• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.271-278
• /
• 2006

Green light emitting $Zn_2SiO_4$Mn and Al co-doped $Zn_2SiO_4$:Mn phosphor were synthesized by a sol-gel method combined with a furnace firing. The luminescent properties of the sample have been investigated. We have found that the phosphor powder with uniform shape show the maximum luminescent intensity when it is prepared with sol-gel method and fired at relatively high temperature ($1100{\sim}1300^{\circ}C$).

• Bulletin of the Korean Chemical Society
• /
• v.19 no.11
• /
• pp.1185-1188
• /
• 1998

Layered nanocomposite, SiO2/TiO2 sol pillared clay, has been prepared by the ion exchange reaction of Na' ion in montmorillonite with positively charged mixed SiO2/TiO2 sol. The nanosized sol particles were synthesized by mixing SiO2 sol solution with TiO2 one, which is obtained by acidic hydrolysis of TEOS and TiCl4, respectively. From powder XRD, the basal spacing (d001) of the sample calcined at 400 ℃ was found to be ca. 60 Å, due to the multistacking of nanosized SiO2 and TiO2 sol particles, which was confirmed by the pore size analysis from 129Xe NMR and micropore analysis calculated from nitrogen adsorption. The BET specific surface area shows the value of 684 m2g-1 (Langmuir 1115 m2g-1), which is the highest among various pillared clays ever reported previously, and the total porosity is found to be 0.51 mlg-1, and the pores are mainly composed of micropore with a size of ca. 11.8 Å. This result agrees with the adsorption capacity obtained from water adsorption. According to diffuse reflectance ultraviolet-visible spectroscopy, it is found that the TiO2 particles stabilized in the interlayer space of montmorillonite are quantum-sized of ca. 20 Å.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.10a
• /
• pp.227.1-227
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.41 no.5
• /
• pp.349-352
• /
• 2004

Organic-inorganic hybrid sol based on ZrO$_2$-SiO$_2$ system was prepared by sol-gel process. Firstly, ZrO$_2$ non-aqueous precursor sol was synthesized and then organosilane compounds which include epoxy silane (GPTS; 3-g1ycidoxypropyl tri-methoxysilane) and acryl silane (ACS; (3-(tri-methoxysilyl)propylmethacrylate)) were added to ZrO$_2$precursor sol for hybridization. Finally, com-mercial silica sol was added to improve the mechanical properties. Synthesized organic-inorganic Zr-hybrid sol was coated on polycarbonate substrate for enhancing it’s mechanical properties, especially hardness. Vicker’s hardness of polycarbonate sub strate was increased from 13.6 to 17.8 MPa and its pencil hardness was increased from 2 to 7 H, respectively, after coating and drying at 10$0^{\circ}C$ for 30 min.

• Journal of the Korean Ceramic Society
• /
• v.30 no.9
• /
• pp.775-783
• /
• 1993

TiO2-SiO2 system anti-reflective(AR) film was prepared to decrease reflectance on the glass surface. The experiments were carried out as fellow, 1) preparation & hydrolysis of TiO2-SiO2 system sols. 2) glass dipping, and 3) drying & heat treatment. We investigated the refractive index and thickness of film with viscosity, zeta-potential of sol, sol concentration, withdrawal speed, drying and heat treatment condition. As a result, we prepared good qualitative Quarter-Half-Quarter type anti-reflective film that had minimum, 0.02% and average reflectance, 0.087% in the visible region.

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.2
• /
• pp.130-136
• /
• 2008

$xTiO_2$-$ySiO_2$ system photocatalysts were developed by sol-gel method based on the change of production parameters, and their structure of crystallization and the specific surface area were measured. Considering the efficiency of the ethanol and phenol degradation using the catalyst, the conclusions were obtained as follows: By means of X-ray analysis of $xTiO_2$-$ySiO_2$ powder that is obtained from Titanium and Silicon alkoxide by sol-gel process, it is shown that crystal structure of anatase type is a dominating structure and, on the other hand, the structure of rutile also partly exists. The increase of $SiO_2$ contents causes the decrease of the degree of crystallization of the gel, whereas the specific surface area preferentially increases. It is shown that more than 90% of ethanol and phenol are degraded when reaction time is about three and an hours, and the maximum degradation rate of ethanol and phenol is shown in $60TiO_2$-$40SiO_2$ catalyst.

• Journal of the Korean Ceramic Society
• /
• v.34 no.7
• /
• pp.774-780
• /
• 1997

Porous low reflective coating films of SiO2.ZrO2 system were prepared from the mixed alkoxide solutions of Zr(O-nC3H7)4 and partially prehydrolyzed TEOS by the sol-gel method using the dip-coating technique. In the case of 90SiO2.10ZrO2 porous coating films with HCl and H2O content was 0.3 mole and 4 mole, 378 m2/g of the specific surface area, 0.254 cm3/g of total pore volume, 30-50$\AA$ of average pore diameter. The transmittance of 90SiO2.10ZrO2 porous coated films was 95.38% at the wavelength of 550 nm, compared with the parent glass, the transmittance was increased with 4.38%.

• Journal of environmental and Sanitary engineering
• /
• v.13 no.3
• /
• pp.58-65
• /
• 1998

Monodispersed $SiO_2/ZnO$ composite fine powders were prepared by Sol-Gel processing and their surface electrical and UV absorbance properties were investigated. Pseudomorph ZnO fine powders were microcapsuled by $SiO_2/ZnO$ sol fabricated using TEOS[tetraethylorthosilicate, purity 98% and ethanol as a solvent with $NH_3$ catalyst. The effects of experimental parameters such as molar ratio of starting materials on the final particle size and shape of $SiO_2/ZnO$ composite fine powder were discussed. As a result, we could controlled the size of monodispersed $SiO_2/ZnO$ composite fine powders without agglomeration, as well as the good dispersibility in aquous solution. The prepared powders were observed to have the mean particle sizes of $0.26-0.78{\mu}m$ with standard deviations of $0.020-0.063{\mu}m$.

• Korean Journal of Materials Research
• /
• v.11 no.9
• /
• pp.740-744
• /
• 2001

The $Y_2SiO_5:Ce$ phosphors were synthesized by sol-gel technique in order to improve the performance of blue emitting phosphors for field emission display(FED). The resulted$Y_2SiO_5:Ce$ phosphors enhanced the emission intensity. In addition, calcination temperature of sol-gel technique(1300~140$0^{\circ}C$) was lower than that of the solid state reaction(>1$600^{\circ}C$). Under 365 nm and low voltage electron excitations. $Ce^{3+}$ -activated $Y_2SiO_5$phosphors showed blue emission band with a range of 400~ 430nm. Especially, 2mol% $Ce^{3+}$ doped $Y_2SiO_5:Ce$phosphors showed the maximum emission intensity. We have also controlled drying temperature of wet gel, pH, and $H_2O$/TEOS molar ratio for the optimum condition of TEOS hydrolysis.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.6
• /
• pp.277-281
• /
• 2009

Superhydrophobic $SiO_2$ thin films were successfully fabricated on a glass substrate by sol-gel method. To fabricate $SiO_2$ thin film with a high roughness, $SiO_2$ nano particles were added into tetraethoxysilane (TEOS) solution. The prepared $SiO_2$ thin film without an addition of $SiO_2$ nano particles showed a very flat surface with ca. 1.27 nm of root mean square (RMS) roughness. Otherwise, the $SiO_2$ thin films fabricated by using coating solutions added $SiO_2$ nano particles of 1.0, 2.0 and 3.0 wt% showed a RMS roughness of ca. 44.10 nm, ca. 69.58 nm, ca. 80.66 nm, respectively. To modify the surfaces of $SiO_2$ thin films to hydrophobic surface, a hydrophobic treatment was carried out using a fluoroalkyltrimethoxysilane (FAS). The $SiO_2$ thin films with a high rough surface were changed from hydrophilic to hydrophobic surface after the FAS treatment. Especially, the prepared $SiO_2$ thin film with a RMS roughness of 80.66 nm showed a water contact angle of $163^{\circ}$.