• Korean Journal of Optics and Photonics
• /
• v.20 no.4
• /
• pp.201-206
• /
• 2009

In this study, we have fabricated a fiber-optic radiation sensor for detection of tritium using inorganic scintillators and optical fibers. We have tested various kinds of inorganic scintillators such as $Gd_2O_2S$ : Tb, $Y_3Al_5O_{12}$ : Ce, and CsI : Tl to select the most effective sensor tip. In addition, we have measured the scintillating lights using a photomultiplier tube as a function of distance between sensor tips to the source with the different activities of hydride tritium. The final results are compared with those which are obtained using a surface activity monitor.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.101-106
• /
• 2008

The $SnO_2$ thin films doped with Pd and CNT as $NO_2$ gas sensor were prepared by spin coating and then the $NO_2$ gas response of these films were evaluated under $1ppm{\sim}5ppm\;NO_2$ concentration and operating temperature of $200^{\circ}C$. It was found that the sensor resistance was increased with $NO_2$ exposure and $NO_2$ concentration. The 3wt% Pd doped sample showed a sensitivity of 26.5 which was 10 times higher than that of pure $SnO_2$. And also the sensitivity of CNT doped sample increased with CNT content and it had 72 when 0.225 wt% of CNT was added under 5ppm $NO_2$ concentration.

• Korean Journal of Optics and Photonics
• /
• v.23 no.3
• /
• pp.124-127
• /
• 2012

We designed and fabricated dichroic filters for high-power fiber lasers to protect the pumping laser diode from counterpropagating laser beams. The transmittance at laser diode wavelengths of 905 nm~925 nm was designed to be less than 0.1% and the transmittance at the fiber laser or Brillouin scattering wavelengths of 1020 nm ~ 1100 nm was designed to be more than 99.9%. Since oxide materials have good adhesion to the $SiO_2$ substrate, $SiO_2/Ta_2O_5$ were used as coating materials. The filter was fabricated according to our optimized design and its characteristics were compared with the theoretical design. As a result, the transmittance at laser diode wavelengths of 905 nm~925 nm was measured to be less than 0.1%, and the transmittance at the fiber laser or Brillouin scattering wavelengths of 1020 nm~1100 nm was measured to be more than 95.5%, which coincided well with the theoretical design considering processing errors. The filter was found to operate well over 1W of input laser power.

• Korean Journal of Materials Research
• /
• v.25 no.6
• /
• pp.300-304
• /
• 2015

Nanorod ZnO and spherical nano ZnO for gas sensors were prepared by hydrothermal reaction method and hydrazine method, respectively. The nano-ZnO gas sensors were fabricated by a screen printing method on alumina substrates. The gas sensing properties were investigated for hydrocarbon gas. The effects of Co concentration on the structural and morphological properties of the nano ZnO:Co were investigated by X-ray diffraction and scanning electron microscope (SEM), respectively. XRD patterns revealed that nanorod and spherical ZnO:Co with a wurtzite structure were grown with (100), (002), (101) peaks. The sensitivity of nanorod and spherical ZnO:Co sensors was measured for 5 ppm $CH_4$ and $CH_3CH_2CH_3$ gas at room temperature by comparing the resistance in air with that in target gases. The highest sensitivity to the $CH_4$ and $CH_3CH_2CH_3$ gas of spherical nano ZnO:Co sensors was observed at Co 6 wt%. The spherical nano ZnO:Co sensor exhibited a higher sensitivity to hydrocarbon gas than nanorod ZnO.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.10
• /
• pp.865-870
• /
• 2000

In this paper, catalytic combustible gas sensor was fabricated and tested under flammable gases such as CH$_4$and $C_4$H$_{10}$by using Pt coil as a heater and/or temperature sensing element. Fine $Al_2$O$_3$powder was used for a bead and Pt, Pd noble metal powder for a catalyst. Resistance variation of Pt wire was traced by the changes of the gas concentrations in a chamber. Output voltage was then monitored to obtain the gas concentration from the resistance variation. In this experiment, MgO was used to protect cracks in the based and TiO$_2$to increase the sensitivity of the sensors. Water glass was also added to enhance the selectivity to the combustible gases.s.

• Journal of Sensor Science and Technology
• /
• v.29 no.6
• /
• pp.369-373
• /
• 2020

A hydrogen sensor was fabricated by utilizing a bundle of metal oxide nanostructures whose growth positions were selectively controlled by utilizing graphene, which is a carbon of atomic-unit thickness. To verify the reducing ability of graphene, it was confirmed that the multi-composition metal oxide V₂O₅ was converted into VO₂ on the graphene surface. Because of the role of graphene as a reducing catalyst, it was confirmed that ZnO and MoO₃ nanostructures were grown at high density only on the graphene surface. The fabricated gas sensor showed excellent sensitivity.

• Proceedings of the KIEE Conference
• /
• 1992.07b
• /
• pp.759-761
• /
• 1992

$0.10Pb(Sb_{1/2}Sn_{1/2})O_3-0.25PbTiO_3-0.65PbZrO_3+MnO_2(0.18mol%)$, NiO(0.15mol%) temary compound ceramics won fabricated by the mixed-oxide method. Noise properties of the pyroelectric infrared sensor were investigated with particle size of the raw materials and gain size of the specimens. Particle size were decreased and sintered density, voltage resposivity were increased with increasing the ball-mill times. The specimen ball-milled for a 80[hr] showed a good pop-corn noise properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.826-829
• /
• 2002

$MoO_3$ thin films were deposited on electrode and heater screen-printed alumina substrates in en atmosphere by RF reactive sputtering. The deposition was performed at $300^{\circ}C$ with 350W of a forward power in an $Ar-O_2$ atmosphere. The working pressure was maintained at $3{\times}10^{-2}$mtorr and all deposited films were annealed at $500^{\circ}C$ for 5hours. The surface morphology of films was observed by using a SEM and crystalline phases were analyzed by XRD. The sensing properties were investigated in term of gas concentration under exposure of reducing gases such as $H_2$, $NH_3$ and CO.

• Journal of Sensor Science and Technology
• /
• v.25 no.1
• /
• pp.51-56
• /
• 2016

This study evaluates the performance of an optical sensor and measurement system (CMA-24) which can analyze the fluctuation of dissolved oxygen and pH simultaneously. In the optical sensor system, the fluorescent materials, Rudpp and HPTS which are sensitive to dissolved oxygen and pH, respectively, are coated on the bottom of a 24-well -plate by the sol-gel technology. The detection times of the emission light of the oxygen sensor were $4,186{\pm}13.90{\mu}s$ and $4,452{\pm}36.68{\mu}s$ for the dissolved oxygen of 17% $O_2$ and 7.6% $O_2$, respectively. On the other hand, the detection times of the pH sensor were $6,699.43{\pm}14.64{\mu}s$, $6,722.24{\pm}6.21{\mu}s$, and $6,748.52{\pm}2.63{\mu}s$ using pH 6, 7, and 8, respectively. When we determined cellular respiration levels of C2C12 myocytes with CMA-24, $O_2$/pH measurement system, the ratio of the uncoupled to coupled OCR (oxygen consumption rate) was 1.41. The results mean that this CMA-24 system shows almost the same sensitiveness as the commercial system.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.276-283
• /
• 1997

A dry impregnation method was used for preparing pellet type Pt/$SnO_2$ gas sensor. The crystal structure, direction of the crystal, crystal size and microstructure between the catalyst and the support ($SnO_2$) were characterized with electron diffraction analysis, transmission electron microscopy, scanning electron microscopy. The characterization indicates that when Pt/$SnO_2$ sample is calcined at $400^{\circ}C$, the Cl content associated with the Pt phase diminishes and the part of Pt is moved into $SnO_2$ support. This results in the enhancement of gas sensitivity. After the reactor with a Pt/$SnO_2$ sample was run with a flow rate of 30 sccm (a mixture of 0.5% $H_2$ in $_N2$) for a while, the resistance of $SnO_2$ was saturated, but the $SnO_2$ kept absorbing $H_2$ gas. This indicates that the surface state was saturated. For the 14 ppm $H_2$ gas, the sensitivity of Pt/$SnO_2$ devices was about 81% at an operating temperature of $300^{\circ}C$.