• 한국세라믹학회지
• /
• 제41권5호
• /
• pp.349-352
• /
• 2004

Organic-inorganic hybrid sol based on ZrO$_2$-SiO$_2$ system was prepared by sol-gel process. Firstly, ZrO$_2$ non-aqueous precursor sol was synthesized and then organosilane compounds which include epoxy silane (GPTS; 3-g1ycidoxypropyl tri-methoxysilane) and acryl silane (ACS; (3-(tri-methoxysilyl)propylmethacrylate)) were added to ZrO$_2$precursor sol for hybridization. Finally, com-mercial silica sol was added to improve the mechanical properties. Synthesized organic-inorganic Zr-hybrid sol was coated on polycarbonate substrate for enhancing it’s mechanical properties, especially hardness. Vicker’s hardness of polycarbonate sub strate was increased from 13.6 to 17.8 MPa and its pencil hardness was increased from 2 to 7 H, respectively, after coating and drying at 10$0^{\circ}C$ for 30 min.

• Journal of the Optical Society of Korea
• /
• 제18권1호
• /
• pp.45-49
• /
• 2014

Well-crystallized $BaSi_2O_5:Eu^{2+}$ phosphor films were synthesized by heat treatment of spin-coated BaO:Eu on $SiO_2$ glass. We investigated luminescence-structure properties of these phosphor films as a function of heat-treatment temperature. From x-ray diffraction patterns, our $BaSi_2O_5:Eu^{2+}$ phosphor films revealed that (111)- and (204)-crystal planes of $BaSi_2O_5$ crystal were dominantly increased with an increase of heat-treatment temperature. Photoluminescence intensities of $BaSi_2O_5:Eu^{2+}$ phosphor films were increased with amount of these crystal planes. It can be explained that $Eu^{2+}$ ions were stably occupied at specific crystal orientation of $BaSi_2O_5$ crystal, enhancing the luminescent intensities of $BaSi_2O_5:Eu^{2+}$ phosphor films. In addition, our $BaSi_2O_5:Eu^{2+}$ phosphor films had transmittance of 70% at 510 nm,.due to the dense morphology and specific crystallinity of $BaSi_2O_5:Eu^{2+}$ phosphor films.

• 동력기계공학회지
• /
• 제20권5호
• /
• pp.20-28
• /
• 2016

This study has developed an organic/inorganic hybrid solution by addition of $SiO_2$ polysilicate and Melamine to the urethane. The three types of cold rolled steel were evaluated a corrosion resistance properties by using these solutions. The urethane solution(U) and the urethane solution with $SiO_2$ polysilicate($US_7$) were generate a lot of corrosion. The urethane solution with $SiO_2$ polysilicate and melamine($US_7M_3$) was excellent in corrosion resistance, regardless of the steel type. In addition, corrosion resistance has been shown to depend on the tensile strength. The appearance of coating by U and $US_7$ solution is bumpy surface, and were a lot of fine defects. $US_7M_3$ solution is made a sophisticated molecular cross-linking structure inside the coating, it was a slick surface. Other characteristics are exhibited the excellent property for all solutions.

• 한국광학회지
• /
• 제6권4호
• /
• pp.259-265
• /
• 1995

국내 민수용으로 유통되고 있는 20여종의 무반사 안경렌즈들을 선정하여 광학적 특성을 분석하였다. 분광광도계를 사용하여 측정한 반사특성과 투과특성을 렌즈의 굴절력, 각 무반사층들 및 렌즈기층에 의한 영향과 연결시켜 분석하였다. 흡수단 근방에서의 겉보기 흡수스펙트럼은 기층물질에 따라 결정되며 400-700nm의 파장대역에서 대부분의 시료들의 겉보기 흡수스펙트럼과 반사스펙트럼은 강한 양의 상관관계를 보여준다. 예외적으로 기층에 의한 흡수가 큰 렌즈들은 상관관계가 약해지며 이와 같은 기층에 의한 흡수는 무반사 특성에 부정적인 효과를 가진다. 또한 국내에서 제작되는 $SiO_2/TiO_2/SiO_2/ZrO_2/Cr$ 다층박막층을 c-Si 기층위에 성장시키면서 각 단계별로 ex-situ 분광타원해석법으로 분석하여 $TiO_2$ 박막과 $ZrO_2$ 박막의 조밀도가 80% 정도에 불과하며 박막이 두꺼원 짐에 따라 박막에 수직한 방향으로 균일하지 않음을 확인하였다. 마지막으로 실시간, in-suti 측정을 바탕으로하여 엄밀한 사양이 요구되는 다층박막, 초격자박막 등을 재현성있게 성장시킬 수 있는 가능성에 대해 토의하였다.

• 한국세라믹학회지
• /
• 제33권12호
• /
• pp.1301-1310
• /
• 1996

Generally it requires high sintering temperatures more than 135$0^{\circ}C$ to make semiconductive BaTiO3 ceramics. Also it is very difficult to achieve a homogeneous mixing in solid-state reaction method. Therefore the liquid phase distributed to non-uniform dilute the characteristics of PTCR. In order to improve the uniformity this study is used the sol-gel coating method. Using this method we studied the new manufacturing process that had a high reproducibility and mass production capability. Tetraethyl orthosilicate (TEOS) was used as a source of Si. The semiconductive BaTiO3 ceramics which was produced by sol-gel method for the SiO2 addition and sintered between 124$0^{\circ}C$ and 130$0^{\circ}C$ showed almost same resistivity at room temperature among 125$0^{\circ}C$ and 130$0^{\circ}C$. As the results We could be sintered the semiconducting BaTiO3 ceramics at lower temperature even at 125$0^{\circ}C$ maintaining the same specific resistivity ratio ($\rho$max/$\rho$min) at 130$0^{\circ}C$. The specific resistivity both below and above the Curie temperature were increased by slow cooling and the steepness of the plots in the reasion of transition from low to high resistance increased as the cooling rate decreased.

• 한국세라믹학회지
• /
• 제30권8호
• /
• pp.615-622
• /
• 1993

In order to increase chemical durability of thin films in binary system B2O3-SiO2 and Al2O3-SiO2 on the slide glass by the dip-coating technique from TEOS(Tetraethyl Orthosilicate) and boric acid or aluminum nitrate, phosphoric acid(5~20mol%) was added, respectively. Corrosion of acid and alkali of samples treated with 1N, HCl, NaOH and distilled water at 10$0^{\circ}C$ for 15 minute, were measured IR transmittance and variance of transmittance at visible range. Surface structure of thin film was investigated with SEM and formation of crystal phase according to additiion of phosphoric acid was measrued with XRD. In Al2O3-SiO2 system, change of remarkable characteristic was not obtained at the addition of P2O5 but transmittance of thin film was decreased with addition of P2O5 in B2O3-SiO2 system.

• 한국세라믹학회지
• /
• 제34권4호
• /
• pp.406-412
• /
• 1997

Al2O3/SiC hybrid-composite has been fabricated by the conventional powder process. The addition of $\alpha$-Al2O3 as seed particles in the transformation of ${\gamma}$-Al2O3 to $\alpha$-Al2O3 provided a homogeneity of the microstructure. The grain growth of Al2O3 are significantly surpressed by the addition of nano-size SiC particles. Dislocation were produced due to the difference of thermal expansion coefficient between Al2O3 and SiC and piled up on SiC particles in Al2O3 matrix, resulting in transgranular fracture. The high fracture strength of the composite was contributed to the grain refinement and the transgranular fracture mode. The addition of SiC platelets to Al2O3/SiC nano-composite decreased the fracture strength, but increased the fracture toughness. Coated SiC platelets with nitrides such as BN and Si3N4 enhanced fracture toughness much more than non-coated SiC platelets by enhancing crack deflection.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2015년도 자성 및 자성재료 국제학술대회
• /
• pp.90-90
• /
• 2015

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2016년도 자성 및 자성재료 국제학술대회
• /
• pp.202-202
• /
• 2016

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2016년도 임시총회 및 하계학술연구발표회
• /
• pp.135-135
• /
• 2016