• Transactions on Electrical and Electronic Materials
• /
• v.16 no.6
• /
• pp.346-350
• /
• 2015

In this study, we carried out an investigation of the etch characteristics of TiO₂ thin films and the selectivity of TiO₂ to SiO₂ in adaptive coupled C1₂/Ar plasma. The maximum etch rate of the TiO₂ thin film was 136±5 nm/min at a gas mixing ratio of C1₂/Ar (75%:25%). The X-ray photoelectron spectroscopy (XPS) analysis showed the efficient destruction of oxide bonds by the ion bombardment as well as the accumulation of low volatile reaction products on the etched surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.178-181
• /
• 2003

In this work, we etched PZT films with various additive gases ($O_2$ and Ar) in $Cl_2/CF_4$ plasmas, while mixing ratio was fixed at 8/2. After the etching, the plasma induced damages are characterized in terms of hysteresis curves, leakage current, retention properties, and switching polarization. When the electrical properties of PZT etched in $O_2$ or Ar added $Cl_2/CF_4$ were compared, the value of remanent polarization in $O_2$ added $Cl_2/CF_4$ plasma is higher than that in Ar. added plasma. The maximum etch rate of the PZT thin films was 145 nm/min for 30% Ar added $Cl_2/CF_4$ gas having mixing ratio of 8/2 and 110 nm/min for 10% $O_2$ added to that same gas mixture. In order to recover the ferroelectic properties of the PZT thin films after etching, we annealed the etched PZT thin films at $550^{\circ}C$ in an $O_2$ atmosphere for 10 min. From the hysteresis curves, leakage current, retention property and switching polarization, the reduction of the etching damage and the recovery via the annealing was turned out to be more effective when $O_2$ was added to $Cl_2/CF_4$ than Ar. X-ray diffraction (XRD) showed that the structural damage was lower when $O_2$ was added to $Cl_2/CF_4$. And the improvement in the ferroelectric properties of the annealed samples was consistent with the increased intensities of the (100) and the (200) PZT peaks.

• Applied Science and Convergence Technology
• /
• v.27 no.1
• /
• pp.9-13
• /
• 2018

Samples of anodic oxide film used in semiconductor and display manufacturing processes were prepared at different electrolyte temperatures to investigate the corrosion resistance. The anodic oxide film was grown on aluminum alloy 6061 by using a sulfuric acid ($H_2SO_4$) electrolyte of 1.5 M at $0^{\circ}C$, $5^{\circ}C$, $10^{\circ}C$, $15^{\circ}C$, and $20^{\circ}C$. The insulating properties of the samples were evaluated by measuring the breakdown voltage, which gradually increased from 0.43 kV ($0^{\circ}C$) to 0.52 kV ($5^{\circ}C$), 1.02 kV ($10^{\circ}C$), and 1.46 kV ($15^{\circ}C$) as the electrolyte temperature was increased from $0^{\circ}C$ to $15^{\circ}C$, but then decreased to 1.24 kV ($20^{\circ}C$). To evaluate the erosion of the film by fluorine plasma, the plasma erosion and the contamination particles were measured. The plasma erosion was evaluated by measuring the breakdown voltage after exposing the film to $CF_4/O_2/Ar$ and $NF_3/O_2/Ar$ plasmas. With exposure to $CF_4/O_2/Ar$ plasma, the breakdown voltage of the film slightly decreased at $0^{\circ}C$, by 0.41 kV; however, the breakdown voltage significantly decreased at $20^{\circ}C$, by 0.83 kV. With exposure to $NF_3/O_2/Ar$ plasma, the breakdown voltage of the film slightly decreased at $0^{\circ}C$, by 0.38 kV; however, the breakdown voltage significantly decreased at $20^{\circ}C$, by 0. 77 kV. In addition, for the entire temperature range, the breakdown voltage decreased more when sample was exposed to $NF_3/O_2/Ar$ plasma than to $CF_4/O_2/Ar$ plasma. The decrease of the breakdown voltage was lower in the anodic oxide film samples that were grown slowly at lower temperatures. The rate of breakdown voltage decrease after exposure to fluorine plasma was highest at $20^{\circ}C$, indicating that the anodic oxide film was most vulnerable to erosion by fluorine plasma at that temperature. Contamination particles generated by exposure to the $CF_4/O_2/Ar$ and $NF_3/O_2/Ar$ plasmas were measured on a real-time basis. The number of contamination particles generated after the exposure to the respective plasmas was lower at $5^{\circ}C$ and higher at $0^{\circ}C$. In particular, for the entire temperature range, about five times more contamination particles were generated with exposure to $NF_3/O_2/Ar$ plasma than for exposure to $CF_4/O_2/Ar$ plasma. Observation of the surface of the anodic oxide film showed that the pore size and density of the non-treated film sample increased with the increase of the temperature. The change of the surface after exposure to fluorine plasma was greatest at $0^{\circ}C$. The generation of contamination particles by fluorine plasma exposure for the anodic oxide film prepared in the present study was different from that of previous aluminum anodic oxide films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.319-324
• /
• 2002

In this study, the reduce of plasma etching damage in PZT thin film with addictive gas and re-annealing after etching have been investigated. The PZT thin films were etched as a function of $Cl_2/CF_4$ with addition of Ar and $O_2$ with inductively coupled plasma. The etch rates of PZT thin films were 1450 ${\AA}/min$ at 30% additive Ar and 1100 ${\AA}/min$ at 10% auditive $O_2$ into $Cl_2/CF_4$ gas mixing ratio of 8/2. In order to reduce plasma damage of PZT thin films after etching, the etched PZT thin films were re-annealed at various temperatures at $O_2$ atmosphere. From the hysteresis curries, the ferroelectric properties are improved by $O_2$ re-annealing process. The improvement of ferroelectric behavior at annealed PZT films is consistent wish the increase of the (100) and (200) PZT peaks revealed by x-ray diffraction (XRD). From x ray photoelectron spectroscopy (XPS) analysis, the intensity of Pb-O, Zr-O and Ti-O peak are increased and the chemical residue peak is reduced by $O_2$ re-annealing. The ferroelectric behavior consistent with the dielectric nature of $Ti_xO_y$ is recovered by $O_2$ recombination during rapid thermal annealing process.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.41-42
• /
• 2008

본 논문에서는 As-doped ZnO 박막의 플라즈마 식각 특성 및 메커니즘에 관하여 실험을 수행 하였다. As-doped ZnO 박막 식각 실험은 유도 결합 플라즈마 식각 장비(inductively coupled plasma;ICP)와 $BCl_3$/Ar 플라즈마에 첨가된 $Cl_2$가스의 비, RF 전력, DC bias voltage, 공정 압력에 대한 식각 속도의 변화를 관찰 하였다. $BCl_3$/Ar 플라즈마에 $Cl_2$ 가스 첨가량 6 sccm 까지는 증가하지만 그 이후 $Cl_2$ 가스의 첨가량이 증가할 때 식각속도가 감소하였다. 이는 플라즈마 내에서 Cl 라디칼의 밀도가 증가함에 따라서 $Ar^+$의 에너지가 감소와 비휘발성 식각 부산물의 증가에 의하여 효과적인 물리적 식각이 이루어 지지 못한 것으로 판단된다. OES를 이용하여 플라즈마 내에서 라디칼들의 빛의 세기를 측정하였고, 식각 후 As-type ZnO 박막 표면에서의 화학적 결합을 보기위해 XPS 분석을 실행하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.83-84
• /
• 2007

$BCl_3$/Ar ICP 플라즈마를 이용한 $ZrO_2$ 박막의 식각 메카니즘이 실험 결과와 모델링을 통해 연구되었다. Ar 가스의 증가에 따라, $ZrO_2$의 식각 속도는 선형 변화의 경향을 보이지 않았고, Ar의 약 30% - 35%에서 41.4nm/min의 최대의 속도를 나타내었다. Langmuir probe 측정과 plasma 모델링 결과로부터, $BCl_3$/Ar 가스 혼합비가 플라즈마 파라미터와 active species의 형성에 큰 영향을 미침을 확인하였다. 한편 surface kinetics 모델링 결과로부터, $ZrO_2$의 식각 속도는 ion-assisted chemical reaction mechanism 에 의해 결정됨을 확인하였다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1504-1507
• /
• 2009

In this paper, the etching behavior of ZnO in $CF_4$ plasma mixed Ar was investigated. Previously, the etch rate in $CF_4$/Ar plasma was reported that it is slower than that in Cl containing plasma. But, plasma included Cl atom can produce the by-product such as $ZnCl_2$. In order to solve this film contamination, no Cl containing etching gas is required. We controlled the etching parameter such as source power, substrate bias power, and $CF_4$/Ar gas ratio to acquire the fast etch rate using a ICP etcher. We accomplished the etching rate of 144.85 nm/min with the substrate bias power of 200W. As the energetic fluorine atoms were bonded with Zinc atoms, the fluoride zinc crystal ($ZnF_2$) was observed by X-ray photoelectron spectroscopy (XPS).

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.21-24
• /
• 2000

Ferroelectric YMnO$_3$thin films are excellent dielectric materials for high integrated ferroelectric random access memory (FRAM) with metal-ferroelectric-silicon field effect transistor (MFSFET) structure. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$thin films is 285 $\AA$/min under Cl$_2$/Ar of 10/0, 600 W/-200 V and 15 mTorr. The selectivities of YMnO$_3$over CeO$_2$and $Y_2$O$_3$are 2.85, 1.72, respectively. The results of x-ray photoelectron spectroscopy (XPS) reflect that Y is removed dominantly by chemical reaction between Y and Cl, while Mn is removed more effective by Ar ion bombardment than chemical reaction. The results of secondary ion mass spectrometer (SIMS) were equal to these of XPS. The etch profile of the etched YMnO$_3$film is approximately 65$^{\circ}$and free of residues at the sidewall.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.26-29
• /
• 2001

SrBi$_2$Ta$_2$$O_{9}$ thin films were etched at high-density C1$_2$/CF$_{4}$/Ar in inductively coupled plasma system. The etching of SBT thin films in C1$_2$/CF$_{4}$/Ar were chemically assisted reactive ion etching. The maximum etch rate was 1300 $\AA$/min at 900W in Cl$_2$(20)/CF$_4$(20)/Ar(80). As f power increase, radicals (F, Cl) and ion(Ar) increase. The influence of plasma induced damage during etching process was investigated in terms of the surface morphology and th phase of X-ray diffraction. The chemical residue was investigated with secondary ion mass spectrometry.y.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.344-350
• /
• 1999

The surface chemical structure of three kinds of polyethylene (PE): high density (HD) PE, low density (LD) PE and linear (L)-LDPE exposed to Ar and $O_2$ plasmas has been investigated using XPS. Oxygen was incorporated in a more increased amount for HDPE than for L-LDPE and LDPE. Ar plasma tended to incorporate more oxygen than $O_2$ plasma. The XPS valence band spectra for Ar plasma exhibited a clear peak assigned to $O_2$s character. By chemical derivatization method it was found that the amount of -COOH group at the surface was much greater than that of -OH group. The hydrophilic nature of plasma-treated PE increased in the order: LDPE