
• pp.54-60
• /
• 2015

ZnSnO thin films were deposited by atomic layer deposition (ALD) process using diethyl zinc ($Zn(C_2H_5)_2$) and tetrakis (dimethylamino) tin ($Sn(C_2H_6N)_4$) as metal precursors and water vapor as a reactant. ALD process has several advantages over other deposition methods such as precise thickness control, good conformality, and good uniformity for large area. The composition of ZnSnO thin films was controlled by varying the ratio of ZnO and $SnO_2$ ALD cycles. The ALD ZnSnO film was an amorphous state. The band gap of ZnSnO thin films increased as the Sn content increased. The CIGS solar cell using ZnSnO buffer layer showed about 18% energy conversion efficiency. With such a high efficiency with the ALD ZnSnO buffer and no light soaking effect, AlD ZnSnO buffer mighty be a good candidate to replace Zn(S,O) buffer in CIGSsolar cells.

• 공업화학
• /
• 제5권2호
• /
• pp.327-336
• /
• 1994

본 연구는 아크롤레인의 선택산화반응에서 Mo-V-O와 금속산화물의 기계적 혼합촉매에 대한 synergy 효과를 고찰한 것으로 금속산화물로는 $SnO_2$, ${\alpha}-Sb_2O_4$, $WO_3$, ${\alpha}-Al_2O_3$, CuO, $MnO_2$, $Cu_2O$, MgO, CoO 그리고 ZnO 등을 사용하였다. $SnO_2$나 ${\alpha}-Sb_2O_4$와 Mo-V-O의 혼합물 촉매는 Mo-V-O보다 높은 전화율과 수율을 나타내었는데 이것은 이들이 산소 빈자리에 해리 홉착된 산소를 형성하여 Mo-V-O에 전달하는 상간협동에 의한 것으로 판단된다 그러나 $Cu_2O$, MgO, CuO, $MnO_2$와 Mo-V-O의 혼합물 촉매의 경우 전화율은 증가하였으나 수율은 감소하였고, CoO와 ZnO는 Mo-V-O의 촉매성능을 억제하였다. 각 금속산화물의 역할이 서로 다른 점을 그들의 산화-환원 특성으로 설명하였다.

• 소성∙가공
• /
• 제7권5호
• /
• pp.481-488
• /
• 1998

The active metal brazing was applied to bond Alumina and Ni-Cr steel by Ag-Cu-Zr-Sn alloy and the interfacial microstructure and reaction mechanism were investigated. Polycrystalline monoclinic $ZrO_2$ with a very fine grain of 100-150 nm formed at the alumina grain boundary contacted with Zr segregation layer at the interface. The $ZrO_2$ layer containing the inclusions and cracks were developed at the boundary of inclusion/$ZrO_2$ due to the difference in specific volume. The development of $ZrO_2$ at the interface was successfully explained by the preferential penetration of $ZrO_2$ at the interface was successfully explained by the preferential penetration of Zr atoms a higher concentration of oxygen and a high diffusion rate of Al ions into molten brazing alloy.

• 한국초전도ㆍ저온공학회논문지
• /
• 제16권2호
• /
• pp.33-35
• /
• 2014

We report here results of a study of superconductivity in the ($Ta_{1-x} Sn_x)Sr_2EuCu_2O_z$ system. We observe resistive superconducting transitions for the samples with x = 0.15-0.3, and the highest superconducting transition has been achieved for the sample with x = 0.2 which reveals onset $T_c$ of 43 K and zero-resistivity of 25 K. Thermoelectric power measurements indicate that Sn doping introduces holes into the system and thereby superconductivity can be achieved in the ($Ta_{1-x} Sn_x)Sr_2EuCu_2O_z$ system.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.181.2-181.2
• /
• 2016

OLED 소자는 발광 방향에 따라 Bottom Emission 방식과 Top Emission 방식으로 나뉜다. 이 중 대면적 OLED TV 적용에 개구율이 더 높은 Top Emission방식을 선호하는 추세이다. 높은 개구율을 가진 Top Emission OLED소자를 위해서는 투명하고 전도성이 높은 캐소드가 중요하다. 본 연구에서는 Themal Evaporation 시스템을 이용하여 증착한 $SnO_2/Ag-Pd-Cu(APC)/SnO_2$ hybrid 전극의 특성을 연구하고 Oxide/Metal/Oxide(OMO) hybrid 박막의 bending mechanism을 제시하였다. base pressure는 $1{\times}10^{-6}Torr$로 고정하고 $SnO_2$ 박막은 0.34A / 0.32V, APC 박막은 0.46A / 0.40V의 power로 성막하였다. APC와 $SnO_2$의 두께를 변수로 OMO 전극을 제작하였고 그 전기적, 광학적 특성을 Hall measurement, UV/Visible spectroscopy을 이용하여 분석하고 Figure of merit 값을 바탕으로 최적 두께를 설정하였다. UPS(Ultraviolet Photoelectron Spectroscopy) 분석으로 $SnO_2/APC/SnO_2$ 전극의 일함수을 통해 투명 cathode로 쓰였을 때 $SnO_2$ 층이 buffer layer역할을 함을 확인하였다. XPS(X-ray photoelectron spectroscopy)를 이용하여 정성분석과 정량분석을 하였고 OMO hybrid 전극의 bending mechanism 연구를 위해 다양한 bending test (Inner/Outer dynamic fatigue test, twisting test, rolling test)를 진행하였다. 물리적 힘이 가해진 OMO hybrid 전극의 표면과 구조는 FE-SEM(Field Emission Scanning Electron Microscope) 분석을 통해서 확인할 수 있었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.99-99
• /
• 2014

Transparent oxide semiconductors (TOSs) are. currently attracting attention for application to transparent electrodes in optoelectronic devices and active channel layers in thin-film transistors. One of the key issues for the realization of next generation transparent electronic devices such as transparent complementary metal-oxide-semiconductor thin-film transistors (CMOS TFTs), transparent wall light, sensors, and transparent solar cell is to develop p-type TOSs. In this talks, I will introduce issues and status related to p-type TOSs such as LnCuOQ (Ln=lanthanide, Q=S, Se), $SrCu_2O_2$, $CuMO_2$ (M=Al, Ga, Cr, In), ZnO, $Cu_2O$ and SnO. The growth and properties of SnO and Cu-based oxides and their application to electronic devices will be discussed.

• 한국재료학회지
• /
• 제29권1호
• /
• pp.1-6
• /
• 2019

Recent industrialization has led to a high demand for the use of fossil fuels. Therefore, the need for producing hydrogen and its utilization is essential for a sustainable society. For an eco-friendly future technology, photoelectrochemical water splitting using solar energy has proven promising amongst many other candidates. With this technique, semiconductors can be used as photocatalysts to generate electrons by light absorption, resulting in the reduction of hydrogen ions. The photocatalysts must be chemically stable, economically inexpensive and be able to utilize a wide range of light. From this perspective, cuprous oxide($Cu_2O$) is a promising p-type semiconductor because of its appropriate band gap. However, a major hindrance to the use of $Cu_2O$ is its instability at the potential in which hydrogen ion is reduced. In this study, gold is used as a bottom electrode during electrodeposition to obtain a preferential growth along the (111) plane of $Cu_2O$ while imperfections of the $Cu_2O$ thin films are removed. This study investigates the photoelectrochemical properties of $Cu_2O$. However, severe photo-induced corrosion impedes the use of $Cu_2O$ as a photoelectrode. Two candidates, $TiO_2$ and $SnO_2$, are selected for the passivation layer on $Cu_2O$ by by considering the Pourbaix-diagram. $TiO_2$ and $SnO_2$ passivation layers are deposited by atomic layer deposition(ALD) and a sputtering process, respectively. The investigation of the photoelectrochemical properties confirmed that $SnO_2$ is a good passivation layer for $Cu_2O$.

• 제어로봇시스템학회논문지
• /
• 제13권7호
• /
• pp.616-623
• /
• 2007

A dual micro gas sensor array was fabricated using nano sized $SnO_2$ thin films which had good sensitivities to CO and combustible gases, or $H_2S$ gas for air quality sensors in automobile. The already existed air quality sensor detects oxidizing gases and reducing gases, the air quality sensor(AQS), located near the fresh air inlet detected the harmful gases, the fresh air inlet door/ventilation flap was closed to reduce the amount of pollution entering the vehicle cabin through HVAC(heating, ventilating, and air conditioning) system. In this study, to make $SnO_2$ thin film AQS sensor, thin tin metal layer between 1000 and $2000{\AA}$ thick was oxidized between 600 and $800^{\circ}C$ by thermal oxidation. The gas sensing layers such as $SnO_2$, $SnO_2$(pt) and $SnO_2$(+CuO) were patterned by metal shadow mask for simple fabrication process on the silicon substrate. The micro gas sensors with $SnO_2$(+Pt) and $SnO_2$(CuO) showed good selectivity to CO gas among reducing gases and good sensitivity to $H_2S$ that is main component of bad odor, separately.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.563-566
• /
• 2000

The effect of CuO and CuO-B $i_2$ $O_3$ additives on microwave dielectric properties of (P $b_{0.45}$C $a_{0.55}$)[F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$were investigated to decrease the sintering temperature for usage of Low Temperature Co-firing Ceramics (LTCC). The (P $b_{0.45}$C $a_{0.55}$)[F $e_{0.5}$N $b_{0.5}$)$_{0.9}$S $n_{0.1}$] $O_3$ceramics was sintered at 11$65^{\circ}C$. In order to decrease the sintering temperature, CuO and Cuo-B $i_2$ $O_3$ were added in the (Pb,Ca)[(Fe,Nb)Sn] $O_3$ with CuO-B $i_2$ $O_3$. For the addition of 0.4 wt.% CuO, the sintered density and the dielectric constant of the ceramics were revealed the maximum values of the 6.06g/c $m^2$ and 83 respectively and temperature coefficient of resonance frequency ($\tau$$_{f}$) shifted to the positive value. As increasing B $i_2$ $O_3$to the (Pb,Ca)[(Fe,Nb)Sn] $O_3$ with CuO-B $i_2$ $O_3$with 0.2 wt.% CuO, the sintered density, the $\varepsilon$$_{r}$ and the Q was decreased, and $\tau$$_{f}$ was minimized at 0.2 wt.% CuO, and 0.2 wt.% B $i_2$ $O_3$. For this composition, dielectric properties were $\varepsilon$$_{r}$ of 81, Q. $f_{0}$ of 4400 GHz, and $\tau$$_{f}$ of 5 ppm/$^{\circ}C$ at sintering temperature of 100$0^{\circ}C$. the relationship between the microstructure and properties of ceramics was studied by X-ray diffraction(XRD), scanning electron microscopy(SEM).copy(SEM).oscopy(SEM).copy(SEM).EM).

• 한국분말재료학회지
• /
• 제31권2호
• /
• pp.146-151
• /
• 2024

Pure SnO₂ has proven very difficult to densify. This poor densification can be useful for the fabrication of SnO₂ with a porous microstructure, which is used in electronic devices such as gas sensors. Most electronic devices based on SnO₂ have a porous microstructure, with a porosity of > 40%. In pure SnO₂, a high sintering temperature of approximately 1300℃ is required to obtain > 40% porosity. In an attempt to reduce the required sintering temperature, the present study investigated the low-temperature sinterability of a current system. With the addition of TiO₂, the compositions of the samples were Sn_1-xTi_xO₂-CoO(0.3wt%)-CuO(2wt%) in the range of x ≤ 0.04. Compared to the samples without added TiO₂, densification was shown to be improved when the samples were sintered at 950℃. The dominant mass transport mechanism appears to be grain-boundary diffusion during heat treatment at 950℃.