• 한국세라믹학회지
• /
• 제43권9호
• /
• pp.558-563
• /
• 2006

The electrical and dielectric properties of $ZnO-Pr_6O_{11}CoO-Cr_2O_3La_2O_3-based$ nonlinear resistors were investigated at different sintering temperatures in the range of $1230{\sim}1300^{|circ}C$. As the sintering temperature increased, the breakdown voltage decreased from 777.9 to 108.0V/mm, the nonlinear coefficient greatly decreased from 77.0 to 7.1, and the leakage current increased from $0.4{\mu}A\;to\;50.6{\mu}A$. On the other hand, the donor density from $0.90{\times}10^{18}\;to\;2.59{\times}10^{18}/cm^3$ and the barrier height decreased from 1.89 to 0.69 eV with increasing temperature. The dielectric dissipation factor increased from 0.0879 to 0.2839 for the increase of sintering temperature.

• Transactions on Electrical and Electronic Materials
• /
• 제8권6호
• /
• pp.234-240
• /
• 2007

The electrical properties and dc aging behavior for specified stress state of system, which is composed of quaternary Zn-Pr-Co-Cr, were investigated for different $Dy_2O_3$ addition doping level. As $Dy_2O_3$ doping level increased, the density decreased in the range of 5.51-4.90 $g/cm^3$, reaching maximum at 0.5 mol% and the average ZnO grain size decreased in the range of 17.7-6.0 ${\mu}m$. The incorporation of $Dy_2O_3$ significantly improved the non-ohmic properties, above 30 in non-ohmic coefficient, compared with that of undoped samples. The samples with the best performance of non-ohmic properties were obtained for $Dy_2O_3$ doping level of 1.0 mol%, with 49 in non-ohmic coefficient and 2.6 ${\mu}A/cm^2$ in leakage current. The samples with the highest stability were obtained for $Dy_2O_3$ doping level of 0.5 mol%.

• 한국세라믹학회지
• /
• 제37권11호
• /
• pp.1044-1050
• /
• 2000

ZnO-Pr$_{6}$O$_{11}$-Co$_3$O$_4$-CaO 사성분계에 SiO$_2$를 0.4at%까지 첨가하여 1180, 1200 및 125$0^{\circ}C$에서 소성하여 미세구조 및 전기적인 특성을 조사하였다. 소성온도 120$0^{\circ}C$ 이상에서 치밀한 시편을 얻을 수 있었고, Si는 주로 입계에 분포하고 있으며, SiO$_2$첨가는 결정립성장을 억제하였다. 이 현상은 고상소결만이 일어나 120$0^{\circ}C$에서 소결된 시편과 액상소결이 일어난 125$0^{\circ}C$에서 소결된 시편 모두에서 관찰되었으며, SiO$_2$첨가에 의한 기공의 증가에 기인하는 것으로 판단된다. SiO$_2$의 첨가에 의해 바리스터의 비선형계수가 크게 변화하였으며, 시편의 소성과정이 고상소결인 경우 비선형계수가 증가한 반면 액상소결인 경우에는 감소하였다. 적절한 양의 SiO$_2$(약 0.3at%)를 첨가하여 액상이 형성되지 않는 120$0^{\circ}C$에서 소성하여 80 이상의 비선형계수를 갖는 바리스터를 제조할 수 있었다.

• Transactions on Electrical and Electronic Materials
• /
• 제11권5호
• /
• pp.216-221
• /
• 2010

The microstructure, electrical properties, and DC-accelerated aging behavior of the Zn-Pr-Co-Cr-Y-Er (ZPCC-YE) varistors were investigated for different amounts of erbium oxide ($Er_2O_3$). The microstructure consisted of zinc oxide grain and an intergranular layer ($Pr_6O_{11}$, $Y_2O_3$, and $Er_2O_3$-rich phase) as a secondary phase. The increase of $Er_2O_3$ amount decreased the average grain size and increased the sintered density. As the $Er_2O_3$ amount increased, the breakdown field increased from 5094 V/cm to 6966 V/cm and the nonlinear coefficient increased from 27.8 to 45.1. The ZPCC-YE varistors added with 0.5 to 1.0 mol% $Er_2O_3$ are appropriate for high voltage, with high nonlinearity and stability against DC-accelerated aging stress.

• Bulletin of the Korean Chemical Society
• /
• 제18권2호
• /
• pp.213-217
• /
• 1997

Magnesium reduction of Mo(N-C6H3-2,6-i-Pr2)2Cl2(DME) in the presence of trimethylphosphine led to a mixture of Mo(N-C6H3-2,6-i-Pr2)(PMe3)2Cl3, 1, and Mo2(PMe3)4Cl4, 2. In solution 1 is slowly air-oxidized to Mo(N-2,6-i-Pr2-C6H3)(OPMe3)(PMe3)Cl3, 3. 1 is chemically inert to carbon nucleophiles (ZnMe2, ZnEt2, AlMe3, AlEt3, LiCp, NaCp, TlCp, NaCp*, MeMgBr, EtMgBr), oxygen nucleophiles (LiOEt, LiO-i-Pr, LiOPh, LiOSPh), and hydrides (LiBEt3H, LiBEt3D). Crystal data for 1: orthorhombic space group P212121, a=11.312(3) Å, b=11.908(3) Å, c=19.381(6) Å, Z=4, R(wR2)=0.0463 (0.1067). Crystal data for 2: monoclinic space group Cc, a=18.384(3) Å, b=9.181(2) Å, c=19.118(3) Å, b=124.98(1)°, Z=4, R(wR2)=0.0228 (0.0568). Crystal data for 3: orthorhombic space group P212121, a=11.464(1) Å, b=14.081(2) Å, c=16.614(3) Å, Z=4, R(wR2)=0.0394 (0.0923).

• 한국전기전자재료학회논문지
• /
• 제18권1호
• /
• pp.50-56
• /
• 2005

The electrical properties, clamping voltage characteristics, and stability of dysprosia-doped ZnO-P $r_{6}$ $O_{11}$-based varistors were investigated with different dysprosia contents from 0 to 2.0 mol%. The incorporation of dysprosia in varistor ceramics greatly increased the varistor voltage from 50 to 481.0 V/mm. It was found that the dysprosia is good additive improving a nonlinearity, in which the nonlinear exponent is above or near 50, and the leakage current is below 1.0 $\mu$A. The dysprosia-doped varistors exhibited superior clamping voltage characetristics, in which clamping voltage ratio is above or neat 2 at surge current of 50 A. The 0.5 mol% dysprosia-doped varistors only exhibited high stability, with the rate of varistor voltage of -0.9%, under DC acceleraetd aging stress, 0.95 $V_{lmA}$/15$0^{\circ}C$/24 h.h.h.h.

• Transactions on Electrical and Electronic Materials
• /
• 제15권4호
• /
• pp.213-216
• /
• 2014

The microstructure and varistor properties of ZPCCAE ($ZnO-Pr_6O_{11}-CoO-Cr_2O_3-Al_2O_3-Er_2O_3$) ceramics were investigated with different erbium amounts. Analysis of the microstructure indicated that the ceramics consisted of ZnO grains as a bulk phase, and intergranular layers (mixture of $Pr_6O_{11}$ and $Er_2O_3$) as a minor secondary phase. With the increase of the doped erbium amount, the densities of sintered pellets increased from 5.63 to $5.82g/cm^3$, and the average grain size decreased from 9.0 to $5.7{\mu}m$. The increase of the doped erbium amount increased the breakdown field from 2,649 to 5,074 V/cm, and the nonlinear coefficient from 27.6 to 39.1. It was found that in the range of 0.25 to 0.5 mol%, the doped erbium had little effect on the microstructure and electrical properties.

• 한국결정성장학회지
• /
• 제17권6호
• /
• pp.272-276
• /
• 2007

생산성이 우수한 스컬용융법(Skull melting method)에 의해 다양한 색의 보석용 큐빅지르코니아(Cubic Zirconia) 단결정을 성장시켰다. 큐빅지르코니아 단결정은 굴절률, 분산, 경도가 다이아몬드와 유사하고 3d 전이원소, 4f 희토류원소를 첨가하여 다양한 색개발이 가능하므로 합성보석으로 대표적이다. 첨가제로는 $Pr_6O_{11},\;TiO_2,\;MnO_2,\;Er_2O_3$를 2가지 이상적정 혼합하여 성장시켰고, 색향상과 균일성을 위해 열처리를 병행하였다. 본 연구는 천연 유색보석인 페리도트, 연수정, 적색 투어멀린의 색재현에 그 목적이 있다.

• 한국전기전자재료학회논문지
• /
• 제17권11호
• /
• pp.1167-1173
• /
• 2004

This paper reports the variations of varistor voltage, nonlinear exponent, leakage current, and dissipation factor against surge stress of ZnO-P $r_{6}$ $O_{11}$-CoO-C $r_2$ $O_3$-E $r_2$ $O_3$(ZPCCE)-based varistors manufactured with the variations of sintering temperature. It was found that the variations of electrical parameters against surge stressing current of 100 A/$\textrm{cm}^2$(8x20 ${\mu}\textrm{s}$) is not so large under the surge stress of 700 times. Among varistors, specially the varistor sintered at 134$0^{\circ}C$ exhibited the smallest variations, with %$\Delta$ $V_{lmA}$=+0.23%, %$\Delta$$\alpha$=+0.23%, %$\Delta$ $I_{L}$=0%, %$\Delta$tan$\delta$=-6.94%. The clamping voltage ratio( $V_{c}$/ $V_{lmA}$) of all varistors was less than 2.2.2.2.2.2.2.

• 아시안잔디학회지
• /
• 제18권4호
• /
• pp.179-191
• /
• 2004

피복율 가을 조성 시(2001. 9. 4)의 피복율은 롤잔디의 경우 KB100, KB80+PR20 처리구 모두 1.5개월(2001. 10. 20)이 경과하면 $100\%$의 피복율을 나타내었으며, 파종의 경우는 초종의 혼합비율에 따라 피복율이 차이를 보였는데 PR100 처리구가 다른 처리구에 비하여 가장 높은 피복율을 보였으며 다음으로 KB70+PR 30, KB80+PR20, KB100처리구 순으로 나타났다. 휴면기를 거친 후의 피복율은 PR100 처리구가 가장 높게 나타났으며 파종 후 7개월 (2002. 5. 5)만에 $100\%$ 피복되었다. KB100, KB80+PR20, KB70+PR30처리구들은 처리구간의 피복율에 차이가 거의 없었으며 공히 7.5개월(2002. 5. 20)만에 $100\%$ 피복율을 나타내었다. 봄 조성시(2002. 4. 11)의 조성속도는 모든 처리구가 가을 조성(2001. 9. 4)시 보다 빨랐다. 봄조성시의 피복율은 롤잔디의 경우 KB100, KB80+PR20 처리구 모두 조성 1개월(2002. 5.11) 후 1$100\%$ 피복율을 나타내었으며 파종의 경우는 $100\%$ 피복되는데 소요되는 기간은 PR100 처리구의 경우 3개월(2002. 7, 12)로 가장 빠른 조성을 보였으며 다음으로 KB80+PR2O, KB70+PR30 처리구가 3.5개월(2002. 7. 26)이 소요되었으며 KB100 처리구는 4개월(2002. 8. 9)이 소요되었다. 봄 파종시기별 피복율 4월, 5월, 6월에 각각 파종하여 파종시기별, 초종혼합비율에 따른 한지형 잔디의 피복율을 조사한 결과, 파종시기에 따른 피복율은 모든 초종혼합비에서 4월 파종이 가장 높은 피복율을 나타내었으며 다음으로 5월, 6월 순으로 나타났다. 4월 파종과 5월 파종간의 피복율 차는 상대적으로 낮았으나 6월 파종은 4월, 5월에 비하여 피복율 차이가 크게 나타났다. 초종혼합비 율에 따른 피복율은 4월 5월 파종의 경우는 Perennial ryegrass의 혼합비가 높을수록 피복율이 높았으나 6월 파종의 경우는 KB100, KB80 : PR20, KB70 : PR30, KB50 : PR5O의 혼합구는 Perennial ryegrass의 혼합비가 높을수록 피복율이 낮은 경향을 보였으며 PR 100 구는 이들 혼합구보다 약간 높은 피복율을 보였다. 봄 파종시기별, 초종혼합 비율에 따른 개체수 2002년 4월 1일 파종 후 2002년 7월 5일(조성 후 95일)에 초종혼합비율에 따른 개체수 및 총직립 경수를 조사한 결과, KB100:PR0, KB80 :PR20, KB70:PR30, KB50:PR50, PR100:KB0 처리구의 $1m^2$ 당 개체 수는 각각 16,600개, 6,700개, 4,900개, 3,300개, 12,400개였으며 총직립경 수는 각각 33,200개, 22,800개, 18,000개, 15,000개, 62,000개였다. 개체 수는 KB100:PR0처리구가 가장 높았고, 다음은 PR100:KB0처리구였으며 혼합처리구의 경우는 Kentucky bluegrass 혼합비 율이 높을수록 높았다. 총직립경 수는 PR100:KB0 처리구가 KB100:PR0 처리구보다 오히려 높았으며 혼합 처리구의 경우는 개체수와 비슷한 경향을 보였다. 혼합처리구의 경우 초종별 개체수의 비율은 KB80:PR20는 87:13, KB70:PR30는 78:22, KB50:PR50은 48:52의 비율로 나타났다. 조성시기의 기상과 피복율과의 상관관계 2001년 가을과 2002년 봄의 일일평균기온을 비교하여 보면 가을(9월, 10월, 11월) 3개월간의 일일평균기온은 $13.0^{\circ}C$였으며, 봄(4월, 5월, 6월) 3개월간의 일일평균기온은 $17.3^{\circ}C$로 봄철이 가을철 보다 $4.5^{\circ}C$ 높게 나타났다. 조성시기에 따른 한지형 잔디의 피복율 결과에서 봄철이 가을철보다 조성속도가 빠른 것은 일일평균 기온이 피복율에 영향을 미치는 요인중의 하나로 작용하였다. 2001년 가을과 2002년 봄의 일조시간을 비교하여 보면 가을(9월, 10월, 11월) 3개월간의 평균일조시간은 277시간 이였으며, 봄(4월, 5월, 6월) 3개월간은 301.2시간으로 봄철의 일조시간이 가을철보다 월 94.2시간 많은 것으로 조사되었다. 봄철, 가을철의 강수량은 봄철이 95mm/월, 가을철이 27.3mm/월로 봄철이 가을철보다 약 3배정도 높게 나타났으나 강수량이 많은 봄철에 잔디피복율이 높은 점으로 보아 강수량이 많을수록 잔디생육에 부정적인 영향을 미쳤다고 보기는 어렵다.