• 열처리공학회지
• /
• 제35권3호
• /
• pp.130-138
• /
• 2022

In this study, the characteristic of an amorphous fishing weight material according to controlling the alloy type and alloy composition of the glass forming agent added in PbO₂ oxide was investigated. According to the experimental, when the glass forming agent of 15wt%SiO₂-1wt%MgO content was added in β-PbO₂, an amorphous fishing weight substitute having the lowest friction coefficient, excellent corrosion resistance and durability was obtained. The cell number of PbO₂-15wt%SiO₂-1wt%MgO sample incubated in cell culture fluid tended to hardly decrease even after a lapse of 24 hours, It means that the fabricated PbO₂-15wt%SiO₂-1wt%MgO sample is significantly less-toxic and harmless to the human body, unlikely to metallic lead. It is considered that an fabricated amorphous fishing weight substitute proved to have a potential as an eco-friendly material with little marine pollution.

• 한국세라믹학회지
• /
• 제31권10호
• /
• pp.1202-1208
• /
• 1994

On heating amorphous Pb(Fe2/3W1/3)O3 ceramics, glass transition occurred at 35$0^{\circ}C$, crystallization at 394~420, 485~550 and 540~571$^{\circ}C$ (depending on the heating rates of 2.5~8$0^{\circ}C$/min), phase transformation at 680 and 73$0^{\circ}C$, and melting at 935$^{\circ}C$. A curve-fitting computer program was made using FORTRAN, based on a kinetic equation. Reconstructed thermograms (using the program) turned out to be very close to the measured DSC results for all the heating rates, with average deviation of only 4% at maximum.