• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.799-805
• /
• 2001

Two commercial alumina powders having different particle size of $0.5{\mu}m$ and 3${\mu}$m were presintered at 1120$^{\circ}$C for 2h and then lanthanum aluminosilicate glass was infiltrated at 1100$^{\circ}$C for up to 4h to obtain the densified glass-alumina composites. The effect of alumina particle size on packing factor, microstructure, wetting, porosity and pore size, and mechanical properties of the composite was investigated. The optimum mechanical properties and compaction behavior were observed for the 3${\mu}$m alumina particle dispersed composite. The 3${\mu}$m alumina particle size and distribution for he preform were within 0.1 to 48${\mu}$m and bimodal and random orientation. The strength and the fracture toughness of the composite having 3${\mu}$m alumina particles were 519MPa and $4.5MPa{\cdot}m^{1/2}$, respectively.