• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1352-1354
• /
• 1998

$LiNbO_3$ transistor showed relatively stable characteristic, low interface trap density, and large remanent polarization. This paper reports ferroelectric $LiNbO_3$ thin films grown directly on p-type Si(100) substrates by 13.56 MHz rf magnetron sputtering system for FRAM applications. To take advantage of low temperature requirement for growing films, we deposited $LiNbO_3$ films lower than $300 ^{\circ}C$. RTA(Rapid Thermal Anneal) treatment was performed for as-deposited films in an oxygen atmosphere at $600^{\circ}C$ for 60 sec. We learned from X-ray diffraction that the RTA annealed films were changed from amorphous to poly-crystalline $LiNbO_3$ which exhibited (012), (015), and (022) orientations. The I-V characteristics of $LiNbO_3$ films before and after anneal treatment showed that RTA improved the leakage current of films. The leakage current density of films decreased from $10^{-5}$ to $10^{-7} A/cm^2$ at room temperature measurement. Breakdown electric field of the films exhibited higher than 500 kV/cm. The C-V curves showed the clockwise hysteresis represents ferroelectric switching characteristics. From C-V curves, we calculated dielectric constant of thin film $LiNbO_3$ as 27.5 which is close to that of bulk value.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.264-265
• /
• 2009

본 연구에서 유도결합 플라즈마 식각 장치외 $BCl_3/Ar/Cl_2$ 가스 혼합비를 이용하여 ZnO 박막을 식각 하였을 때, 식각 된 ZnO 박막의 표면 반응에 관하여 관찰하였다. ZnO 박막의 식각 실험 조건은 RF 전력 700 W, 직류바이어스 전압 - 150 V, 공정 압력 15 mTorr로 고정하였고, $Cl_2/(Cl_2+BCl_3+Ar)$ 가스 혼합비를 변경하면서 식각 실험을 수행하였다. $Cl_2$ 가스가 3 sccm 일 때, ZnO 박막의 식각속도는 53 nm/min으로 가장 높았으며, 이때 ZnO 박막에 대한 $SiO_2$의 선택비는 0.89 이었다. 식각된 ZnO 박막의 표면은 XRD (X-ray diffraction)와 AFM(atomic force microscopy)를 이용하여 결정상의 변화와 표면의 거칠기를 분석하였다. AFM 분석 결과에서 Ar, $BCl_3$와 $Cl_2$ 플라즈마를 이용하여 식각된 시료의 표면 거칠기 근 값이 식각전의 시료나 $BCl_3/Ar/Cl_2$ 플라즈마로 식각된 시료보다 큰 것을 확인하였다. 이는 식각된 시료에서의 Zn 양의 감소나 비휘발성 식각 잔류물에 의한 영향으로 판단된다. SIMS(secondary ion mass spectrometery) 분석을 통해 검증 하였다.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.1
• /
• pp.49-53
• /
• 2011

Diamond-like carbon (DLC) films is a metastable form of amorphous carbon containing a significant fraction of Sp3 bond. DLC films have been characterized by a range of attractive mechanical, chemical, tribological, as well as optical and electrical properties. In this study DLC films were prepared by the RF magnetron sputter system on $SiO_2$ substrates using graphite target. The effects of the post annealing temperature on the Property variation of the DLC films were examined. The DLC films were annealed at temperatures ranging from 300 to $500^{\circ}C$ using rapid thermal process equipment in vacuum. The variation of electrical property and surface morphology as a function of annealing treatment was investigated by using a Hall Effect measurement and atomic force microscopy. Raman and X-ray photoelectron spectroscopy analyses revealed a structural change in the DLC films.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.2
• /
• pp.494-500
• /
• 2014

Indium-doped zinc oxide nanocrystals (IZO NCs), capped with stearic acid (SA) of different sizes, were synthesized using a hot injection method in a noncoordinating solvent 1-octadecene (ODE). The ligand exchange process was employed to modify the surface of IZO NCs by replacing the longer-chain ligand of stearic acid with the shorter-chain ligand of butylamine (BA). It should be noted that the ligand-exchange percentage was observed to be 75%. The change of particle size, morphology, and crystal structures were obtained using a field emission scanning electron microscope (FE-SEM) and X-ray diffraction pattern results. In our study, the 5 nm and 10 nm IZO NCs capped with stearic acid (SA-IZO) were ligand-exchanged with butylamine (BA), and were then spin-coated on a thermal oxide ($SiO_2$) gate insulator to fabricate a thin film transistor (TFT) device. The films were then annealed at various temperatures: $350^{\circ}C$, $400^{\circ}C$, $500^{\circ}C$, and $600^{\circ}C$. All samples showed semiconducting behavior and exhibited n-channel TFT. Curing temperature dependent on mobility was observed. Interestingly, mobility decreases with the increasing size of NCs from 5 to 10 nm. Miller-Abrahams hopping formalism was employed to explain the hopping mechanism insight our IZO NC films. By focusing on the effect of size, different curing temperatures, electron coupling, tunneling rate, and inter-NC separation, we found that the decrease in electron mobility for larger NCs was due to smaller electronic coupling.

• Korean Journal of Materials Research
• /
• v.22 no.8
• /
• pp.409-415
• /
• 2012

$TiO_2$ thin films for high energy density capacitors were prepared by r.f. magnetron sputtering at room temperature. Flexible PET (Polyethylene terephtalate) substrate was used to maintain the structure of the commercial film capacitors. The effects of deposition pressure on the crystallization and electrical properties of $TiO_2$ films were investigated. The crystal structure of $TiO_2$ films deposited on PET substrate at room temperature was unrelated to deposition pressure and showed an amorphous structure unlike that of films on Si substrate. The grain size and surface roughness of films decreased with increasing deposition pressure due to the difference of mean free path. X-ray photoelectron spectroscopy (XPS) analysis revealed the formation of chemically stable $TiO_2$ films. The dielectric constant of $TiO_2$ films was significantly changed with deposition pressure. $TiO_2$ films deposited at low pressure showed high dissipation factor due to the surface microstructure. The dielectric constant and dissipation factor of films deposited at 70 mTorr were found to be 100~120 and 0.83 at 1 kHz, respectively. The temperature dependence of the capacitance of $TiO_2$ films showed the properties of class I ceramic capacitors. $TiO_2$ films deposited at 10~30 mTorr showed dielectric breakdown at applied voltage of 7 V. However, the films of 500~300 nm thickness deposited at 50 and 70 mTorr showed a leakage current of ${\sim}10^{-8}{\sim}10^{-9}$ A at 100 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.74-77
• /
• 2004

[ $HfO_2$ ] dielectric layers were grown on the p-type Si(100) substrate by metalorganic molecular beam epitaxy(MOMBE). Hafnium $t-butoxide[Hf(O{\cdot}t-C_4H_9)_4]$ was used as a Hf precursor and Argon gas was used as a carrier gas. The thickness of the layers was measured by scanning electron microscopy (SEM) and high-resolution transmission electron measurement(HR-TEM). The properties of the $HfO_2$ layers were evaluated by X-ray diffraction(XRD), high frequency capacitance-voltage measurement(HF C-V), current-voltage measurement(I-V), and atomic force measurement(AFM). HF C-V measurements have shown that $HfO_2$ layer grown by MOMBE has a high dielectric constant(k=19-21). The properties of $HfO_2$ films are affected by various process variables such as substrate temperature, bubbler temperature, Ar, and $O_2$ gas flows. In this paper, we examined the relationship between the $O_2/Ar$ gas ratio and the electrical properties of $HfO_2$.

• Journal of the Korean Magnetics Society
• /
• v.11 no.1
• /
• pp.21-25
• /
• 2001

$\alpha$-Fe$_2$O$_3$ thin films were prepared on Si substrate by a pulsed laser deposition system and characterized by X-ray and Mossbauer spectroscopy. The appropriate conditions of pulsation was the power of 5.128 W/cm2 at on oxygen pressure of 0.1 Torr at a substrate temperature of 30$0^{\circ}C$. After that the film was heated at 80$0^{\circ}C$ for 1 day. The particles shape deposited on the film was ellipsoidal and the average length and width were 200~300 nm, 70~150 am respectively. The crystal structure was conformed to be of corundums symmetry with the hexagonal unit cell having a lattice constant of u = 5.03$\pm$0.05 $\AA$, c = 13.735$\pm$0.05 $\AA$. The average angles between the atomic spin and the magnetic hyperfine field of Fe ion were 38$^{\circ}$and 48$^{\circ}$ at above and blow the Morin transition temperature respectively. The Morin transition was found to occur at the temperature ranges from 200 K to room temperature and atomic spin direction was assumed to change from 48$^{\circ}$ to 80$^{\circ}$in respect to the c-axis.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.400-400
• /
• 2012

산화물 반도체는 넓은 에너지갭을 가지고 높은 이동성과 높은 투명성을 가지기 때문에 초고 속 박막 트랜지스터(Thin film transistor; TFT)에 많이 응용되고 있다. 그러나 ZnO 및 $In_2O_3$ 산화물 반도체를 박막트랜지스터에 사용할 경우 소자가 불안정하여 전기적 성질이 저하되고 문턱전압의 이동이 일어난다. TFT에 사용되는 산화물 반도체로는 GaInZnO, ZrInZnO, HfInZnO 및 GaSnZnO의 전기적 특성에 관한 연구가 많이 되었다. 그러나 titanium-indium-zinc-oxide (TIZO) TFT에 대한 연구는 비교적 적게 수행 되었다. 본 연구에서는 TFTs의 안정성을 향상하기 위하여 TFT의 채널로 사용되는 TiInZnO를 형성하는데 간단한 제조 공정과 낮은 비용의 용액 증착방법을 사용하였다. 졸-겔 전해액은 Titanium (IV) isopropoxide $[Ti(OCH(CH_3)_2)_4]$, 0.1 M Zinc acetate dihydrate $[Zn(CH_3COO)_2{\cdot}2H_2O]$ 그리고 indium nitrate hydrate $[In(NO_3)_3{\cdot}xH_2O]$을 2-methoxyethanol의 용액에 합성하였다. $70^{\circ}C$에서 한 시간 동안 혼합 하였다. Ti의 몰 비율은 10%, 20% 및 40% 로 각각 달리하여 제작하였다. $SiO_2$층 위에 2,500 rpm 속도로 25초 동안 스핀 코팅하여 TFT를 제작하였다. TIZO 박막에 대한 X-선 광전자 스펙트럼 관측 결과는 Ti 몰 비율이 증가함에 따라 Ti 2p1/2피크의 세기가 증가함을 보여주었다. TiZO 박막에 Ti 원자를 첨가하면 $O^{2-}$ 이온이 감소하기 때문에 전하의 농도가 변화하였다. 전하 농도의 변화는 TiZO 채널을 사용하여 제작한 TFT의 문턱전압을 양 방향으로 이동 하였으며 off-전류를 감소하였다. TiZO 채널을 사용하여 제작한 TFT의 드레인 전류-게이트 전압 특성은 on/off비율이 $0.21{\times}107$ 만큼 크며 이것은 TFT 소자로서 우수한 성능을 보여주고 있다.

• Proceedings of the KIEE Conference
• /
• 2015.07a
• /
• pp.1151-1152
• /
• 2015

Silicon zinc oxide (SZO) thin films were deposited via co-sputtering. Two kinds of post-treatment, furnace annealing and hot pressing, were carried out on the deposited SZO films. The effects of the post-treatment on the chemical bond and surface roughness of the deposited SZO films were analyzed as functions of the post-treatment conditions that were used. It was observed from the X-ray photoelectron spectroscopy (XPS) results that the amount of Si-O bonds in the SZO film drastically increased after the low-temperature furnace annealing. The experiment results showed that the hot pressing method would be favorable as it could improve the electrical characteristics of the SZO-TFTs.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.2
• /
• pp.174-181
• /
• 2007

In this study, $SiO_2/poly(ethylene-co-vinyl$ alcohol)(EVOH) hybrid coating materials with gas barrier property could be produced using sol-gel method. The biaxially oriented polypropylene (BOPP) substrate with surface pretreatment was coated with the prepared hybrid sols containing various inorganic silicate component by a spin coating method. Crystallization behavior of the hybrids was investigated in terms of analysis of X-ray diffraction and cooling thermogram from DSC experiment. From the morphological observation of the $SiO_2/EVOH$ hybrid gel, it was confirmed that there existed an optimum content of inorganic silicate precursor, Tetraethylorthosilicate (TEOS), to produce hybrid materials with dense microstructure, exhibiting uniformly dispersed silica particles with average size below 100 nm. When TEOS was added at below or above the optimum content, particle clusters with large domain were observed, resulting in phase separation. This morphological result was found to be in good agreement with that of oxygen permeability of the hybrid coated films. In the case of film coated with hybrid prepared from addition of 0.01 - 0.02mol of TEOS, a remarkable improvement in barrier property could be obtained, however, with the addition of TEOS more than 0.04 mol, the barrier property was dramatically reduced because of phase separation and micro-crack formation on the film surface.